The effects of the ultrasonic treatment on the microstructure and mechanical properties of Mg-6Zn-0.5Y-2Sn alloy were investigated. The results show that the ultrasonic treatment has significant effect on the microstr...The effects of the ultrasonic treatment on the microstructure and mechanical properties of Mg-6Zn-0.5Y-2Sn alloy were investigated. The results show that the ultrasonic treatment has significant effect on the microstructure and mechanical properties of Mg-6Zn-0.5Y-2Sn alloy. The phases in Mg-6Zn-0.5Y-2Sn alloy are α-Mg, MgZn2, MgSnY, Mg2Sn, and a small amount of I-phase. With the application of ultrasonic treatment, I-phase nearly disappears, and with increasing the ultrasonic treatment power, the coarse dendrites gradually change into roundish equiaxed grains. The second phases at the α-Mg boundaries transform from coarse, semicontinuous and non-uniform to fine, discontinuous, uniform and dispersive. When the ultrasonic treatment power is 700 W, the best comprehensive mechanical properties of Mg-6Zn-0.5Y-2Sn alloy are obtained. Compared with the untreated alloy, the 0.2%tensile yield strength, ultimate tensile strength and elongation are improved by 28%, 30%and 67%, respectively.展开更多
In this work,a high-strength Mg–10Gd–6Y–1.5Zn–0.5Zr(wt.%)alloy was fabricated by successive multi-pass equal channel angular pressing(ECAP).The microstructure and mechanical property of as-cast and ECAP alloys wer...In this work,a high-strength Mg–10Gd–6Y–1.5Zn–0.5Zr(wt.%)alloy was fabricated by successive multi-pass equal channel angular pressing(ECAP).The microstructure and mechanical property of as-cast and ECAP alloys were systematically researched by X-ray diffractometer,scanning electron microscopy,transmission electron microscopy and compression test.The results show that the microstructure of as-cast alloy consists ofα-Mg grains,Mg24Y5 networks,18R blocks,fine 14H lamellas,and fewY-rich particles.After 8 passes ECAP,dynamic recrystallization ofα-Mg is developed and their average grain size decreases to about 1μm.The network Mg_(24)Y_(5) phase at grain boundaries is broken into small particles with average diameter lower than 0.5μm.Moreover,18R blocks are kinked and delaminated,or broken into small particles and blended with Mg24Y5 particles.14H lamellas grow gradually or are dynamically precipitated within certainα-Mg grains.Compression tests indicate that 8p ECAP alloy exhibits excellent mechanical property with compressive strength of 537 MPa and fracture strain of 17.0%.The significant improvement for both strength and ductility of deformed alloy could be ascribed to DRX grains,refined Mg24Y5 particles,18R kinking and dynamical precipitation of 14H.展开更多
Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on ...Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on the mechanical properties and wear behavior of the alloy were studied. The RUE process was carried out for 4 passes in total, starting at 0 ℃ and decreasing by 10 ℃ for each pass. The results showed that as the number of RUE passes increased, the grain refinement effect was obvious, and the second phase in the alloy was evenly distributed. Room temperature tensile properties of the alloy and the deepening of the RUE degree showed a positive correlation trend, which was due to the grain refinement, uniform distribution of the second phase and texture weakening. And the microhardness of the alloy showed that the microhardness of RUE is the largest in 2 passes. The change in microhardness was the result of dynamic competition between the softening effect of DRX and the work hardening effect. In addition, the wear resistance of the alloy showed a positive correlation with the degree of RUE under low load conditions. When the applied load was higher, the wear resistance of the alloy treated with RUE decreased compared to the initial state alloy. This phenomenon was mainly due to the presence of oxidative wear on the surface of the alloy, which could balance the positive contribution of severe plastic deformation to wear resistance to a certain extent.展开更多
基金Project(cstc2015jcyj BX0036)supported by Chongqing Research Program of Basic Research and Frontier Technology,ChinaProject(51571040)supported by the National Natural Science Foundation of ChinaProject supported by the Sharing Fund of Chongqing University’s Large-scale Equipment,China
文摘The effects of the ultrasonic treatment on the microstructure and mechanical properties of Mg-6Zn-0.5Y-2Sn alloy were investigated. The results show that the ultrasonic treatment has significant effect on the microstructure and mechanical properties of Mg-6Zn-0.5Y-2Sn alloy. The phases in Mg-6Zn-0.5Y-2Sn alloy are α-Mg, MgZn2, MgSnY, Mg2Sn, and a small amount of I-phase. With the application of ultrasonic treatment, I-phase nearly disappears, and with increasing the ultrasonic treatment power, the coarse dendrites gradually change into roundish equiaxed grains. The second phases at the α-Mg boundaries transform from coarse, semicontinuous and non-uniform to fine, discontinuous, uniform and dispersive. When the ultrasonic treatment power is 700 W, the best comprehensive mechanical properties of Mg-6Zn-0.5Y-2Sn alloy are obtained. Compared with the untreated alloy, the 0.2%tensile yield strength, ultimate tensile strength and elongation are improved by 28%, 30%and 67%, respectively.
基金National Key Research and Development Program of China(2016YFB0301100)Chongqing Research Program of Basic Research and Frontier Technology(cstc2015jcyjBX0036)+1 种基金National Natural Science Foundation of China(51571040)Sharing Fund of Chongqing University’s Large-Scale Equipment
基金the Natural Science Foundation of Jiangsu Province of China(No.BK20160869)the financial support from the Nantong Science and Technology Project(No.GY12015009)+1 种基金the Fundamental Research Funds for the Central Universities(No.2015B01314)the National Natural Science Foundation of China(No.51501039).
文摘In this work,a high-strength Mg–10Gd–6Y–1.5Zn–0.5Zr(wt.%)alloy was fabricated by successive multi-pass equal channel angular pressing(ECAP).The microstructure and mechanical property of as-cast and ECAP alloys were systematically researched by X-ray diffractometer,scanning electron microscopy,transmission electron microscopy and compression test.The results show that the microstructure of as-cast alloy consists ofα-Mg grains,Mg24Y5 networks,18R blocks,fine 14H lamellas,and fewY-rich particles.After 8 passes ECAP,dynamic recrystallization ofα-Mg is developed and their average grain size decreases to about 1μm.The network Mg_(24)Y_(5) phase at grain boundaries is broken into small particles with average diameter lower than 0.5μm.Moreover,18R blocks are kinked and delaminated,or broken into small particles and blended with Mg24Y5 particles.14H lamellas grow gradually or are dynamically precipitated within certainα-Mg grains.Compression tests indicate that 8p ECAP alloy exhibits excellent mechanical property with compressive strength of 537 MPa and fracture strain of 17.0%.The significant improvement for both strength and ductility of deformed alloy could be ascribed to DRX grains,refined Mg24Y5 particles,18R kinking and dynamical precipitation of 14H.
基金financially supported by the Natural Science Foundation of Shanxi Province (No. 201901D111176)the Joint Funds of the National Natural Science Foundation of china (Grant No. U20A20230)+3 种基金the Bureau of science, technology and industry for National Defense of China (No. WDZC2019JJ006)the Key R&D program of Shanxi Province (International Cooperation) (No. 201903D421036)the National Natural Science Foundation of China (Grant No. 52075501)Scientific and Technological Innovation Programs of Higher Education Institutions in Shanxi (No. 2018002)。
文摘Based on the deforming technique of severe plastic deformation(SPD), the grain refinement of a Mg-9Gd-3Y-2Zn-0.5Zr alloy treated with decreasing temperature reciprocating upsetting-extrusion(RUE) and its influence on the mechanical properties and wear behavior of the alloy were studied. The RUE process was carried out for 4 passes in total, starting at 0 ℃ and decreasing by 10 ℃ for each pass. The results showed that as the number of RUE passes increased, the grain refinement effect was obvious, and the second phase in the alloy was evenly distributed. Room temperature tensile properties of the alloy and the deepening of the RUE degree showed a positive correlation trend, which was due to the grain refinement, uniform distribution of the second phase and texture weakening. And the microhardness of the alloy showed that the microhardness of RUE is the largest in 2 passes. The change in microhardness was the result of dynamic competition between the softening effect of DRX and the work hardening effect. In addition, the wear resistance of the alloy showed a positive correlation with the degree of RUE under low load conditions. When the applied load was higher, the wear resistance of the alloy treated with RUE decreased compared to the initial state alloy. This phenomenon was mainly due to the presence of oxidative wear on the surface of the alloy, which could balance the positive contribution of severe plastic deformation to wear resistance to a certain extent.