One-pass asymmetric hot extrusion performed at 673 K was applied to fabricate an AZ31 magnesium alloy sheet.Finite element method(FEM) was used to model the process of asymmetric hot-extrusion.Simulation results indic...One-pass asymmetric hot extrusion performed at 673 K was applied to fabricate an AZ31 magnesium alloy sheet.Finite element method(FEM) was used to model the process of asymmetric hot-extrusion.Simulation results indicate that strain rate gradient through the thickness introduced a grain size gradient along the thickness direction and shear deformation during the asymmetric hot-extrusion results in weakened and tilted(0002) basal texture.The asymmetric hot extrusion effectively weakens the basal texture and improves the ductility at room temperature.展开更多
Effects of Mg content on the microstructure and mechanical properties of low Zn-containing Al−xMg−3Zn−1Cu cast alloys(x=3−5,wt.%)were investigated.As Mg content increased in the as-cast alloys,the grains were refined ...Effects of Mg content on the microstructure and mechanical properties of low Zn-containing Al−xMg−3Zn−1Cu cast alloys(x=3−5,wt.%)were investigated.As Mg content increased in the as-cast alloys,the grains were refined due to enhanced growth restriction,and the formation ofη-Mg(AlZnCu)_(2) and S-Al_(2)CuMg phases was inhibited while the formation of T-Mg_(32)(AlZnCu)_(49 )phase was promoted when Mg content exceeded 4 wt.%.The increase of Mg content encumbered the solution kinetics by increasing the size of eutectic phase but accelerated and enhanced the age-hardening through expediting precipitation kinetics and elevating the number density of the precipitates.As Mg content increased,the yield strength and tensile strength of the as-cast,solution-treated and peak-aged alloys were severally improved,while the elongation of the alloys decreased.The tensile strength and elongation of the peak-aged Al−5Mg−3Zn−1Cu alloy exceed 500 MPa and 5%,respectively.Precipitation strengthening implemented by T′precipitates is the predominant strengthening mechanism in the peak-aged alloys and is enhanced by increasing Mg content.展开更多
The microstructure of Mg-8Zn-4Al-1Ca aged alloy was investigated by TEM and HRTEM. The results show that the hardening produced in the Mg-8Zn-4Al-1Ca alloy is considerably higher than that in the Mg-8Zn-4A1 alloy. A d...The microstructure of Mg-8Zn-4Al-1Ca aged alloy was investigated by TEM and HRTEM. The results show that the hardening produced in the Mg-8Zn-4Al-1Ca alloy is considerably higher than that in the Mg-8Zn-4A1 alloy. A dense dispersion of disc-like Ca2Mg6Zn3 precipitates are formed in Mg-8Zn-4Al-1Ca alloy aged at 160 ℃ for 16 h. In addition, the lattice distortions, honeycomb-looking Moir＆#233; fringes, edge dislocations and dislocation loop also exist in the microstructure. The precipitates of alloy aged at 160 ℃ for 48 h are coarse disc-like and fine dispersed grainy. When the alloy is subjected to aging at 160 ℃ for 227 h, the microstructure consists of numerous MgZn2 precipitates and Ca2Mg6Zn3 precipitates. All the analyses show that Ca is a particularly effective trace addition in improving the age-hardening and postponing the formation of MgZn2 precipitates in Mg-8Zn-4Al alloy aged at 160 ℃.展开更多
The effects of addition of minor amount of(0.5 wt.%) antimony(Sb) or gadolinium(Gd) and combined addition of Sb and Gd(0.5 wt.%,respectively) on the hot tearing susceptibility(HTS) of Mg-5Al-3Ca alloy were investigate...The effects of addition of minor amount of(0.5 wt.%) antimony(Sb) or gadolinium(Gd) and combined addition of Sb and Gd(0.5 wt.%,respectively) on the hot tearing susceptibility(HTS) of Mg-5Al-3Ca alloy were investigated experimentally using a “T-shaped” hot tearing measuring system. Various solidification parameters of the alloys were measured and calculated through thermal analysis experiments. The microstructure, grain size, and morphology of the crack zone were characterized by scanning electron microscopy and electron backscatter diffraction, and the crystal phases of the alloys were analyzed by X-ray diffraction and energy-dispersive X-ray spectroscopy. The results showed that the addition of 0.5 wt.% Gd resulted in the increase in the vulnerable temperature range(Tv) and reduced the eutectic structure content that could participate in feeding, thereby improving the HTS of the alloy. However, addition of 0.5 wt.% Sb or combined addition of Gd and Sb(0.5 wt.%, respectively) to the Mg-5Al-3Ca alloy shortened the Tvand improved the skeleton strength of the alloy, thereby reducing HTS. Moreover, significantly refined structure of Mg-5Al-3Ca-0.5Gd-0.5Sb alloy improved the feeding ability of the eutectic structure, thus the alloy exhibited the lowest HTS.展开更多
Biodegradable metals as electrodes, interconnectors, and device conductors are essential components in the emergence of transient electronics, either for passive implants or active electronic devices, especially in th...Biodegradable metals as electrodes, interconnectors, and device conductors are essential components in the emergence of transient electronics, either for passive implants or active electronic devices, especially in the fields of biomedical electronics. Magnesium and its alloys are strong candidates for biodegradable and implantable conducting materials because of their high conductivity and biocompatibility, in addition to their well-understood dissolution behavior. One critical drawback of Mg and its alloys is their considerably high dissolution rates originating from their low anodic potential, which disturbs the compatibility to biomedical applications. Herein, we introduce a single-phase thin film of a Mg-Zn binary alloy formed by sputtering, which enhances the corrosion resistance of the device electrode, and verify its applicability in biodegradable electronics. The formation of a homogeneous solid solution of single-phase Mg-3Zn was confirmed through X-ray diffraction and transmission electron microscopy. In addition, the dissolution behavior and chemistry was also investigated in various biological fluids by considering the effect of different ion species. Micro-tensile tests showed that the Mg-3Zn alloy electrode exhibited an enhanced yield strain and elongation in relation to a pure Mg electrode. Cell viability test revealed the high biocompatibility rate of the Mg-3Zn binary alloy thin film. Finally, the fabrication of a wireless heater demonstrated the integrability of biodegradable electrodes and highlighted the ability to prolong the lifecycle of thermotherapy-relevant electronics by enhancing the dissolution resistance of the Mg alloy.展开更多
基金Project(50471069)supported by the National Natural Science Foundation of China
文摘One-pass asymmetric hot extrusion performed at 673 K was applied to fabricate an AZ31 magnesium alloy sheet.Finite element method(FEM) was used to model the process of asymmetric hot-extrusion.Simulation results indicate that strain rate gradient through the thickness introduced a grain size gradient along the thickness direction and shear deformation during the asymmetric hot-extrusion results in weakened and tilted(0002) basal texture.The asymmetric hot extrusion effectively weakens the basal texture and improves the ductility at room temperature.
基金supported by the National Natural Science Foundation of China (Nos. 51674166, U1902220)the National Key R&D Program of China (No. 2021YFB3701303)。
文摘Effects of Mg content on the microstructure and mechanical properties of low Zn-containing Al−xMg−3Zn−1Cu cast alloys(x=3−5,wt.%)were investigated.As Mg content increased in the as-cast alloys,the grains were refined due to enhanced growth restriction,and the formation ofη-Mg(AlZnCu)_(2) and S-Al_(2)CuMg phases was inhibited while the formation of T-Mg_(32)(AlZnCu)_(49 )phase was promoted when Mg content exceeded 4 wt.%.The increase of Mg content encumbered the solution kinetics by increasing the size of eutectic phase but accelerated and enhanced the age-hardening through expediting precipitation kinetics and elevating the number density of the precipitates.As Mg content increased,the yield strength and tensile strength of the as-cast,solution-treated and peak-aged alloys were severally improved,while the elongation of the alloys decreased.The tensile strength and elongation of the peak-aged Al−5Mg−3Zn−1Cu alloy exceed 500 MPa and 5%,respectively.Precipitation strengthening implemented by T′precipitates is the predominant strengthening mechanism in the peak-aged alloys and is enhanced by increasing Mg content.
基金Project(51141007)supported by the National Natural Science Foundation of ChinaProject(E2013501096)supported by Hebei Province Natural Science Foundation,China
文摘The microstructure of Mg-8Zn-4Al-1Ca aged alloy was investigated by TEM and HRTEM. The results show that the hardening produced in the Mg-8Zn-4Al-1Ca alloy is considerably higher than that in the Mg-8Zn-4A1 alloy. A dense dispersion of disc-like Ca2Mg6Zn3 precipitates are formed in Mg-8Zn-4Al-1Ca alloy aged at 160 ℃ for 16 h. In addition, the lattice distortions, honeycomb-looking Moir＆#233; fringes, edge dislocations and dislocation loop also exist in the microstructure. The precipitates of alloy aged at 160 ℃ for 48 h are coarse disc-like and fine dispersed grainy. When the alloy is subjected to aging at 160 ℃ for 227 h, the microstructure consists of numerous MgZn2 precipitates and Ca2Mg6Zn3 precipitates. All the analyses show that Ca is a particularly effective trace addition in improving the age-hardening and postponing the formation of MgZn2 precipitates in Mg-8Zn-4Al alloy aged at 160 ℃.
基金financial support from Joint Research Fund Liaoning-Shenyang National Laboratory for Materials Science (2019JH3/30100014)Liaoning Bai Qian Wan Talents Program. Liaoning Revitalization Talents Program (Nos. XLYC1807021 and 1907007)+2 种基金High Level Innovation Team of Liaoning Province(XLYC1908006)Project of Liaoning Education Department(Nos. LQGD2019002, and LJGD2020008)Liaoning Nature Fund Guidance Plan (No. 2019-ZD-0210)。
文摘The effects of addition of minor amount of(0.5 wt.%) antimony(Sb) or gadolinium(Gd) and combined addition of Sb and Gd(0.5 wt.%,respectively) on the hot tearing susceptibility(HTS) of Mg-5Al-3Ca alloy were investigated experimentally using a “T-shaped” hot tearing measuring system. Various solidification parameters of the alloys were measured and calculated through thermal analysis experiments. The microstructure, grain size, and morphology of the crack zone were characterized by scanning electron microscopy and electron backscatter diffraction, and the crystal phases of the alloys were analyzed by X-ray diffraction and energy-dispersive X-ray spectroscopy. The results showed that the addition of 0.5 wt.% Gd resulted in the increase in the vulnerable temperature range(Tv) and reduced the eutectic structure content that could participate in feeding, thereby improving the HTS of the alloy. However, addition of 0.5 wt.% Sb or combined addition of Gd and Sb(0.5 wt.%, respectively) to the Mg-5Al-3Ca alloy shortened the Tvand improved the skeleton strength of the alloy, thereby reducing HTS. Moreover, significantly refined structure of Mg-5Al-3Ca-0.5Gd-0.5Sb alloy improved the feeding ability of the eutectic structure, thus the alloy exhibited the lowest HTS.
基金supported by the Renewable Energy Technology Development (Develop technology to enhance reliability and durability for parts of hydrogen storage tank system) (2022303004020B) grant funded by the Korea Energy Technology Evaluation Planning (KETEP)the Ministry of Science and ICT (Development Project for Emerging Research Instruments Technology),(Project Number: (2022)ERIC)06_1Commercialization Promotion Agency for R&D Outcomes (COMPA)。
文摘Biodegradable metals as electrodes, interconnectors, and device conductors are essential components in the emergence of transient electronics, either for passive implants or active electronic devices, especially in the fields of biomedical electronics. Magnesium and its alloys are strong candidates for biodegradable and implantable conducting materials because of their high conductivity and biocompatibility, in addition to their well-understood dissolution behavior. One critical drawback of Mg and its alloys is their considerably high dissolution rates originating from their low anodic potential, which disturbs the compatibility to biomedical applications. Herein, we introduce a single-phase thin film of a Mg-Zn binary alloy formed by sputtering, which enhances the corrosion resistance of the device electrode, and verify its applicability in biodegradable electronics. The formation of a homogeneous solid solution of single-phase Mg-3Zn was confirmed through X-ray diffraction and transmission electron microscopy. In addition, the dissolution behavior and chemistry was also investigated in various biological fluids by considering the effect of different ion species. Micro-tensile tests showed that the Mg-3Zn alloy electrode exhibited an enhanced yield strain and elongation in relation to a pure Mg electrode. Cell viability test revealed the high biocompatibility rate of the Mg-3Zn binary alloy thin film. Finally, the fabrication of a wireless heater demonstrated the integrability of biodegradable electrodes and highlighted the ability to prolong the lifecycle of thermotherapy-relevant electronics by enhancing the dissolution resistance of the Mg alloy.