The paper reports on the atomic investigation aboutβphase in Mg_(96)Gd_(2)Y_(1)Ni_(1) alloy by using the first-principles study and the high-angle annular dark-field scanning transmission electron microscope(HAADF-ST...The paper reports on the atomic investigation aboutβphase in Mg_(96)Gd_(2)Y_(1)Ni_(1) alloy by using the first-principles study and the high-angle annular dark-field scanning transmission electron microscope(HAADF-STEM)corrected by atomic Cs.By using HAADF-STEM,the rectangularβphases were observed in the underage and peak aging stages in Mg_(96)Gd_(2)Y_(1)Ni_(1) alloy.Theβphase could be precipitated from the previously precipitatedβphase,and theβphase grew in steps when it was precipitated.A special transition structure of three atomic layer thicknesses was first observed at the edge of theβphase and the structure of this interface is probably as theβ/Mg_(1) interface for the analysis of thermodynamic characterization and electronic characterization.Theβ'phase and theβ_(H) structure were precipitated only at the edge of the length directions of theβphase.Theβ'phase continues to grow into aβphase directly without the formation ofβ_(1) phase,resulting in an increase in the length of theβphase,which is discovered for the first time.展开更多
基金financially supported by the National Natural Science Foundation of China(Grant No.51825101)the National Key Research and Development Program of China(Grant No.2016YFB0701201)。
文摘The paper reports on the atomic investigation aboutβphase in Mg_(96)Gd_(2)Y_(1)Ni_(1) alloy by using the first-principles study and the high-angle annular dark-field scanning transmission electron microscope(HAADF-STEM)corrected by atomic Cs.By using HAADF-STEM,the rectangularβphases were observed in the underage and peak aging stages in Mg_(96)Gd_(2)Y_(1)Ni_(1) alloy.Theβphase could be precipitated from the previously precipitatedβphase,and theβphase grew in steps when it was precipitated.A special transition structure of three atomic layer thicknesses was first observed at the edge of theβphase and the structure of this interface is probably as theβ/Mg_(1) interface for the analysis of thermodynamic characterization and electronic characterization.Theβ'phase and theβ_(H) structure were precipitated only at the edge of the length directions of theβphase.Theβ'phase continues to grow into aβphase directly without the formation ofβ_(1) phase,resulting in an increase in the length of theβphase,which is discovered for the first time.