Creep aging forming(CAF) is a potential process used to manufacture large integral components of magnesium(Mg) alloys. The selected stress plays a crucial role in creep aging processes but the mechanism by which stres...Creep aging forming(CAF) is a potential process used to manufacture large integral components of magnesium(Mg) alloys. The selected stress plays a crucial role in creep aging processes but the mechanism by which stress loading method affects creep aging of Mg alloys is still unclear. In this paper, the microstructural evolution of precipitated phases and precipitation-free zones(PFZ) at grain boundaries with different stress loading modes(unstressed, unidirectional tensile stress, and cyclic stress) at 250 ℃ were investigated along with changes in mechanical properties. The results showed that the addition of stress during aging effectively promoted the precipitation of precipitated phases, while unaffecting grain size. Unidirectional tensile stress caused directional growth of β phase([1010]), as well as rotation of weave towards the basal plane texture, resulting in namely stress orientation effect. Solute atoms diffused in the direction of tensile stress while vacancies moved perpendicular to the direction of tensile stress, resulting in PFZ at grain boundaries(157.06 nm). By contrast, cyclic stresses led to the growth of β phase in three directions([1010], [1100] and [0110]). The solute atoms and vacancies were uniformly distributed in the Mg matrix instead of directional diffusion, effectively reducing the width of PFZ(112.39 nm) at the grain boundary. These features significantly improved the mechanical properties of alloy specimens after cyclic stress creep aging when compared to unidirectional stress creep aging, with yield strength(YS), ultimate tensile strength(UTS), and elongation(EL) enhanced from 171.6 MPa, 305.5 MPa, and 4.4%to 174.8 MPa, 326.3 MPa, and 6.9%, respectively.展开更多
The corrosion behaviours of Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys prepared by as-casting and extrusion were investigated in 5% NaCl aqueous solution by immersion and electrochemical tests. The microstructure indicates ...The corrosion behaviours of Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys prepared by as-casting and extrusion were investigated in 5% NaCl aqueous solution by immersion and electrochemical tests. The microstructure indicates the mean grain size of 15 μm for the extruded and 100 μm for the as-cast Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys. The corrosion morphology of as-cast sample shows pitting corrosion and little filiform corrosion, but that of the extruded sample shows pitting corrosion at the initial stage. The corrosion rate of extruded sample is higher than that of as-cast Mg-5Y-7Gd-1Nd-0.5Zr alloy according to the immersion test. The second phases containing RE acting as cathodes improve the corrosion properties. The corrosion potentials of as-cast and extruded Mg-5Y-7Gd-1Nd-0.5Zr alloys are -1.658 V and -1.591 V, respectively. The origins of the distinctive corrosion behavior of as-cast and extruded Mg-5Y-7Gd-1Nd-0.5Zr Mg alloys were discussed.展开更多
Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on ...Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on the mechanical properties and wear behavior of the alloy were studied. The RUE process was carried out for 4 passes in total, starting at 0 ℃ and decreasing by 10 ℃ for each pass. The results showed that as the number of RUE passes increased, the grain refinement effect was obvious, and the second phase in the alloy was evenly distributed. Room temperature tensile properties of the alloy and the deepening of the RUE degree showed a positive correlation trend, which was due to the grain refinement, uniform distribution of the second phase and texture weakening. And the microhardness of the alloy showed that the microhardness of RUE is the largest in 2 passes. The change in microhardness was the result of dynamic competition between the softening effect of DRX and the work hardening effect. In addition, the wear resistance of the alloy showed a positive correlation with the degree of RUE under low load conditions. When the applied load was higher, the wear resistance of the alloy treated with RUE decreased compared to the initial state alloy. This phenomenon was mainly due to the presence of oxidative wear on the surface of the alloy, which could balance the positive contribution of severe plastic deformation to wear resistance to a certain extent.展开更多
Fine grained Mg-7Gd-5Y-1.2Nd-0.5Zr alloy was investigated by dynamic compression tests using a Split Hopkinson Pressure Bar under the strain rates in the range 1000-2000 s^(-1) and the temperature range 293-573 K alon...Fine grained Mg-7Gd-5Y-1.2Nd-0.5Zr alloy was investigated by dynamic compression tests using a Split Hopkinson Pressure Bar under the strain rates in the range 1000-2000 s^(-1) and the temperature range 293-573 K along the normal direction.The microstructure was measured by optical microscopy,electron back-scattering diffraction,transmission electron microscopy and X-ray diffractometry.The results showed that Mg-7Gd-5Y-1.2Nd-0.5Zr alloy had the positive strain rate strengthening effect and thermal softening effect at high temperature.The solid solution of Gd and Y atoms in Mg-7Gd-5Y-1.2Nd-0.5Zr alloy reduced the asymmetry of α-Mg crystals and changed the critical shear stress of various deformation mechanisms.The main deformation mechanisms were prismatic slip and pyramidal(a)slip,{102}tension twinning,and dynamic recrystallization caused by local deformation such as particle-stimulated nucleation.c 2020 Published by Elsevier B.V.on behalf of Chongqing University.展开更多
The microstructures of an Mg-4Y-3Nd-0.5Zr alloy by differential pressure casting were investigated using scanning electron microscopy （SEM） and transmission electron microscopy （TEM）, and its tensile deformation b...The microstructures of an Mg-4Y-3Nd-0.5Zr alloy by differential pressure casting were investigated using scanning electron microscopy （SEM） and transmission electron microscopy （TEM）, and its tensile deformation behavior was measured using a Gleeble1500D themo-simulation machine in the temperature range of 200 to 400 ℃ at initial strain rates of 5×10^-4 to 10^-1 s^-1. Results show that the as-cast microstructure consists of primary α-Mg phase and bone-shaped Mg5RE eutectic phase distributed along the grain boundary. The eutectic phase is dissolved into the matrix after solution treatment and subsequently precipitates during peak aging. Tensile deformation tests show that the strain rate has little effect on stress under 300 ℃. Tensile stress decreases with an increase in temperature and the higher strain rate leads to an increase in stress above 300 ℃. The fracture mechanism exhibits a mixed quasi-cleavage fracture at 200 ℃, while the fracture above 300 ℃ is a ductile fracture. The dimples are melted at 400 ℃ with the lowest strain rate of 10^-4 s^-1.展开更多
The sliding friction and wear behaviors of Mg-11Y-5Gd-2Zn-0.5Zr （wt%） alloy were investigated under oil lubricant condition by pin-on-disk configuration with a constant sliding distance of 1,000 m in the temperature...The sliding friction and wear behaviors of Mg-11Y-5Gd-2Zn-0.5Zr （wt%） alloy were investigated under oil lubricant condition by pin-on-disk configuration with a constant sliding distance of 1,000 m in the temperature range of 25-200℃. Results indicate that the volumetric wear rates and average friction coefficients decrease with the increase of sliding speeds, and increase with the increase of test temperature below 150℃. The hard and thermally stable Mg12（Y,Gd）Zn phase with long-period stacking order structure in the alloy presents significant wear resistance, The wear mechanism below 100℃ is abrasive wear as a result of plastic extrusion deformation. The corporate effects of severe abrasive, oxidative, and delaminating wear result in the tribological mechanism above 100℃.展开更多
The corrosion behaviors of T5 （225 ℃, 6.5 h） and T6 （460 ℃, 2 h ＋ 225 ℃, 12 h） peak-aged Mg-7Gd- 5Y-1Nd-0.5Zr alloys with oxide films were investigated by optical microscope （OM）, scanning electron microsco...The corrosion behaviors of T5 （225 ℃, 6.5 h） and T6 （460 ℃, 2 h ＋ 225 ℃, 12 h） peak-aged Mg-7Gd- 5Y-1Nd-0.5Zr alloys with oxide films were investigated by optical microscope （OM）, scanning electron microscopy （SEM）, and energy-dispersive spectroscopy （EDS）. The weight loss rates and electrochemical tests were also analyzed. The thicknesses of T5 and T6 oxide films are roughly 0.6 and 1.0 μm, respectively. The components of oxide films mainly consist of O, Mg, Y, Nd, and Gd, and the T6 oxide film results in surfaces with larger peaks than T5 oxide film. In addition, Y, Nd, and Gd peaks are all higher than those of Mg-7Gd-5Y- 1Nd-0.5Zr alloys, but Mg peak is consistently far below than that of the alloys. The specimens could be arranged in de- creasing order of corrosion rates and corrosion current densi- ties： T6 oxide film 〈 T5 oxide film 〈 T6 without oxide film 〈 T5 without oxide film. The oxide films are compact to increase the corrosion resistance for Mg-7Gd-5Y-1Nd-0.5Zr alloys, which will provide a guiding insight into the corrosion and protection of Mg-RE alloys in atmospheric environments.展开更多
基金supported by Natural Science Foundation of Shanxi province (20210302123135,20210302123163)Science and Technology Major Project of Shanxi province (20191102008)+6 种基金Scientific and Technological Achievements Transformation Guidance Special Project of Shanxi province (202104021301022)The Ministry of Science and Higher Education of the Russian Federation for financial support under the Megagrant (No.075-15-2022-1133)the National Research Foundation (NRF) grant funded by the Ministry of Science and ICT (2015R1A2A1A01006795) of Korea through the Research Institute of Advanced MaterialsThe central government guided local science and technology development projects (YDZJSX2021A010)China Postdoctoral Science Foundation (2022M710541)the projects of International Cooperation in Shanxi (201803D421086)Research Project Supported by Shanxi Scholarship Council of China (2022- 038)。
文摘Creep aging forming(CAF) is a potential process used to manufacture large integral components of magnesium(Mg) alloys. The selected stress plays a crucial role in creep aging processes but the mechanism by which stress loading method affects creep aging of Mg alloys is still unclear. In this paper, the microstructural evolution of precipitated phases and precipitation-free zones(PFZ) at grain boundaries with different stress loading modes(unstressed, unidirectional tensile stress, and cyclic stress) at 250 ℃ were investigated along with changes in mechanical properties. The results showed that the addition of stress during aging effectively promoted the precipitation of precipitated phases, while unaffecting grain size. Unidirectional tensile stress caused directional growth of β phase([1010]), as well as rotation of weave towards the basal plane texture, resulting in namely stress orientation effect. Solute atoms diffused in the direction of tensile stress while vacancies moved perpendicular to the direction of tensile stress, resulting in PFZ at grain boundaries(157.06 nm). By contrast, cyclic stresses led to the growth of β phase in three directions([1010], [1100] and [0110]). The solute atoms and vacancies were uniformly distributed in the Mg matrix instead of directional diffusion, effectively reducing the width of PFZ(112.39 nm) at the grain boundary. These features significantly improved the mechanical properties of alloy specimens after cyclic stress creep aging when compared to unidirectional stress creep aging, with yield strength(YS), ultimate tensile strength(UTS), and elongation(EL) enhanced from 171.6 MPa, 305.5 MPa, and 4.4%to 174.8 MPa, 326.3 MPa, and 6.9%, respectively.
基金Project (2011BAE22B01) supported by the National Key Technology R&D Program of China
文摘The corrosion behaviours of Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys prepared by as-casting and extrusion were investigated in 5% NaCl aqueous solution by immersion and electrochemical tests. The microstructure indicates the mean grain size of 15 μm for the extruded and 100 μm for the as-cast Mg-5Y-7Gd-1Nd-0.5Zr magnesium alloys. The corrosion morphology of as-cast sample shows pitting corrosion and little filiform corrosion, but that of the extruded sample shows pitting corrosion at the initial stage. The corrosion rate of extruded sample is higher than that of as-cast Mg-5Y-7Gd-1Nd-0.5Zr alloy according to the immersion test. The second phases containing RE acting as cathodes improve the corrosion properties. The corrosion potentials of as-cast and extruded Mg-5Y-7Gd-1Nd-0.5Zr alloys are -1.658 V and -1.591 V, respectively. The origins of the distinctive corrosion behavior of as-cast and extruded Mg-5Y-7Gd-1Nd-0.5Zr Mg alloys were discussed.
基金financially supported by the Natural Science Foundation of Shanxi Province (No. 201901D111176)the Joint Funds of the National Natural Science Foundation of china (Grant No. U20A20230)+3 种基金the Bureau of science, technology and industry for National Defense of China (No. WDZC2019JJ006)the Key R&D program of Shanxi Province (International Cooperation) (No. 201903D421036)the National Natural Science Foundation of China (Grant No. 52075501)Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi (No. 2018002)。
文摘Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on the mechanical properties and wear behavior of the alloy were studied. The RUE process was carried out for 4 passes in total, starting at 0 ℃ and decreasing by 10 ℃ for each pass. The results showed that as the number of RUE passes increased, the grain refinement effect was obvious, and the second phase in the alloy was evenly distributed. Room temperature tensile properties of the alloy and the deepening of the RUE degree showed a positive correlation trend, which was due to the grain refinement, uniform distribution of the second phase and texture weakening. And the microhardness of the alloy showed that the microhardness of RUE is the largest in 2 passes. The change in microhardness was the result of dynamic competition between the softening effect of DRX and the work hardening effect. In addition, the wear resistance of the alloy showed a positive correlation with the degree of RUE under low load conditions. When the applied load was higher, the wear resistance of the alloy treated with RUE decreased compared to the initial state alloy. This phenomenon was mainly due to the presence of oxidative wear on the surface of the alloy, which could balance the positive contribution of severe plastic deformation to wear resistance to a certain extent.
基金National Natural Science Foundation of China(Nos.51571145,51404137)City of Ningbo"science and technology innovation 2025"major special project(new energy vehicle lightweight magnesium alloy material precision forming technology)(No.2018B10045).
文摘Fine grained Mg-7Gd-5Y-1.2Nd-0.5Zr alloy was investigated by dynamic compression tests using a Split Hopkinson Pressure Bar under the strain rates in the range 1000-2000 s^(-1) and the temperature range 293-573 K along the normal direction.The microstructure was measured by optical microscopy,electron back-scattering diffraction,transmission electron microscopy and X-ray diffractometry.The results showed that Mg-7Gd-5Y-1.2Nd-0.5Zr alloy had the positive strain rate strengthening effect and thermal softening effect at high temperature.The solid solution of Gd and Y atoms in Mg-7Gd-5Y-1.2Nd-0.5Zr alloy reduced the asymmetry of α-Mg crystals and changed the critical shear stress of various deformation mechanisms.The main deformation mechanisms were prismatic slip and pyramidal(a)slip,{102}tension twinning,and dynamic recrystallization caused by local deformation such as particle-stimulated nucleation.c 2020 Published by Elsevier B.V.on behalf of Chongqing University.
基金supported by the Ministry of Science and Technology of China through Grant 2009GJB 2001.1
文摘The microstructures of an Mg-4Y-3Nd-0.5Zr alloy by differential pressure casting were investigated using scanning electron microscopy （SEM） and transmission electron microscopy （TEM）, and its tensile deformation behavior was measured using a Gleeble1500D themo-simulation machine in the temperature range of 200 to 400 ℃ at initial strain rates of 5×10^-4 to 10^-1 s^-1. Results show that the as-cast microstructure consists of primary α-Mg phase and bone-shaped Mg5RE eutectic phase distributed along the grain boundary. The eutectic phase is dissolved into the matrix after solution treatment and subsequently precipitates during peak aging. Tensile deformation tests show that the strain rate has little effect on stress under 300 ℃. Tensile stress decreases with an increase in temperature and the higher strain rate leads to an increase in stress above 300 ℃. The fracture mechanism exhibits a mixed quasi-cleavage fracture at 200 ℃, while the fracture above 300 ℃ is a ductile fracture. The dimples are melted at 400 ℃ with the lowest strain rate of 10^-4 s^-1.
基金supported by the National Natural Science Foundation of China (No. 51074106)Key HiTech Research and Development Program of China (No. 2009AA033501)National Key Technology R&D Program of China (No. 2011BAE22B01-5)
文摘The sliding friction and wear behaviors of Mg-11Y-5Gd-2Zn-0.5Zr （wt%） alloy were investigated under oil lubricant condition by pin-on-disk configuration with a constant sliding distance of 1,000 m in the temperature range of 25-200℃. Results indicate that the volumetric wear rates and average friction coefficients decrease with the increase of sliding speeds, and increase with the increase of test temperature below 150℃. The hard and thermally stable Mg12（Y,Gd）Zn phase with long-period stacking order structure in the alloy presents significant wear resistance, The wear mechanism below 100℃ is abrasive wear as a result of plastic extrusion deformation. The corporate effects of severe abrasive, oxidative, and delaminating wear result in the tribological mechanism above 100℃.
基金financially supported by the National Natural Science Foundation of China(No.51204020)the National Basic Research Program of China(Nos.2013CB632202 and 2013CB632205)
文摘The corrosion behaviors of T5 （225 ℃, 6.5 h） and T6 （460 ℃, 2 h ＋ 225 ℃, 12 h） peak-aged Mg-7Gd- 5Y-1Nd-0.5Zr alloys with oxide films were investigated by optical microscope （OM）, scanning electron microscopy （SEM）, and energy-dispersive spectroscopy （EDS）. The weight loss rates and electrochemical tests were also analyzed. The thicknesses of T5 and T6 oxide films are roughly 0.6 and 1.0 μm, respectively. The components of oxide films mainly consist of O, Mg, Y, Nd, and Gd, and the T6 oxide film results in surfaces with larger peaks than T5 oxide film. In addition, Y, Nd, and Gd peaks are all higher than those of Mg-7Gd-5Y- 1Nd-0.5Zr alloys, but Mg peak is consistently far below than that of the alloys. The specimens could be arranged in de- creasing order of corrosion rates and corrosion current densi- ties： T6 oxide film 〈 T5 oxide film 〈 T6 without oxide film 〈 T5 without oxide film. The oxide films are compact to increase the corrosion resistance for Mg-7Gd-5Y-1Nd-0.5Zr alloys, which will provide a guiding insight into the corrosion and protection of Mg-RE alloys in atmospheric environments.