A systematic investigation of secondary phase dissolution in Mg-Sn alloys

As-cast Mg-Sn alloys(3,6,and 9 wt%Sn)were solution treated at 653,703 and 753 K(380,430 and 480℃)for 1,4,8,12 and 24 h to determine the variation of secondary phase with respect to Sn content,temperature and time.Mg-3 wt%Sn exhibits Mg2Sn dissolution at all solution treatment temperatures whereas Mg-6 and 9 wt%Sn alloy displays Mg2Sn reprecipitation and dissolution depending on the heat treatment temperature.In addition,a combined mathematical model that predicts the secondary phase dissolution and solute redistribution as a function of temperature and time is presented in this work.This model is a significant improvement compared to the previous studies where the dissolution and homogenization processes are considered independently.The effect of grain size and solute mobility upon the dissolution and homogenization kinetics is discussed as well.

Microstructure, mechanical and bio-corrosion properties of as-extruded Mg-Sn-Ca alloys

The as-extruded Mg？Sn？Ca alloys were prepared and investigated for orthopedic applications via using optical microscopy, scanning electron microscopy, X-ray diffraction, as well as tensile, immersion and electrochemical tests. The results showed that, with the addition of 1% Sn and the Ca content of 0.2%？0.5%, the microstructure of the as-extruded Mg？Sn？Ca alloys became homogenous, which led to increased mechanical properties and improved corrosion resistance. Further increase of Ca content up to 1.5% improved the strength, but deteriorated the ductility and corrosion resistance. For the alloy containing 0.5% Ca, when the Sn content increased from 1% to 3%, the ultimate tensile strength increased with a decreased corrosion resistance, and the lowest yield strength and ductility appeared with the Sn content of 2%. These behaviors were determined by Sn/Ca mass ratio. The analyses showed that as-extruded Mg？1Sn？0.5Ca alloy was promising as a biodegradable orthopedic implant.

Microstructures and tensile properties of as-extruded Mg-Sn binary alloys

The microstructure and mechanical properties of Mg-xSn （x-3, 7 and 14, mass fraction, %） alloys extruded indirectly at 300 ℃ were investigated by means of optical microscopy, scanning electron microscopy and tensile test. The grain size of the a-Mg matrix decreases from 220, 160 and 93 μm after the homogenization treatment to 28, 3 and 16 μm in the three alloys after extrusion, respectively. The results show that the grain refinement is most remarkable in the as-extruded Mg-7Sn alloy. At the same time, the amount of the Mg2Sn particles remarkably increases in the Mg-7Sn alloy with very uniform distribution in the a-Mg matrix. In contrast, the Mg2Sn phase inherited from the solidification with a large size is mainly distributed along grain boundary in the Mg-14Sn alloy. The tensile tests at room temperature show that the ultimate tensile strength of the as-extruded Mg-7Sn alloy is the highest, i.e., 255 MPa, increased by 120% as compared with that of as-cast samples.

生物可降解挤压态Mg-Sn-Zn-Zr合金组织与腐蚀性能的研究

采用气体保护法制备了高强塑性Mg-Sn-Zn-Zr(TZK)合金,然后在不同温度(300、350、400℃)对其进行挤压变形,并对合金的微观组织、物相组成和体外降解行为进行研究。结果表明:300℃挤压后合金的组织为均匀细小的等轴晶,晶粒尺寸最小,为6.57μm;析氢量和腐蚀速率最低,耐腐蚀性能最好。随挤压温度升高,合金的晶粒长大,组织中出现孪晶,导致其耐腐蚀性能变差。

Influence of alloying elements on microstructure and microhardness of Mg-Sn-Zn-based alloys

The phase evolution in （88%-91%）Mg-8%Sn-l%Zn-X （X=A1, Mn and/or Ce） system was analyzed via CALPHAD method and simulations were used in precise selection of the chemical composition. The influence of the addition of different alloying elements such as A1, Mn and Ce on the microstructure and microhardness of Mg-8%Sn-l%Zn-based alloys was investigated. Combined addition of A1 and Mn shows features distinct from separate addition of A1 or Mn. Additions of l%AI and l%Mn to base alloy result in the formation of massive A1-Mn phase in a-Mg matrix grains. Addition of Ce element can refme the second eutectic precipitates and form intermetallic compounds with Sn. Fine rod-like Sn-Ce phase presents mainly on the grain boundaries and plays a role in inhibiting grain growth. The effects of alloying elements on Vickers microhardness and indentation size effect of base alloy were examined.

Microstructure and mechanical properties of as-cast Mg-Sn-Ca alloys and effect of alloying elements

The effect of Sn, Ca, Al, Si and Zn addition on the compressive strength of cast Mg-Sn-Ca （TX） alloys was studied in the temperature range of 25-250 °C and correlated with the microstructure. The Sn to Ca mass ratio up to 2.5 contributes to the formation of Mg2Ca phase at the grain boundaries and CaMgSn in the matrix, while a ratio of 3 gives only CaMgSn phase mostly in the matrix. While the compressive strength decreases with the increase in temperature, for Sn/Ca up to 2.5, a plateau occurs in 100-175 °C, which is attributed to the strengthening by Mg2Ca. However, for ratio of 3, the strength is lower and decreases more gradually. Mg-3Sn-2Ca （TX32） has the highest strength and the addition of 0.4%Al increases its strength but simultaneous addition of Si lowers the strength. Likewise, the addition of Zn improves its strength but simultaneous addition of Al slightly decreases the strength. The results are correlated with the types of intermetallic phases that form in various alloys.

Microstructure and tensile properties of as-extruded Mg-Sn-Y alloys

The microstructure and tensile properties of the Mg-1.0%Sn-xY(x=1.5%,3.0%,3.5%,atom fraction)alloys extruded indirectly at 350℃ were investigated by means of optical microscopy,scanning electron microscopy and tensile test.The mean grain sizes ofα-Mg matrix in the three extruded alloys are 6,8 and 12μm,respectively,slightly increasing with the addition of Y. The relationship between microstructure and strength was discussed in detail.The results show that the addition of Y has little effect on the grain refinement of the as-extruded Mg-Sn based alloys above.The only MgSnY phase is detected in the Mg-Sn-1.5%Y alloy, and the Sn3Y5 phase in the Mg-Sn-3.5%Y alloy,whereas both of them simultaneously exist in the Mg-Sn-3.0%Y alloy.The particle shape of MgSnY and Sn3Y5 phase,inherited from the solidification,has little change before and after hot extrusion.Mg-Sn-3.0%Y alloy has the highest ultimate tensile strength(UTS),305 MPa,by over 50%compared with that of the other two alloys.

Strengthening mechanisms of indirect-extruded Mg-Sn based alloys at room temperature

The strength of a material is dependent on how dislocations in its crystal lattice can be easily propagated.These dislocations create stress fields within the material depending on their intrinsic character.Generally,the following strengthening mechanisms are relevant in wrought magnesium materials tested at room temperature:fine-grain strengthening,precipitate strengthening and solid solution strengthening as well as texture strengthening.The indirect-extruded Mg-8Sn(T8)and Mg-8Sn-1Al-1Zn(TAZ811)alloys present superior tensile properties compared to the commercial AZ31 alloy extruded in the same condition.The contributions to the strengthen of Mg-Sn based alloys made by four strengthening mechanisms were calculated quantitatively based on the microstructure characteristics,physical characteristics,thermomechanical analysis and interactions of alloying elements using AZ31 alloy as benchmark.

Discharge properties of Mg-Sn-Y alloys as anodes for Mg-air batteries

Mg-Sn-Y alloys with different Sn contents(wt%)were assessed as anode candidates for Mg-air batteries.The relationship between microstructure(including the second phase,grain size,and texture)and discharge properties of the Mg-Sn-Y alloys was examined using microstructure observation,electrochemical measurements,and galvanostatic discharge tests.The Mg-0.7Sn-1.4Y alloy had a high steady discharge voltage of 1.5225 V and a high anodic efficiency of 46.6% at 2.5 mA·cm^(-2).These good properties were related to its microstructure:small grain size of 3.8μm,uniform distribution of small second phase particles of 0.6μm,and a high content(vol%)of(1120)/(1010)orientated grains.The scanning Kelvin probe force microscopy(SKPFM)indicated that the Sn_(3)Y_(5) and MgSnY phases were effective cathodes causing micro-galvanic corrosion which promoted the dissolution of Mg matrix during the discharge process.

Mg-Sn基合金沉淀强化研究进展

Mg-Sn基合金是应用前景广阔的时效强化型合金,添加合金元素可以细化Mg_(2)Sn沉淀相,并增强其时效强化效果,合金化元素选择及添加量是优化Mg-Sn合金力学性能的关键因素。本文总结了6种有理和9种无理的Mg_(2)Sn与Mg基体的取向关系,具有有理取向的Mg_(2)Sn沉淀位于基面呈板状和棒状,而无理取向的Mg_(2)Sn沉淀为非基面的板状和盘状。结合形貌和取向,进一步综述合金元素对Mg_(2)Sn沉淀相形核和生长的影响规律,其中Al、Zn元素促使非基面Mg_(2)Sn相析出;Ag、Na元素为Mg_(2)Sn相提供更多的形核位点;Ca和Y元素形成高熔点的三元相,时效效果不理想。基于研究现状,展望了Mg-Sn基合金研究趋势和方向。

Microstructure evolution and age-hardening response in Mg-Sn-Sm alloys under a wide range of Sm/Sn ratio

The microstructure evolution and age-hardening response for different Sm/Sn ratios(0-2.55,in wt.%)of Mg-Sn-Sm alloys were investigated.The second phase formation in as-cast alloys and the Mg_(3)Sm precipitates formed in aged alloys were characterized using XRD,FESEM and HAADF-STEM with EDS techniques.Results indicate that the Sm/Sn ratio has a great influence on the phase constitution,α-Mg grain size and age-hardening response.With the increment of Sm/Sn ratio,Mg_(41)Sm_(5) and thermally stable MgSnSm phases precipitate.When the Sm/Sn ratio is about 1.19,the secondary dendrite arm spacing ofα-Mg grains significantly decreases.Furthermore,the alloy with Sm/Sn ratio up to 2.55 exhibits the highest age-hardening response,the hardness value increases from 52 HB at solution-treated condition to 74 HB at peak-aged condition(ageing at 220 ℃ for a short time of 4 h).This is attributed to the large volume fraction of needle-like Mg_(3)Sm precipitates formed in theα-Mg matrix during ageing treatment,which results in a significant precipitation strengthening effect.

Accelerated design of high-performance Mg-Mn-based magnesium alloys based on novel bayesian optimization

Magnesium(Mg),being the lightest structural metal,holds immense potential for widespread applications in various fields.The development of high-performance and cost-effective Mg alloys is crucial to further advancing their commercial utilization.With the rapid advancement of machine learning(ML)technology in recent years,the“data-driven''approach for alloy design has provided new perspectives and opportunities for enhancing the performance of Mg alloys.This paper introduces a novel regression-based Bayesian optimization active learning model(RBOALM)for the development of high-performance Mg-Mn-based wrought alloys.RBOALM employs active learning to automatically explore optimal alloy compositions and process parameters within predefined ranges,facilitating the discovery of superior alloy combinations.This model further integrates pre-established regression models as surrogate functions in Bayesian optimization,significantly enhancing the precision of the design process.Leveraging RBOALM,several new high-performance alloys have been successfully designed and prepared.Notably,after mechanical property testing of the designed alloys,the Mg-2.1Zn-2.0Mn-0.5Sn-0.1Ca alloy demonstrates exceptional mechanical properties,including an ultimate tensile strength of 406 MPa,a yield strength of 287 MPa,and a 23%fracture elongation.Furthermore,the Mg-2.7Mn-0.5Al-0.1Ca alloy exhibits an ultimate tensile strength of 211 MPa,coupled with a remarkable 41%fracture elongation.

Relationship between the unique microstructures and behaviors of high-entropy alloys

High-entropy alloys(HEAs),which were introduced as a pioneering concept in 2004,have captured the keen interest of nu-merous researchers.Entropy,in this context,can be perceived as representing disorder and randomness.By contrast,elemental composi-tions within alloy systems occupy specific structural sites in space,a concept referred to as structure.In accordance with Shannon entropy,structure is analogous to information.Generally,the arrangement of atoms within a material,termed its structure,plays a pivotal role in dictating its properties.In addition to expanding the array of options for alloy composites,HEAs afford ample opportunities for diverse structural designs.The profound influence of distinct structural features on the exceptional behaviors of alloys is underscored by numer-ous examples.These features include remarkably high fracture strength with excellent ductility,antiballistic capability,exceptional radi-ation resistance,and corrosion resistance.In this paper,we delve into various unique material structures and properties while elucidating the intricate relationship between structure and performance.

Unveiling the influence of dendrite characteristics on the slip/twinning activity and the strain hardening capacity of Mg-Sn-Li-Zn cast alloys

This work explores the correlation between the characteristics of the cast structure(dendrite growth pattern,dendrite morphology and macro-texture)and strain hardening capacity during high temperature deformation of Mg-5Sn-0.3Li-0 and 3Zn multi-component alloys.The three dimensional(3D)morphology of the dendrite structure demonstrates the transition of the growth directions from<1123>,<1120>and<1122>to<1123>and<1120>due to the addition of Zn.The simultaneous effects of growing tendency and the decrement of dendrite coarsening rate at the solidification interval lead to dendrite morphology transition from the globular-like to the hyper-branch structure.This morphology transition results in the variation of the solidification macro-texture,which has effectively influenced the dominant deformation mechanisms(slip/twin activity).The higher activity of the slip systems increases the tendency of the dendrite arms for bending along the deformation direction and fragmentation.Apart from this,the dendrite holding hyper-branch structure with an average thickness below 20μm are more favorable for fragmentation.The dendrite fragmentation leads to considerable softening fractions,and as an effective strain compensation mechanism increases the workability of dendritic structure.

Research advances of magnesium and magnesium alloys globally in 2023

Magnesium materials have attracted the attention of many researchers,and the related research is expanding.This article summarizes the advance in the research and development of magnesium materials globally in 2023 from bibliometric and scientific perspectives.More than 4680 articles on Mg and its alloys were published and indexed in the Web of Science(WoS)Core Collection database last year.The bibliometric analyses show that the traditional structural Mg alloys,functional Mg materials,and corrosion and protection of Mg alloys are still the main research focus.Therefore,this review paper mainly focuses on the research progress of Mg cast alloys,Mg wrought alloys,bio-magnesium alloys,Mg-based energy storage materials,corrosion and protection of Mg alloys in 2023.In addition,future research directions are proposed based on the challenges and obstacles identified throughout this review.

Influence of Metalloid Elements on the Magnetic Properties and Anisotropy of FeNi-based Amorphous Alloys

The magnetic properties and anisotropy of amor- phous(Fe_(80)Ni_(20))_(78)Si_xB_(22-x).alloys have been investigated systematically.The maximum permeability,coercive force and remanence have been determined for as-prepared and annealed samples,The results on the technical magnetic properties of this alloy system have been discussed and compared with Masumoto's.

Microstructure and corrosion behavior of Mg-Sn-Ca alloys after extrusion

Mg-Sn-Ca alloys promise a reasonable corrosion resistance in combination with good creep resistance, likely due to the presence of Ca2-xMgxSn and other phases. The selected alloys with 3% Sn and Ca in the range of 1%-2% have been extruded in order to achieve more homogeneous microstructure compared with the as-cast alloys. Optical microscopy(OM) and X-ray diffraction(XRD) techniques were used to study the microstructure and phases of these alloys. The corrosion behavior of these alloys was investigated by means of salt spray test and potentio-dynamic measurements. The results obtained on the alloys Mg-3Sn (T3), Mg-3Sn-1Ca (TX31), and Mg-3Sn-2Ca (TX32) indicate the presence of the same phases in as-cast and after extrusion, namely Mg2Sn, Ca2-xMgxSn, and Ca2-xMgxSn/Mg2Ca, respectively. However, due to the occurrence of extensive recrystallization in the extrusion process, the grain size has significantly reduced after extrusion. The reduction leads to the improvement of the corrosion resistance after extrusion which is then comparable with the commercial alloy AZ91D.

Microstructure and damping properties of LPSO phase dominant Mg-Ni-Y and Mg-Zn-Ni-Y alloys

This work studied the microstructure,mechanical properties and damping properties of Mg_(95.34)Ni_(2)Y_(2.66) and Mg_(95.34)Zn_(1)Ni_(1)Y_(2.66)alloys systematically.The difference in the evolution of the long-period stacked ordered(LPSO)phase in the two alloys during heat treatment was the focus.The morphology of the as-cast Mg_(95.34)Ni_(2)Y_(2.66)presented a disordered network.After heat treatment at 773 K for 2 hours,the eutectic phase was integrated into the matrix,and the LPSO phase maintained the 18R structure.As Zn partially replaced Ni,the crystal grains became rounded in the cast alloy,and lamellar LPSO phases and more solid solution atoms were contained in the matrix after heat treatment of the Mg_(95.34)Zn_(1)Ni_(1)Y_(2.66)alloy.Both Zn and the heat treatment had a significant effect on damping.Obvious dislocation internal friction peaks and grain boundary internal friction peaks were found after temperature-dependent damping of the Mg_(95.34)Ni_(2)Y_(2.66)and Mg_(95.34)Zn_(1)Ni_(1)Y_(2.66)alloys.After heat treatment,the dislocation peak was significantly increased,especially in the alloy Mg_(95.34)Ni_(2)Y_(2).66.The annealed Mg_(95.34)Ni_(2)Y_(2.66)alloy with a rod-shaped LPSO phase exhibited a good damping performance of 0.14 atε=10^(−3),which was due to the difference between the second phase and solid solution atom content.These factors also affected the dynamic modulus of the alloy.The results of this study will help in further development of high-damping magnesium alloys.

Recent innovations in laser additive manufacturing of titanium alloys

Titanium(Ti)alloys are widely used in high-tech fields like aerospace and biomedical engineering.Laser additive manufacturing(LAM),as an innovative technology,is the key driver for the development of Ti alloys.Despite the significant advancements in LAM of Ti alloys,there remain challenges that need further research and development efforts.To recap the potential of LAM high-performance Ti alloy,this article systematically reviews LAM Ti alloys with up-to-date information on process,materials,and properties.Several feasible solutions to advance LAM Ti alloys are reviewed,including intelligent process parameters optimization,LAM process innovation with auxiliary fields and novel Ti alloys customization for LAM.The auxiliary energy fields(e.g.thermal,acoustic,mechanical deformation and magnetic fields)can affect the melt pool dynamics and solidification behaviour during LAM of Ti alloys,altering microstructures and mechanical performances.Different kinds of novel Ti alloys customized for LAM,like peritecticα-Ti,eutectoid(α+β)-Ti,hybrid(α+β)-Ti,isomorphousβ-Ti and eutecticβ-Ti alloys are reviewed in detail.Furthermore,machine learning in accelerating the LAM process optimization and new materials development is also outlooked.This review summarizes the material properties and performance envelops and benchmarks the research achievements in LAM of Ti alloys.In addition,the perspectives and further trends in LAM of Ti alloys are also highlighted.

Microstructures,corrosion behavior and mechanical properties of as-cast Mg-6Zn-2X(Fe/Cu/Ni)alloys for plugging tool applications

Mg-6Zn-2X(Fe/Cu/Ni)alloys were prepared through semi-continuous casting,with the aim of identifying a degradable magnesium(Mg)alloy suitable for use in fracturing balls.A comparative analysis was conducted to assess the impacts of adding Cu and Ni,which result in finer grains and the formation of galvanic corrosion sites.Scanner electronic microscopy examination revealed that precipitated phases concentrated at grain boundaries,forming a semi-continuous network structure that facilitated corrosion penetration in Mg-6Zn-2Cu and Mg-6Zn-2Ni alloys.Pitting corrosion was observed in Mg-6Zn-2Fe,while galvanic corrosion was identified as the primary mechanism in Mg-6Zn-2Cu and Mg-6Zn-2Ni alloys.Among the tests,the Mg-6Zn-2Ni alloy exhibited the highest corrosion rate(approximately 932.9 mm/a)due to its significant potential difference.Mechanical testing showed that Mg-6Zn-2Ni alloy possessed suitable ultimate compressive strength,making it a potential candidate material for degradable fracturing balls,effectively addressing the challenges of balancing strength and degradation rate in fracturing applications.