Nd3＋ substituted spinel ferrites with formula MgxCd1-xNd0.03Fe1.97O4（x = 0.0.2,0.4,0.6.0.8 and 1.0）were prepared by oxalate co-precipitation method using novel microwave sintering technique. AR grade sulphates were...Nd3＋ substituted spinel ferrites with formula MgxCd1-xNd0.03Fe1.97O4（x = 0.0.2,0.4,0.6.0.8 and 1.0）were prepared by oxalate co-precipitation method using novel microwave sintering technique. AR grade sulphates were used as starting chemicals. The samples were sintered at optimized power of 70 W for10 min in a microwave oven（800 W）. The structural analysis of these samples was done by using X-ray diffraction, scanning electron microscope and Fourier transform IR techniques. The XRD analysis of the synthesized ferrite confirms the formation of cubic spinel structure of ferrite. The influence of Nd3＋substitution on various structural parameters of Mg-Cd ferrites was reported. IR study indicates the spectra contain two intense absorption bands around 600 and 400 cm^（-1） in addition with four extra bands. The magnetic properties of all ferrites were studied by using a vibration sample magnetometer.The crystallite and grain size dependant magnetic properties are observed. The composition Mg_（0.6）Cd_（0.4）Nd_（0.03）Fe_（1.97）O_4 has better magnetic properties that can be used in recording media. The fast synthesis of spinel ferrites is yielded due to use of the microwave sintering technique.展开更多
文摘Nd3＋ substituted spinel ferrites with formula MgxCd1-xNd0.03Fe1.97O4（x = 0.0.2,0.4,0.6.0.8 and 1.0）were prepared by oxalate co-precipitation method using novel microwave sintering technique. AR grade sulphates were used as starting chemicals. The samples were sintered at optimized power of 70 W for10 min in a microwave oven（800 W）. The structural analysis of these samples was done by using X-ray diffraction, scanning electron microscope and Fourier transform IR techniques. The XRD analysis of the synthesized ferrite confirms the formation of cubic spinel structure of ferrite. The influence of Nd3＋substitution on various structural parameters of Mg-Cd ferrites was reported. IR study indicates the spectra contain two intense absorption bands around 600 and 400 cm^（-1） in addition with four extra bands. The magnetic properties of all ferrites were studied by using a vibration sample magnetometer.The crystallite and grain size dependant magnetic properties are observed. The composition Mg_（0.6）Cd_（0.4）Nd_（0.03）Fe_（1.97）O_4 has better magnetic properties that can be used in recording media. The fast synthesis of spinel ferrites is yielded due to use of the microwave sintering technique.