H_2 generation kinetics/thermodynamics and hydrolysis mechanism of high-performance La-doped Mg-Ni alloys in Na Cl solution——A large-scale and quick strategy to get hydrogen

In this work,La-doped Mg-Ni multiphase alloys were prepared by resistance melting furnace(RMF)and then modified by high-energy ball milling(HEBM).The hydrolysis H_(2) generation kinetics/thermodynamics of prepared alloys in Na Cl solutions have been investigated with the help of nonlinear and linear fitting by Avrami-Erofeev and Arrhenius equations.Combining the microstructure information before and after hydrolysis and thermodynamics fitting results,the hydrolysis H_(2) generation mechanism based on nucleation&growth has been elaborated.The final H_(2) generation capacities of 0La,5La,10La and 15 La alloys are 677,653,641 and 770 m L·g^(-1)H_(2) in 240 min at291 K,respectively.While,the final H_(2) generation capacities of HEBM 0La,5La,10La and 15 La alloys are 632,824,611 and 653 m L·g^(-1)H_(2) in 20 min at 291 K,respectively.The as-cast 15La alloy and HEMB 5La alloy present the best H_(2) production rates and final H_(2) production capacities,especially the HEBM 5La can rapidly achieve high H_(2) generation capacity(670 and 824 m L·g^(-1)H_(2) )at low temperature(291 K)within short time(5 and 20 min).The difference between the H_(2) generation capacities is mainly originated from the initial nucleation rate of Mg(OH)_(2) and the subsequent processes affected by the microstructures and phase compositions of the hydrolysis alloys.Relative low initial nucleation rate and fully growth of Mg(OH)_(2) nucleus are the premise of high H_(2) generation capacity due to the hydrolysis H_(2) generation process consisted by the nucleation,growth and contacting of Mg(OH)_(2) nucleus.To utilization H_(2) by designing solid state H_(2) generators using optimized Mg-based alloys is expected to be a feasible H_(2) generation strategy at the moment.

Phase component and microstructure of laser-sintered Mg-Ni alloys

The Mg-Ni hydrogen storage alloys were prepared using the laser sintering technology. The effects of laser sintering power on the phase component and the weight loss of Mg element for the Mg-Ni alloys were investigated. The samples P1, P2 and P3 consisted of five phases： Mg2Ni, MgNi2, Mg, Ni and MgO. The weight loss of Mg element remarkably increased at 1200 W. The addition of extra Mg significantly promoted the reaction between Mg and Ni. Mg2Ni, MgNi2, and a small amount of Ni and MgO phases were present in the samples PM （pestie milling） and BM （ball milling）. The sample PM has a homogeneous microstructure, and the contents of Mg2Ni and MgNi2 were approximately consistent with those of the Mg-Ni alloy under the equilibrium conditions. The maximum hydrogen storage capacity of the sample BM was 1.72 wt.% and the sample can be activated easily at 573 K （only 3 activation cycles）.

Microstructure and damping properties of LPSO phase dominant Mg-Ni-Y and Mg-Zn-Ni-Y alloys

This work studied the microstructure,mechanical properties and damping properties of Mg_(95.34)Ni_(2)Y_(2.66) and Mg_(95.34)Zn_(1)Ni_(1)Y_(2.66)alloys systematically.The difference in the evolution of the long-period stacked ordered(LPSO)phase in the two alloys during heat treatment was the focus.The morphology of the as-cast Mg_(95.34)Ni_(2)Y_(2.66)presented a disordered network.After heat treatment at 773 K for 2 hours,the eutectic phase was integrated into the matrix,and the LPSO phase maintained the 18R structure.As Zn partially replaced Ni,the crystal grains became rounded in the cast alloy,and lamellar LPSO phases and more solid solution atoms were contained in the matrix after heat treatment of the Mg_(95.34)Zn_(1)Ni_(1)Y_(2.66)alloy.Both Zn and the heat treatment had a significant effect on damping.Obvious dislocation internal friction peaks and grain boundary internal friction peaks were found after temperature-dependent damping of the Mg_(95.34)Ni_(2)Y_(2.66)and Mg_(95.34)Zn_(1)Ni_(1)Y_(2.66)alloys.After heat treatment,the dislocation peak was significantly increased,especially in the alloy Mg_(95.34)Ni_(2)Y_(2).66.The annealed Mg_(95.34)Ni_(2)Y_(2.66)alloy with a rod-shaped LPSO phase exhibited a good damping performance of 0.14 atε=10^(−3),which was due to the difference between the second phase and solid solution atom content.These factors also affected the dynamic modulus of the alloy.The results of this study will help in further development of high-damping magnesium alloys.

A_(2)B_(7)-type La-Mg-Ni alloys prepared by Mg thermal diffusion for improved hydrogen storage performance

A novel approach based on thermal diffusion was used to achieve controllable Mg content in A_(2)B_(7)-type La-Mg-Ni-based alloys.The formation mechanism of the A_(2)B_(7)-type phase as a result of the thermal diffusion process and the effect of Mg content on hydrogen storage performance were investigated.X-ray diffraction(XRD)patterns and Rietveld refinement results showed that increased Mg transformed the LaNi_(5)phase in the La_(0.74)Sm_(0.03)Y_(0.23)Ni_(4.32)Al_(0.04)precursor alloy into a superlattice structure.Scanning electron microscopy(SEM)images showed that Mg was evenly distributed in the alloy bulk.Mg in the superlattice significantly inhibited the phase decomposition of the superlattice structure during the hydrogen absorption/desorption cycles.An A_(2)B_(7)-type La_(0.57)Sm_(0.02)Y_(0.18)Mg_(0.23)Ni_(3.38)Al_(0.03)alloy composed of Gd_(2)Co_(7)and Ce_(2)Ni_(7)phases was successfully synthesized.The pressure-composition isotherm profiles showed that the alloy had a hydrogen storage capacity as high as 1.73 wt%,with good cycling stability.After 50 cycles of hydrogen absorption/desorption,the alloy retained a hydrogen storage capacity of 1.45 wt%,with a capacity retention rate of up to 84.28%.The Mg thermal diffusion process thus provides a new approach for the controlled preparation of La-Mg-Ni-based alloys.

Scanning transmission electron microscopy and atom probe tomography analysis of non-stoichiometry long-period-stacking-ordered structures in Mg-Ni-Y/Sm alloys

The long-period-stacking-ordered(LPSO)structure affects the mechanical,corrosion and hydrolysis properties of Mg alloys.The current work employs high angle annular dark field-scanning transmission electron microscopy(HAADF-STEM)and atom probe tomography(APT)to investigate the structural and local chemical information of LPSO phases formed in Mg-Ni-Y/Sm ternary alloys after extended isothermal annealing.Depending on the alloying elements and their concentrations,Mg-Ni-Y/Sm develops a two-phase LPSO+α-Mg structure in which the LPSO phase contains defects,hybrid LPSO structure,and Mg insertions.HAADF-STEM and APT indicate non-stoichiometric LPSO with incomplete Ni_(6)(Y/Sm)_(8) clusters.In addition,the APT quantitatively determines the local composition of LPSO and confirms the presence of Ni within the Mg bonding layers.These results provide insight into a better understanding of the structure and hydrolysis properties of LPSO-Mg alloys.

Effects of stoichiometric ratio La/Mg on structures and electrochemical performances of as-cast and annealed La-Mg-Ni-based A_2B_7-type electrode alloys

In order to investigate the influences of the stoichiometric ratio of La/Mg （increasing La and decreasing Mg on the same mole ratio） on the structure and electrochemical performances of the La-Mg-Ni-based A2B7-type electrode alloy, the as-cast and the annealed ternary Lao.8＋xMgo.2_xNi3.5 （x=0-0.05） electrode alloys were prepared. The characterization of electrode alloys by X-ray diffraction （XRD） and scanning electron microscopy （SEM） shows that all the as-cast and the annealed alloys hold two major phases of （La,Mg）2Ni7 and LaNi5 as well as a residual phase of LaNi3. Moreover, the increase of La/Mg ratio brings on a decline of （La,Mg）2Ni7 phase and a rise of LaNi5 and LaNi3 phases. The variation of La/Mg ratio gives rise to an evident change of the electrochemical performances of the alloys. The discharge capacities of the as-cast and the annealed alloys evidently decrease with growing the La/Mg ratio, while the cycle stabilities of the alloys visibly augment under the same condition. Furthermore, the high rate discharge ability （HRD）, the electrochemical impedance spectrum （EIS）, the Tafel polarization curves, and the potential step measurements all indicate that the electrochemical kinetic properties of the alloy electrodes increase with the La/Mg ratio rising.

Glass-forming ability and crystallization of Mg-Ni amorphous alloys with Y addition

Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) amorphous alloys were obtained by single-roller melt-spinning technique and the effect of Y addition on the glass forming ability(GFA), crystallization and micro-hardness of Mg-Ni alloys were studied. The results show that the GFA of Mg86.33Ni13.67-xYx(x=0, 1, 3, 6, 10) is improved successfully with the Y addition. The highest GFA appeares at x=6, while the reduced glass transition temperature (Trg) is 0.5225 and the supercooled liquid region(ΔTx) is 42.06 K; the position of the main diffraction halo is different for the alloys, and the maximum of the main diffraction halo of alloys with x=0, 1, 3 corresponds to the main peaks of a metastable fcc-Mg6Ni or fcc-Mg6Ni + Ni-Y intermetallic phases, and for the alloys with x=6, 10, it corresponds to Mg-Y and Ni-Y intermetallic phases; the micro-hardness of the alloys is improved with Y additions, and the highest micro-hardness is obtained at x=6 at.%, which is 960 MPa.

Effect of stoichiometry and Cu-substitution on the phase structure and hydrogen storage properties of Ml-Mg-Ni-based alloys

To improve the electrochemical properties of rare-earth-Mg-Ni-based hydrogen storage alloys, the effects of stoichiometry and Cu-substitution on the phase structure and thermodynamic properties of the alloys were studied. Nonsubstituted Ml0.80Mg0.20（Ni2.90Co0.50-Mn0.30Al0.30）x （x=0.68, 0.70, 0.72, 0.74, 0.76） alloys and Cu-substituted Ml0.80Mg0.20（Ni2.90Co0.50-yCuyMn0.30Al0.30）0.70 （y=0, 0.10, 0.30, 0.50） alloys were prepared by induction melting. Phase structure analysis shows that the nonsubstituted alloys consist of a LaNi5 phase, a LaNi3 phase, and a minor La2Ni7 phase;in addition, in the case of Cu-substitution, the Nd2Ni7 phase appears and the LaNi3 phase vanishes. Ther-modynamic tests show that the enthalpy change in the dehydriding process decreases, indicating that hydride stability decreases with in-creasing stoichiometry and increasing Cu content. The maximum discharge capacity, kinetic properties, and cycling stability of the alloy electrodes all increase and then decrease with increasing stoichiometry or increasing Cu content. Furthermore, Cu substitution for Co ame-liorates the discharge capacity, kinetics, and cycling stability of the alloy electrodes.

Influence of rapid quenching on cyclic stability of La-Mg-Ni system (AB_3-type) electrode alloys

Aiming at the improvement of the cyclic stability of La-Mg-Ni system （PuNi3-type） hydrogen storage alloy, Ni in the alloy was partly substituted by Fe. The electrode alloys of La0.7Mg0.3Co0.45Ni255-xFex （x=0, 0.1, 0.2, 0.3, 0.4） were prepared by casting and rapid quenching. The influence of the quenching on cyclic stability as well as structure of the alloys was investigated in detail. The results of electrochemical measurement indicated that rapid quenching significantly improved cyclic stability. When the quenching rate rose from 0 （As-cast was defined as a quenching rate of 0 m/s） to 30 m/s, the cyclic life of Fe-free alloy （x=-0） increased from 81 to 105 cycles, and for alloy containing Fe（x=0.4）, it grew from 106 to 166 cycles at a current density of 600 mA/g. The results obtained by XRD, TEM and SEM revealed that the as-cast and quenched alloys had multiphase structures, including two major phases （La, Mg）Ni3 and LaNi5 as well as an imptLrity phase LaNi2. Rapid quenching helped the formation of an amorphous-like structure in Fe containing alloys.

Direct synthesis of La-Mg-Ni-Co type hydrogen storage alloys from oxide mixtures

(La;Mg;);(Ni;Co;);（x = 0.125, 0.25, 0.5） alloys were synthesized from the sintered mixture of La;O;+ Ni O + Co O + Mg O in the molten CaCl;electrolyte at 750 °C and the electrochemical hydrogen storage capacities of the synthesized alloys were measured. Non-hygroscopic LaNiO;phase formed during sintering（at 1200 °C for 2 h） as a result of the reaction of hygroscopic La;O;with NiO. Another sinter product was Mg;Ni;O phase. Both mixed oxide sinter products facilitated the La-Ni and Mg-Ni phase formations. X-ray diffraction peaks indicated that the first stable phase appeared in the alloy structure was LaNi;which formed upon reduction of La;NiO;phase. Increase in Mg content caused formation of La;Mg;Ni;phase in the alloy structure and the presence of this phase improved the hydrogen storage performance of the electrodes. It was observed that(La;Mg;);(Ni;Co;);（x = 0.125, 0.25, 0.5） alloys have promising discharge capacities change between 319 m Ah/g and 379 m Ah/g depending on the alloy Mg content.

Effect of eutectic phase on damping and mechanical properties of as-cast Mg-Ni hypoeutectic alloys

Dynamic mechanical analysis (DMA) was applied to systematically investigate the low frequency damping properties of as-cast hypoeutectic Mg-Ni alloys. The results show that the as-cast hypoeutectic Mg-Ni alloys exhibit high damping capacities. The strain amplitude dependent damping curve has its own special characteristic, in which the damping is strongly related to the strain amplitude. The effect of the eutectic phase on damping and the mechanical properties of as-cast hypoeutectic Mg-Ni alloys were also discussed in detail.

Electrochemical Hydrogen Storage Performances of the Si Added La-Mg-Ni-based A_2B_7-type Electrode Alloys for Ni/MH Battery Application

The casting and annealing technologies were applied to fabricate the La0.8Mg0.2Ni3.3Co0.2Six （x = 0-0.2） electrode alloys. The effects of Si content and annealing temperature on the structure and electrochemical performances of the alloys were investigated systematically. The analyses of XRD and SEM show that all the alloys possess a multiphase structure, involving two main phases （La, Mg）2Ni7 and LaNi5 as well as a residual phase LaNi3. The addition of Si brings on an evident increase in the LaNi5 phase and a decrease in the （La, Mg）2Ni7 phase, without altering the main phase component of the alloy, which also makes the lattice constants and cell volumes of the alloy enlarged. Likewise, the annealing treatment engenders the same action on the lattice constants and cell volumes as adding Si. Simultaneously, it gives rise to the variation of the phase abundance and the coarsening of the alloy grains. The electrochemical measurements indicate that the addition of Si ameliorates the cycle stability of the as-cast and annealed alloys significantly, but impairs their discharge capacities clearly. Similarly, the annealing treatment makes a positive contribution to the cycle stability of the alloy evidently, and the discharge capacity of the alloy shows a maximum value with annealing temperature rising. Furthermore, the high rate discharge ability （HR） first augments and then declines with the rising of Si content and annealing temperature.

Effect of cobalt content on electrochemical performance of La-Mg-Ni system (Ce_2Ni_7-type) electrode alloys

In order to improve the cyclic stability of La-Mg-Ni system （Ce2Ni7-type） alloy electrode, small amount of Co was added in La0.75Mg0.25Ni3.5 alloy. The effect of Co on electrochemical performance and microstructure of the alloys were investigated in detail. XRD results showed that the alloys had multiphase structure composed of （La, Mg）2Ni7, LaNi5 and small amount of LaNi2 phases. The discharge capacity of the alloys first increased and then decreased with increasing Co content. At a discharge current density of 900 mA/g, the HRD of the alloy electrodes increased from 81.3% （x=0） to 89.2 % （x=0.2）, and then reduced to 87.8 % （x=0.6）. After 60 charge/discharge cycles, the capacity retention rate of the alloys enhanced from 52.67% to 61.32%, and the capacity decay rate of the alloys decreased from 2.60 to 2.05 mAh/g per cycle with increasing Co content. The obtained results by XPS and XRD showed that the fundamental reasons for the capacity decay of the La-Mg-Ni system （Ce2Ni7-type） alloy electrodes were corrosion and oxidation as well as passivation of Mg and Lain alkaline solution.

Effects of substituting Ni with M (M=Cu, Al and Mn) on microstructures and electrochemical characteristics of La-Mg-Ni system (PuNi_3-type) electrode alloys

In order to improve the electrochemical cycle stability of La-Mg-Ni system (PuNi3-type) hydrogen storage alloy, Ni in the alloys was partially substituted by M (M=Cu, Al, Mn). A new La-Mg-Ni system electrode alloys La0.7Mg0.3Ni2.55-xCo0.45Mx (M=Cu, Al, Mn; x=0, 0.1) were prepared by casting and rapid quenching. The effects of element substitution and rapid quenching on the microstructures and electrochemical performances of the alloys were investigated. The results by XRD, SEM and TEM show that the alloys have a multiphase structure, including the (La, Mg)Ni3 phase, the LaNi5 phase and the LaNi2 phase. The rapid quenching and element substitution have an imperceptible influence on the phase compositions of the alloys, but both change the phase abundance of the alloys. The rapid quenching significantly improves the composition homogeneity of the alloys and markedly decreases the grain size of the alloys. The Cu substitution promotes the formation of an amorphous phase in the as-quenched alloy, and a reversal result by the Al substitution. The electrochemical measurement indicates that the element substitution decreases the discharge capacity of the alloys, whereas it obviously improves the cycle stability of the alloys. The positive influence of element substitution on the cycle life of the alloys is in sequence Al>Cu>Mn, and negative influence on the discharge capacity is in sequence Al>Mn>Cu. The rapid quenching significantly enhances the cycle stability of the alloys, but it leads to a different extent decrease of the discharge capacity of the alloys.

Structure and Electrochemical Properties of A_2B_7-Type La-Mg-Ni Hydrogen Storage Alloys

Investigation of alloy structure shows that La2-xMgxNi7 （x = 0.3 - 0.8） alloys are mainly com- posed of Ce/Ni7-type, Gd2Co7-type and PuNi3-type phase. The influence of Mg content in alloys on the phase structure is great, resulting in a linear decrease of the unit cell parameters of main phases and increase of hydrogen absorption/desorption plateau as Mg content increases. Electrochemical measurements show that as the Mg content increases, the discharge capacity of alloy electrodes first increases and then decreases. The cyclic stability presents a deteriorative trend. La1.4Mg0.6 Ni7 alloy electrode exhibits the maximum electrochemical discharge capacity （378 mAh·g^-1）, and the La1.6Mg0.4Ni7 alloy electrode shows the best cyclic stability （S270 = 81%）.

Structures and Electrochemical Performances of As-spun RE-Mg-Ni-Mn-based Alloys Applied to Ni-MH Battery

The La-Mg-Ni-Mn-based AB_2-type La_（1-x）Ce_xMgNi_（3.5）Mn_（0.5）（x = 0, 0.1, 0.2, 0.3, and 0.4） alloys were fabricated by melt spinning technology. The effects of Ce content on the structures and electrochemical hydrogen storage performances of the alloys were studied systematically. The XRD and SEM analyses proved that the experimental alloys consist of a major phase LaMgNi_4 and a secondary phase LaNi_5. The variation of Ce content causes an obvious change in the phase abundance of the alloys without changing the phase composition. Namely, with the increase of Ce content, the LaMgNi_4 phase augments and the LaNi_5 phase declines. The lattice constants and cell volumes of the alloys clearly shrink with increasing Ce content. Moreover, the Ce substitution for La results in the grains of the alloys clearly refined. The electrochemical tests showed that the substitution of Ce for La obviously improves the cycle stability of the as-spun alloys. The analyses on the capacity degradation mechanism demonstrate that the improvement can be attributed to the ameliorated anti-corrosion and antioxidation ability originating from substituting partial La with Ce. The as-spun alloys exhibit excellent activation capability, reaching the maximum discharge capacities just at the first cycling without any activation treatment. The substitution of Ce for La evidently improves the discharge potential characteristics of the as-spun alloys. The discharge capacity of the alloys first increases and then decreases with growing Ce content. Furthermore, a similar trend also exists in the electrochemical kinetics of the alloys, including the high rate discharge ability（HRD）, hydrogen diffusion coefficient（D）, limiting current density（IL） and charge transfer rate.

Hydrogen storage behavior of nanocrystalline and amorphous La-Mg-Ni-based LaMg_(12)-type alloys synthesized by mechanical milling

Nanocrystalline and amorphous LaMg11Ni+x%Ni(x=100,200,mass fraction)alloys were synthesized by mechanicalmilling.The electrochemical hydrogen storage properties of the as-milled alloys were tested by an automatic galvanostatic system.The gaseous hydrogen absorption and desorption properties were investigated by Sievert’s apparatus and differential scanningcalorimeter(DSC)connected with a H2detector.The results indicated that increasing Ni content significantly improves the gaseousand electrochemical hydrogen storage performances of the as-milled alloys.The gaseous hydrogen absorption capacities andabsorption rates of the as-milled alloys have the maximum values with the variation of the milling time.But the hydrogen desorptionkinetics of the alloys always increases with the extending of milling time.In addition,the electrochemical discharge capacity andhigh rate discharge(HRD)ability of the as-milled alloys both increase first and then decrease with milling time prolonging.

Composition Range of Amorphous Mg-Ni-Y Alloys

Based on the thermodynamic point of view, a method for predication of the composition range of amorphous ternary alloys was proposed. The composition range of amorphous ternary alloys is determined by the comparison of the excess free energy of the amorphous alloy and the free energy of competing crystalline states. The free energy is extrapolated from the data of three binary alloys by using Toop′s model. The method was applied to predict the composition range of amorphous Mg Ni Y alloys. The theoretical results are in good agreement with the available experimental results. It indicates that the present method can be used to predict the composition range for amorphous ternary alloys.

The electrochemical characteristics of AB_(4)-type rare earth-Mg-Ni-based superlattice structure hydrogen storage alloys for nickel metal hydride battery

Rare earth-Mg-Ni-based alloys with superlattice structures are new generation negative electrode materials for the nickel metal hydride batteries.Among them,the novel AB_(4)-type superlattice structure alloy is supposed to have superior cycling stability and rate capability.Yet its preparation is hindered by the crucial requirement of temperature and the special composition which is close to the other superlattice structure.Here,we prepare rare earth-Mg-Ni-based alloy and study the phase transformation of alloys to make clear the formation of AB_(4)-type phase.It is found Pr_(5)Co_(19)-type phase is converted from Ce_(5)Co_(19)-type phase and shows good stability at higher temperature compared to the Ce_(5)Co_(19)-type phase in the range of 930-970℃.Afterwards,with further 5℃increasing,AB_(4)-type superlattice structure forms at a temperature of 975℃by consuming Pr_(5)Co_(19)-type phase.In contrast with A_(5)B_(19)-type alloy,AB_(4)-type alloy has superior rate capability owing to the dominant advantages of charge transfer and hydrogen diffusion.Besides,AB_(4)-type alloy shows long lifespan whose capacity retention rates are 89.2%at the 100;cycle and 82.8%at the 200;cycle,respectively.AB_(4)-type alloy delivers 1.53 wt.%hydrogen storage capacity at room temperature and exhibits higher plateau pressure than Pr_(5)Co_(19)-type alloy.The work provides novel AB_(4)-type alloy with preferable electrochemical performance as negative electrode material to inspire the development of nickel metal hydride batteries.

Electrochemical Hydrogen Storage Performance of the Nanocrystalline and Amorphous Pr-Mg-Ni-based Alloys Synthesized by Mechanical Milling

The PrMg12-type composite alloy of PrMg_(11)Ni + x wt% Ni (x=100,200) with an amorphous and nanocrystalline microstructure were synthesized through the mechanical milling.Effects of milling duration and Ni content on the microstructures and electrochemical hydrogen storage performances of the ball-milled alloys were methodically studied.The ball-milled alloys obtain the optimum discharge capacities at the first cycle.Increasing Ni content dramatically enhances the electrochemical property of alloys.Milling time varying may obviously impact the electrochemical performance of these alloys.The discharge capacities show a significant upward trend with milling duration prolonging,but milling for a longer time more than 40 h induces a slight decrease in the discharge capacity of the x=200 alloy.As milling duration increases,the cycle stability clearly lowers,while it first declines and then augments under the same condition for the x=200 alloy.The high-rate discharge abilities of the ball-milled alloys show the optimum values with milling time varying.