This work investigated the effects of different Y additions(0,1.5,3.0 and 4.5 wt.%)on the microstructural evolution and mechanical performance of cast Mg−3Nd−0.2Zn−0.5Zr alloy.The results show that as the Y content in...This work investigated the effects of different Y additions(0,1.5,3.0 and 4.5 wt.%)on the microstructural evolution and mechanical performance of cast Mg−3Nd−0.2Zn−0.5Zr alloy.The results show that as the Y content increases,the key secondary phases in as-cast alloys change from the Mg_(12)Nd type to the Mg_(24)Y_(5) type.Meanwhile,the number density of Zn−Zr particles in the grains of as-quenched alloys gradually decreases.HAADF-STEM observations of peak-aged samples reveal that element Y is greatly enriched in the globularβ¢precipitates,leading to a significantly increased volume fraction and promoted precipitation kinetics ofβ¢precipitates,resulting in enhanced strength of the alloy.Tensile tests reveal that,with the addition of 4.5 wt.%Y,the yield strength of the base alloy is substantially increased by 88 and 61 MPa after being aged at 200 and 225°C under peak-aged conditions,respectively.展开更多
基金supported by the National Natural Science Foundation of China(Nos.U2037601,51775334 and 51821001)the National Key Research&Development Program of China(No.2016YFB0701205)+2 种基金the Joint Innovation Fund of CALT and College,China(No.CALT2020-TS07)the Open Fund of State Key Laboratory of Advanced Forming Technology and Equipment,China(No.SKL2020005)the Research Program of Joint Research Center of Advanced Spaceflight Technologies,China(No.USCAST2020-14).
文摘This work investigated the effects of different Y additions(0,1.5,3.0 and 4.5 wt.%)on the microstructural evolution and mechanical performance of cast Mg−3Nd−0.2Zn−0.5Zr alloy.The results show that as the Y content increases,the key secondary phases in as-cast alloys change from the Mg_(12)Nd type to the Mg_(24)Y_(5) type.Meanwhile,the number density of Zn−Zr particles in the grains of as-quenched alloys gradually decreases.HAADF-STEM observations of peak-aged samples reveal that element Y is greatly enriched in the globularβ¢precipitates,leading to a significantly increased volume fraction and promoted precipitation kinetics ofβ¢precipitates,resulting in enhanced strength of the alloy.Tensile tests reveal that,with the addition of 4.5 wt.%Y,the yield strength of the base alloy is substantially increased by 88 and 61 MPa after being aged at 200 and 225°C under peak-aged conditions,respectively.