The effects of addition of minor amount of(0.5 wt.%) antimony(Sb) or gadolinium(Gd) and combined addition of Sb and Gd(0.5 wt.%,respectively) on the hot tearing susceptibility(HTS) of Mg-5Al-3Ca alloy were investigate...The effects of addition of minor amount of(0.5 wt.%) antimony(Sb) or gadolinium(Gd) and combined addition of Sb and Gd(0.5 wt.%,respectively) on the hot tearing susceptibility(HTS) of Mg-5Al-3Ca alloy were investigated experimentally using a “T-shaped” hot tearing measuring system. Various solidification parameters of the alloys were measured and calculated through thermal analysis experiments. The microstructure, grain size, and morphology of the crack zone were characterized by scanning electron microscopy and electron backscatter diffraction, and the crystal phases of the alloys were analyzed by X-ray diffraction and energy-dispersive X-ray spectroscopy. The results showed that the addition of 0.5 wt.% Gd resulted in the increase in the vulnerable temperature range(Tv) and reduced the eutectic structure content that could participate in feeding, thereby improving the HTS of the alloy. However, addition of 0.5 wt.% Sb or combined addition of Gd and Sb(0.5 wt.%, respectively) to the Mg-5Al-3Ca alloy shortened the Tvand improved the skeleton strength of the alloy, thereby reducing HTS. Moreover, significantly refined structure of Mg-5Al-3Ca-0.5Gd-0.5Sb alloy improved the feeding ability of the eutectic structure, thus the alloy exhibited the lowest HTS.展开更多
ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that...ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.展开更多
Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on ...Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on the mechanical properties and wear behavior of the alloy were studied. The RUE process was carried out for 4 passes in total, starting at 0 ℃ and decreasing by 10 ℃ for each pass. The results showed that as the number of RUE passes increased, the grain refinement effect was obvious, and the second phase in the alloy was evenly distributed. Room temperature tensile properties of the alloy and the deepening of the RUE degree showed a positive correlation trend, which was due to the grain refinement, uniform distribution of the second phase and texture weakening. And the microhardness of the alloy showed that the microhardness of RUE is the largest in 2 passes. The change in microhardness was the result of dynamic competition between the softening effect of DRX and the work hardening effect. In addition, the wear resistance of the alloy showed a positive correlation with the degree of RUE under low load conditions. When the applied load was higher, the wear resistance of the alloy treated with RUE decreased compared to the initial state alloy. This phenomenon was mainly due to the presence of oxidative wear on the surface of the alloy, which could balance the positive contribution of severe plastic deformation to wear resistance to a certain extent.展开更多
To understand the solidification pathway and microstructure evolution of Mg-9Al-2Ca alloy,the cooling curve of the alloy solidified under furnace cooling was measured and the water-quenched samples were observed.The e...To understand the solidification pathway and microstructure evolution of Mg-9Al-2Ca alloy,the cooling curve of the alloy solidified under furnace cooling was measured and the water-quenched samples were observed.The experimental results show that the matrix phase of α-Mg dendrites is first generated at 596℃ during the solidification process,then the eutectic phases of Al_(2)Ca and Mg_(17)Al_(12) are formed at 518 and 447℃,respectively,and the solidification is terminated at 436℃.In the process of solidification,the seaweed dendrites of α-Mg get coarser and are gradually transformed into the global dendrites;besides,the secondary dendrite arms spacing(SDAS)of α-Mg as well as the solid fraction are both increased,while the increasing rate of SDAS of α-Mg and the solid fraction in the temperature region of 600-550℃ is faster than that in the temperature region of 550-436℃.And a power function relationship can be used to illustrate the change of the SDAS and the solid fraction with the temperature of solidification.展开更多
In this work,a new(Y,Gd)H_(2) precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD,SEM with EDS,TEM with EDS techniques and thermodynamics analysis.Results show that t...In this work,a new(Y,Gd)H_(2) precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD,SEM with EDS,TEM with EDS techniques and thermodynamics analysis.Results show that the as-cast alloy contains α-Mg,Mg_(24)(Gd,Y)_(5),and(Y,Gd)H_(2) phase.The(Y,Gd)H_(2) phase usually forms near the eutectic phase Mg_(24)(Gd,Y)_(5) or in the α-Mg grains,displaying a rectangle-shape.The Mg_(24)(Gd,Y)_(5) and(Y,Gd)H_(2) phases crystalize in bcc and fcc structure,respectively,and the(Y,Gd)H_(2) phase has a semi-coherent relationship with α-Mg matrix.The thermodynamics calculation results reveal that the hydrogen dissolved in the melt leads to the formation of hydrides.It is also found that the(Y,Gd)H_(2) hydride can form directly from the liquid phase during solidification.Additionally,it can precipitate by the decomposition of Mg_(24)(Gd,Y)_(5) phase due to absorbing hydrogen from the remaining melt.展开更多
基金financial support from Joint Research Fund Liaoning-Shenyang National Laboratory for Materials Science (2019JH3/30100014)Liaoning Bai Qian Wan Talents Program. Liaoning Revitalization Talents Program (Nos. XLYC1807021 and 1907007)+2 种基金High Level Innovation Team of Liaoning Province(XLYC1908006)Project of Liaoning Education Department(Nos. LQGD2019002, and LJGD2020008)Liaoning Nature Fund Guidance Plan (No. 2019-ZD-0210)。
文摘The effects of addition of minor amount of(0.5 wt.%) antimony(Sb) or gadolinium(Gd) and combined addition of Sb and Gd(0.5 wt.%,respectively) on the hot tearing susceptibility(HTS) of Mg-5Al-3Ca alloy were investigated experimentally using a “T-shaped” hot tearing measuring system. Various solidification parameters of the alloys were measured and calculated through thermal analysis experiments. The microstructure, grain size, and morphology of the crack zone were characterized by scanning electron microscopy and electron backscatter diffraction, and the crystal phases of the alloys were analyzed by X-ray diffraction and energy-dispersive X-ray spectroscopy. The results showed that the addition of 0.5 wt.% Gd resulted in the increase in the vulnerable temperature range(Tv) and reduced the eutectic structure content that could participate in feeding, thereby improving the HTS of the alloy. However, addition of 0.5 wt.% Sb or combined addition of Gd and Sb(0.5 wt.%, respectively) to the Mg-5Al-3Ca alloy shortened the Tvand improved the skeleton strength of the alloy, thereby reducing HTS. Moreover, significantly refined structure of Mg-5Al-3Ca-0.5Gd-0.5Sb alloy improved the feeding ability of the eutectic structure, thus the alloy exhibited the lowest HTS.
基金Funded by the National Natural Science Foundation of China(No.51401155)the School Foundation(No.XAGDXJJ1012)The Open Fund of Shaanxi Key Laboratory of Photoelectric Functional Materials and Devices(No.ZSKJ201416)
文摘ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.
基金financially supported by the Natural Science Foundation of Shanxi Province (No. 201901D111176)the Joint Funds of the National Natural Science Foundation of china (Grant No. U20A20230)+3 种基金the Bureau of science, technology and industry for National Defense of China (No. WDZC2019JJ006)the Key R&D program of Shanxi Province (International Cooperation) (No. 201903D421036)the National Natural Science Foundation of China (Grant No. 52075501)Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi (No. 2018002)。
文摘Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on the mechanical properties and wear behavior of the alloy were studied. The RUE process was carried out for 4 passes in total, starting at 0 ℃ and decreasing by 10 ℃ for each pass. The results showed that as the number of RUE passes increased, the grain refinement effect was obvious, and the second phase in the alloy was evenly distributed. Room temperature tensile properties of the alloy and the deepening of the RUE degree showed a positive correlation trend, which was due to the grain refinement, uniform distribution of the second phase and texture weakening. And the microhardness of the alloy showed that the microhardness of RUE is the largest in 2 passes. The change in microhardness was the result of dynamic competition between the softening effect of DRX and the work hardening effect. In addition, the wear resistance of the alloy showed a positive correlation with the degree of RUE under low load conditions. When the applied load was higher, the wear resistance of the alloy treated with RUE decreased compared to the initial state alloy. This phenomenon was mainly due to the presence of oxidative wear on the surface of the alloy, which could balance the positive contribution of severe plastic deformation to wear resistance to a certain extent.
基金Funded by the Ph D Research Startup Foundation of Jining University(No.2017BSZX02)。
文摘To understand the solidification pathway and microstructure evolution of Mg-9Al-2Ca alloy,the cooling curve of the alloy solidified under furnace cooling was measured and the water-quenched samples were observed.The experimental results show that the matrix phase of α-Mg dendrites is first generated at 596℃ during the solidification process,then the eutectic phases of Al_(2)Ca and Mg_(17)Al_(12) are formed at 518 and 447℃,respectively,and the solidification is terminated at 436℃.In the process of solidification,the seaweed dendrites of α-Mg get coarser and are gradually transformed into the global dendrites;besides,the secondary dendrite arms spacing(SDAS)of α-Mg as well as the solid fraction are both increased,while the increasing rate of SDAS of α-Mg and the solid fraction in the temperature region of 600-550℃ is faster than that in the temperature region of 550-436℃.And a power function relationship can be used to illustrate the change of the SDAS and the solid fraction with the temperature of solidification.
基金financially supported by the Key Project of Equipment Pre-research Field Fund under Grant No.61409230407the National Natural Science Foundation of China(NSFC)under Grant No.51601054the Central Government Guides Local Science and Technology Development Fund Projects under Grant No.206Z1005G。
文摘In this work,a new(Y,Gd)H_(2) precipitate was identified and systematically investigated in the as-cast Mg-6Gd-3Y-0.5Zr alloy by XRD,SEM with EDS,TEM with EDS techniques and thermodynamics analysis.Results show that the as-cast alloy contains α-Mg,Mg_(24)(Gd,Y)_(5),and(Y,Gd)H_(2) phase.The(Y,Gd)H_(2) phase usually forms near the eutectic phase Mg_(24)(Gd,Y)_(5) or in the α-Mg grains,displaying a rectangle-shape.The Mg_(24)(Gd,Y)_(5) and(Y,Gd)H_(2) phases crystalize in bcc and fcc structure,respectively,and the(Y,Gd)H_(2) phase has a semi-coherent relationship with α-Mg matrix.The thermodynamics calculation results reveal that the hydrogen dissolved in the melt leads to the formation of hydrides.It is also found that the(Y,Gd)H_(2) hydride can form directly from the liquid phase during solidification.Additionally,it can precipitate by the decomposition of Mg_(24)(Gd,Y)_(5) phase due to absorbing hydrogen from the remaining melt.
基金Project(51141007)supported by the National Natural Science Foundation of ChinaProject(E2013501096)supported by Hebei Province Natural Science Foundation,China