The high activity of metallic magnesium and alloys limits its potential in biomedical applications;in recent years,extensive efforts have been devoted to modulating this reactivity.In this work,we present Mg(OH)_(2) a...The high activity of metallic magnesium and alloys limits its potential in biomedical applications;in recent years,extensive efforts have been devoted to modulating this reactivity.In this work,we present Mg(OH)_(2) and TiO_(2)barrier coatings to reduce the degradation of magnesium alloy(Mg-Ca-Zn)surfaces.These coatings were deposited by the anodization method and the spin-coating technique,respectively.The anodized layer was coated with TiO_(2)generated from the hydrolysis of 3%weight of TTIP(Ti[OCH(CH_(3))_(2)]_(4),Titanium(IV)isopropoxide)in 2-Propanol deposited by the spin-coating method.Studying the degradation in Ringer’s solution by electrochemical impedance spectroscopy and OCP revealed a 98%reduction in pittings in uncoated samples after 14 days of immersion.The p H measurements revealed that the TiO_(2)coating reduced the alkalization of the physiological environment,keeping the pH at 6.0 values.In vitro studies of two types of bacteria(E.coli and S.aureus)exhibited zones of inhibition in the agar and activity bactericidal(kill time test).The mechanisms behind the improved degradation resistance and enhanced antibacterial activity are presented and discussed here.Surface modification with Mg(OH)_(2)/TiO_(2)coatings is a promising strategy to control the biodegradation of magnesium implants for bone regeneration.展开更多
Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part i...Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.展开更多
Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nano...Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nanocrystalline is in the range of 10\20 nm, the mean size is 16 nm.展开更多
基金financed by the FOMIX-Yucatán 2008-108160,CONACYT LAB-2009-01-123913,292692,294643,188345,and 204822 projectsthe financial support received from CONACYT。
文摘The high activity of metallic magnesium and alloys limits its potential in biomedical applications;in recent years,extensive efforts have been devoted to modulating this reactivity.In this work,we present Mg(OH)_(2) and TiO_(2)barrier coatings to reduce the degradation of magnesium alloy(Mg-Ca-Zn)surfaces.These coatings were deposited by the anodization method and the spin-coating technique,respectively.The anodized layer was coated with TiO_(2)generated from the hydrolysis of 3%weight of TTIP(Ti[OCH(CH_(3))_(2)]_(4),Titanium(IV)isopropoxide)in 2-Propanol deposited by the spin-coating method.Studying the degradation in Ringer’s solution by electrochemical impedance spectroscopy and OCP revealed a 98%reduction in pittings in uncoated samples after 14 days of immersion.The p H measurements revealed that the TiO_(2)coating reduced the alkalization of the physiological environment,keeping the pH at 6.0 values.In vitro studies of two types of bacteria(E.coli and S.aureus)exhibited zones of inhibition in the agar and activity bactericidal(kill time test).The mechanisms behind the improved degradation resistance and enhanced antibacterial activity are presented and discussed here.Surface modification with Mg(OH)_(2)/TiO_(2)coatings is a promising strategy to control the biodegradation of magnesium implants for bone regeneration.
文摘Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.
文摘Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nanocrystalline is in the range of 10\20 nm, the mean size is 16 nm.