Biodegradable Mg-based implants are widely used in clinical applications because they exhibit mechanical properties comparable to those of human bone and require no revision surgery for their removal.Among Mg-based al...Biodegradable Mg-based implants are widely used in clinical applications because they exhibit mechanical properties comparable to those of human bone and require no revision surgery for their removal.Among Mg-based alloys,Mg–Zn–Ca–(Mn)alloys have been extensively investigated for medical applications because the constituent elements of these alloys,Mg,Zn,Ca,and Mn,are present in human tissues as nutrient elements.In this study,we investigated the effect of the hot extrusion temperature on the microstructure,mechanical properties,and biodegradation rate of Mg–Zn–Ca–(Mn)alloys.The results showed that the addition of Mn and a decrease in the extrusion temperature resulted in grain refinement followed by an increase in the strength and a decrease in the elongation at fracture of the alloys.The alloys showed different mechanical properties along the directions parallel and perpendicular to the extrusion direction.The corrosion test of the alloys in the Hanks’solution revealed that the addition of Mn significantly reduced the corrosion rate of the alloys.The Mg–2 wt%Zn–0.7 wt%Ca–1 wt%Mn alloy hot-extruded at 300℃ with an ultimate tensile strength of 278MPa,an yield strength of 229MPa,an elongation at fracture of 10%,and a corrosion rate of 0.3 mm/year was found to be suitable for orthopedic implants.展开更多
In this study,the microstructural evolution,mechanical properties and biocorrosion performance of a Mg–Zn–Ca–Mn alloy were investigated under different conditions of heat treatment,extrusion,one pass and two passes...In this study,the microstructural evolution,mechanical properties and biocorrosion performance of a Mg–Zn–Ca–Mn alloy were investigated under different conditions of heat treatment,extrusion,one pass and two passes of half equal channel angular pressing(HECAP)process.The results showed significant grain refinement of the homogenized alloy after two passes of HECAP process from 345μm to 2μm.Field emission scanning electron microscopy(FESEM)revealed the presence of finer Mg_(6)Zn_(3)Ca_(2)phase as well asα-Mn phase after HECAP process.The results also showed that mechanical characteristics such as yield strength,ultimate tensile strength and elongation of the HECAPed samples improved by~208%,~144%and~100%compared to the homogenized one,respectively.Crystallographic texture analysis indicated that most of the grains at the surface were reoriented parallel to the(0001)basal plane after HECAP process.Electrochemical corrosion tests and immersion results indicated that the sample with two passes of HEACP had the highest biocorrosion resistance confirming that the basal planes had the lowest corrosion rate compared to the non-basal ones.The mechanical behavior and bio-corrosion evaluation demonstrated that the HECAPed Mg–Zn–Ca–Mn alloy has great potential for biomedical applications and a mechanism was proposed to explain the interrelations between the thermomechanical processing and bio-corrosion behavior.展开更多
The effects of Zn content on the microstxucture and the mechanical and corrosion properties of as-cast low-alloyed Mg-xZn~.2Ca alloys （x = 0.6wt%, 2.0wt%, 2.5wt%, hereafter denoted as 0.6Zn, 2.0Zn, and 2.5Zn alloys, ...The effects of Zn content on the microstxucture and the mechanical and corrosion properties of as-cast low-alloyed Mg-xZn~.2Ca alloys （x = 0.6wt%, 2.0wt%, 2.5wt%, hereafter denoted as 0.6Zn, 2.0Zn, and 2.5Zn alloys, respectively） axe investigated. The results show that the Zn content not only influences grain refinement but also induces different phase precipitation behaviors. The as-cast microstxucture of the 0.6Zn alloy is composed of ct-Mg, Mg2Ca, and Ca2Mg6Zn3 phases, whereas 2.0Zn and 2.5Zn alloys only contain ct-Mg and Ca2Mg6Zn3 phases, as revealed by X-ray diffraction （XRD） and txonsmission electron microscopy （TEM） analyses. Moreover, with in- creasing Zn content, both the ultimate tensile strength （UTS） and the elongation to fracture first increase and then decrease. Among the three investigated alloys, the largest UTS （178 MPa） and the highest elongation to fracture （6.5%） are obtained for the 2.0Zn alloy. In addition, the corrosion rate increases with increasing Zn content. This paper provides on updated investigation of the alloy composi- tion-microstxucture-property relationships of different Zn-containing Mg-Zn-Ca alloys.展开更多
Mg69Zn27Ca4 alloys with diameters of 1.5, 2 and 3 mm were fabricated using copper mold injection casting method. Microstructural analysis reveals that the alloy with a diameter of 1.5 mm is almost completely composed ...Mg69Zn27Ca4 alloys with diameters of 1.5, 2 and 3 mm were fabricated using copper mold injection casting method. Microstructural analysis reveals that the alloy with a diameter of 1.5 mm is almost completely composed of amorphous phase. However, with the cooling rate decline, a little α-Mg and MgZn dendrites can be found in the amorphous matrix. Based on the microstructural and tensile results, the ductile dendrites are conceived to be highly responsible for the enhanced compressive strain from 1.3% to 3.1% by increasing the sample diameter from 1.5 mm to 3 mm. In addition, the Mg69Zn27Ca4 alloy with 1.5 mm diameter has the best corrosion properties. The current Mg-based alloys show much better corrosion resistance than the traditionally commercial wrought magnesium alloy ZK60 in simulated sea-water.展开更多
基金The authors gratefully acknowledge the financial support from the Ministry of Science and Higher Education of the Russian Federation in the framework of Increase Competitiveness Program of NUST 《MISiS》(№ К2-2019-008)implemented by a governmental decree dated 16th of March 2013,N 211.
文摘Biodegradable Mg-based implants are widely used in clinical applications because they exhibit mechanical properties comparable to those of human bone and require no revision surgery for their removal.Among Mg-based alloys,Mg–Zn–Ca–(Mn)alloys have been extensively investigated for medical applications because the constituent elements of these alloys,Mg,Zn,Ca,and Mn,are present in human tissues as nutrient elements.In this study,we investigated the effect of the hot extrusion temperature on the microstructure,mechanical properties,and biodegradation rate of Mg–Zn–Ca–(Mn)alloys.The results showed that the addition of Mn and a decrease in the extrusion temperature resulted in grain refinement followed by an increase in the strength and a decrease in the elongation at fracture of the alloys.The alloys showed different mechanical properties along the directions parallel and perpendicular to the extrusion direction.The corrosion test of the alloys in the Hanks’solution revealed that the addition of Mn significantly reduced the corrosion rate of the alloys.The Mg–2 wt%Zn–0.7 wt%Ca–1 wt%Mn alloy hot-extruded at 300℃ with an ultimate tensile strength of 278MPa,an yield strength of 229MPa,an elongation at fracture of 10%,and a corrosion rate of 0.3 mm/year was found to be suitable for orthopedic implants.
文摘In this study,the microstructural evolution,mechanical properties and biocorrosion performance of a Mg–Zn–Ca–Mn alloy were investigated under different conditions of heat treatment,extrusion,one pass and two passes of half equal channel angular pressing(HECAP)process.The results showed significant grain refinement of the homogenized alloy after two passes of HECAP process from 345μm to 2μm.Field emission scanning electron microscopy(FESEM)revealed the presence of finer Mg_(6)Zn_(3)Ca_(2)phase as well asα-Mn phase after HECAP process.The results also showed that mechanical characteristics such as yield strength,ultimate tensile strength and elongation of the HECAPed samples improved by~208%,~144%and~100%compared to the homogenized one,respectively.Crystallographic texture analysis indicated that most of the grains at the surface were reoriented parallel to the(0001)basal plane after HECAP process.Electrochemical corrosion tests and immersion results indicated that the sample with two passes of HEACP had the highest biocorrosion resistance confirming that the basal planes had the lowest corrosion rate compared to the non-basal ones.The mechanical behavior and bio-corrosion evaluation demonstrated that the HECAPed Mg–Zn–Ca–Mn alloy has great potential for biomedical applications and a mechanism was proposed to explain the interrelations between the thermomechanical processing and bio-corrosion behavior.
基金supported by the National Natural Science Foundation of China(No.51671017)Fundamental Research Funds for the Central Universities(No.FRF-GF-17-B3)+1 种基金Beijing Laboratory of Metallic Materials and Processing for Modern Transportation,the Opening Research Fund of State Key Laboratory for Advanced Metals and Materials(Nos.2016Z-11,2017Z-08)State's Key Project of Research and Development Plan(No.2016YFB0300801)
文摘The effects of Zn content on the microstxucture and the mechanical and corrosion properties of as-cast low-alloyed Mg-xZn~.2Ca alloys （x = 0.6wt%, 2.0wt%, 2.5wt%, hereafter denoted as 0.6Zn, 2.0Zn, and 2.5Zn alloys, respectively） axe investigated. The results show that the Zn content not only influences grain refinement but also induces different phase precipitation behaviors. The as-cast microstxucture of the 0.6Zn alloy is composed of ct-Mg, Mg2Ca, and Ca2Mg6Zn3 phases, whereas 2.0Zn and 2.5Zn alloys only contain ct-Mg and Ca2Mg6Zn3 phases, as revealed by X-ray diffraction （XRD） and txonsmission electron microscopy （TEM） analyses. Moreover, with in- creasing Zn content, both the ultimate tensile strength （UTS） and the elongation to fracture first increase and then decrease. Among the three investigated alloys, the largest UTS （178 MPa） and the highest elongation to fracture （6.5%） are obtained for the 2.0Zn alloy. In addition, the corrosion rate increases with increasing Zn content. This paper provides on updated investigation of the alloy composi- tion-microstxucture-property relationships of different Zn-containing Mg-Zn-Ca alloys.
基金the financial support for this work from the National Natural Science Foundation of China(Nos.U1764254,51871166)the Tianjin Natural Science Foundation,China(No.20JCYBJC00620)。
基金Project(NCET-11-0554)supported by the Program for New Century Excellent Talents in UniversityProject(2011BAE22B04)supportedby the National Key Technology R&D Program of ChinaProject(51271206)supported by the National Natural Science Foundation of China
文摘Mg69Zn27Ca4 alloys with diameters of 1.5, 2 and 3 mm were fabricated using copper mold injection casting method. Microstructural analysis reveals that the alloy with a diameter of 1.5 mm is almost completely composed of amorphous phase. However, with the cooling rate decline, a little α-Mg and MgZn dendrites can be found in the amorphous matrix. Based on the microstructural and tensile results, the ductile dendrites are conceived to be highly responsible for the enhanced compressive strain from 1.3% to 3.1% by increasing the sample diameter from 1.5 mm to 3 mm. In addition, the Mg69Zn27Ca4 alloy with 1.5 mm diameter has the best corrosion properties. The current Mg-based alloys show much better corrosion resistance than the traditionally commercial wrought magnesium alloy ZK60 in simulated sea-water.