Microstructure of Mg-8Zn-4Al-1Ca aged alloy

The microstructure of Mg-8Zn-4Al-1Ca aged alloy was investigated by TEM and HRTEM. The results show that the hardening produced in the Mg-8Zn-4Al-1Ca alloy is considerably higher than that in the Mg-8Zn-4A1 alloy. A dense dispersion of disc-like Ca2Mg6Zn3 precipitates are formed in Mg-8Zn-4Al-1Ca alloy aged at 160 ℃ for 16 h. In addition, the lattice distortions, honeycomb-looking Moir＆#233; fringes, edge dislocations and dislocation loop also exist in the microstructure. The precipitates of alloy aged at 160 ℃ for 48 h are coarse disc-like and fine dispersed grainy. When the alloy is subjected to aging at 160 ℃ for 227 h, the microstructure consists of numerous MgZn2 precipitates and Ca2Mg6Zn3 precipitates. All the analyses show that Ca is a particularly effective trace addition in improving the age-hardening and postponing the formation of MgZn2 precipitates in Mg-8Zn-4Al alloy aged at 160 ℃.

均匀化退火等温冷却对Mg-12Al-1Zn镁合金组织性能的影响

研究了均匀化退火等温冷却对石墨型铸造Mg-12Al-1Zn镁合金组织及性能的影响，探讨不同等温温度和保温时间对p- Mg17Al12相析出形貌和合金力学性能的影响.结果表明：合金在420℃固溶均匀化24h 后再分别经200℃、250℃、300℃等温冷却1~6h.β-Mg17Al12相相相析出量随着时间的延长而增加，形态也随着时间的延长发生变化，主要以层片状组织析出.合金在420℃保温24h 再经250益保温6h 后，布氏硬度达到最高值90.7H B.

均匀化退火对Mg-12Al-1Zn合金组织和性能的影响

对石墨型铸造Mg-12Al-1Zn合金均匀化退火后的组织及性能进行了研究。结果表明:在420℃保温24 h均匀化退火后,β-Mg_(17)Al_(12)相以层片状组织析出,随着退火冷却速度的降低,β-Mg_(17)Al_(12)相的析出量逐渐增多,在冷却速度为0.0201 K/s时完全析出,平均层片间距随冷却速度降低而增大,并有少量溶断。经均匀化退火后,合金的布氏硬度值比铸态有所提高,且随着冷却速度的降低,布氏硬度先增大后减小,在冷却速度为0.0201 K/s时达到最高值87.7 HB。

均匀化退火等温冷却对Mg-10Al-1Zn镁合金组织性能的影响

对Mg-10Al-1Zn镁合金进行均匀化退火等温冷却处理,探讨等温温度和时间对β-Mg17Al12相析出形貌和合金力学性能的影响。研究结果表明：在420℃保温24h再经200~300℃保温1~6h后,β-Mg17Al12相均以层片状形态均匀析出。β-Mg17Al12相析出量随时间延长而增加,平均层片间距随等温温度升高而增大。合金在420℃保温24h再经250℃保温2h后,布氏硬度达到最高值80.1HB。

均匀化退火对高铝镁合金组织性能的影响

以石墨型铸造Mg-10Al-1Zn合金为原料,通过观察样品的显微组织、测试样品的布氏硬度,来分析均匀化处理后不同的冷却速度对样品组织和性能的影响。结果表明:在420℃保温24 h连续冷却后,合金中的β-Mg17Al12相均以层片状的形态析出。随着冷却速度的减小,β-Mg17Al12相析出数量逐渐增多直至完全析出。经均匀化连续退火后,合金的布氏硬度值均比铸态58.7 HB有所提高,且随着冷却速度的减小布氏硬度呈现先升高后下降的趋势,在冷却速度为0.0183 K·s-1时到达最高值81.2 HB。