In this work,a high-strength Mg–10Gd–6Y–1.5Zn–0.5Zr(wt.%)alloy was fabricated by successive multi-pass equal channel angular pressing(ECAP).The microstructure and mechanical property of as-cast and ECAP alloys wer...In this work,a high-strength Mg–10Gd–6Y–1.5Zn–0.5Zr(wt.%)alloy was fabricated by successive multi-pass equal channel angular pressing(ECAP).The microstructure and mechanical property of as-cast and ECAP alloys were systematically researched by X-ray diffractometer,scanning electron microscopy,transmission electron microscopy and compression test.The results show that the microstructure of as-cast alloy consists ofα-Mg grains,Mg24Y5 networks,18R blocks,fine 14H lamellas,and fewY-rich particles.After 8 passes ECAP,dynamic recrystallization ofα-Mg is developed and their average grain size decreases to about 1μm.The network Mg_(24)Y_(5) phase at grain boundaries is broken into small particles with average diameter lower than 0.5μm.Moreover,18R blocks are kinked and delaminated,or broken into small particles and blended with Mg24Y5 particles.14H lamellas grow gradually or are dynamically precipitated within certainα-Mg grains.Compression tests indicate that 8p ECAP alloy exhibits excellent mechanical property with compressive strength of 537 MPa and fracture strain of 17.0%.The significant improvement for both strength and ductility of deformed alloy could be ascribed to DRX grains,refined Mg24Y5 particles,18R kinking and dynamical precipitation of 14H.展开更多
Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on ...Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on the mechanical properties and wear behavior of the alloy were studied. The RUE process was carried out for 4 passes in total, starting at 0 ℃ and decreasing by 10 ℃ for each pass. The results showed that as the number of RUE passes increased, the grain refinement effect was obvious, and the second phase in the alloy was evenly distributed. Room temperature tensile properties of the alloy and the deepening of the RUE degree showed a positive correlation trend, which was due to the grain refinement, uniform distribution of the second phase and texture weakening. And the microhardness of the alloy showed that the microhardness of RUE is the largest in 2 passes. The change in microhardness was the result of dynamic competition between the softening effect of DRX and the work hardening effect. In addition, the wear resistance of the alloy showed a positive correlation with the degree of RUE under low load conditions. When the applied load was higher, the wear resistance of the alloy treated with RUE decreased compared to the initial state alloy. This phenomenon was mainly due to the presence of oxidative wear on the surface of the alloy, which could balance the positive contribution of severe plastic deformation to wear resistance to a certain extent.展开更多
基金the Natural Science Foundation of Jiangsu Province of China(No.BK20160869)the financial support from the Nantong Science and Technology Project(No.GY12015009)+1 种基金the Fundamental Research Funds for the Central Universities(No.2015B01314)the National Natural Science Foundation of China(No.51501039).
文摘In this work,a high-strength Mg–10Gd–6Y–1.5Zn–0.5Zr(wt.%)alloy was fabricated by successive multi-pass equal channel angular pressing(ECAP).The microstructure and mechanical property of as-cast and ECAP alloys were systematically researched by X-ray diffractometer,scanning electron microscopy,transmission electron microscopy and compression test.The results show that the microstructure of as-cast alloy consists ofα-Mg grains,Mg24Y5 networks,18R blocks,fine 14H lamellas,and fewY-rich particles.After 8 passes ECAP,dynamic recrystallization ofα-Mg is developed and their average grain size decreases to about 1μm.The network Mg_(24)Y_(5) phase at grain boundaries is broken into small particles with average diameter lower than 0.5μm.Moreover,18R blocks are kinked and delaminated,or broken into small particles and blended with Mg24Y5 particles.14H lamellas grow gradually or are dynamically precipitated within certainα-Mg grains.Compression tests indicate that 8p ECAP alloy exhibits excellent mechanical property with compressive strength of 537 MPa and fracture strain of 17.0%.The significant improvement for both strength and ductility of deformed alloy could be ascribed to DRX grains,refined Mg24Y5 particles,18R kinking and dynamical precipitation of 14H.
基金financially supported by the Natural Science Foundation of Shanxi Province (No. 201901D111176)the Joint Funds of the National Natural Science Foundation of china (Grant No. U20A20230)+3 种基金the Bureau of science, technology and industry for National Defense of China (No. WDZC2019JJ006)the Key R&D program of Shanxi Province (International Cooperation) (No. 201903D421036)the National Natural Science Foundation of China (Grant No. 52075501)Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi (No. 2018002)。
文摘Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on the mechanical properties and wear behavior of the alloy were studied. The RUE process was carried out for 4 passes in total, starting at 0 ℃ and decreasing by 10 ℃ for each pass. The results showed that as the number of RUE passes increased, the grain refinement effect was obvious, and the second phase in the alloy was evenly distributed. Room temperature tensile properties of the alloy and the deepening of the RUE degree showed a positive correlation trend, which was due to the grain refinement, uniform distribution of the second phase and texture weakening. And the microhardness of the alloy showed that the microhardness of RUE is the largest in 2 passes. The change in microhardness was the result of dynamic competition between the softening effect of DRX and the work hardening effect. In addition, the wear resistance of the alloy showed a positive correlation with the degree of RUE under low load conditions. When the applied load was higher, the wear resistance of the alloy treated with RUE decreased compared to the initial state alloy. This phenomenon was mainly due to the presence of oxidative wear on the surface of the alloy, which could balance the positive contribution of severe plastic deformation to wear resistance to a certain extent.