The electrochemical process of Mg-Sr codeposition was studied in MgCl2-SrCl2-KCl melts containing different MgCl2 concentrations at 700 ℃ by cyclic voltammetry, chronopotentiometry and chronoamperometry. The results ...The electrochemical process of Mg-Sr codeposition was studied in MgCl2-SrCl2-KCl melts containing different MgCl2 concentrations at 700 ℃ by cyclic voltammetry, chronopotentiometry and chronoamperometry. The results show that the actual precipitation potential of Sr reduces by nearly 0.5 V because of the depolarization effects of Sr activity reduced by forming Mg-Sr alloy. The codeposition potential condition of Mg and Sr to form Mg-Sr alloy is as follows： When electrode potential is more negative than -1.5 V, the magnesium will precipitate; when electrode potential is more negative than -2.0 V, the magnesium and strontium will both deposit. The control step of codeposition process of Mg and Sr is not diffusion control step. The codeposition current condition of Mg and Sr to form Mg-Sr alloy by chronoptentiometry is as follows： cathode current densities are higher than 0.71, 1.57 and 2.83 A/cm^2 in MgCl2-SrCl2-KCl melts with MgCl2 concentrations of 2%, 5% and 10% （mass fraction）, respectively. Key words：展开更多
The effects of various Mg-Sr master alloys(conventional as-cast,rapidly-solidified,rolled and solutionized) on microstructural refinement of ZK60 magnesium alloy were investigated.The results indicate that the refinem...The effects of various Mg-Sr master alloys(conventional as-cast,rapidly-solidified,rolled and solutionized) on microstructural refinement of ZK60 magnesium alloy were investigated.The results indicate that the refinement efficiency of various Mg-Sr master alloys in ZK60 alloy is different.The rolled Mg-Srmaster alloy is found to have relatively higher refinement efficiency than the conventional as-cast,solutionized and rapidly-solidified Mg-Sr master alloys.After being treated with the rolled Mg-Sr master alloy,the ZK60 alloy obtains the minimum average grain size of 33μm.The difference of various Mg-Sr master alloys in refinement efficiency might be related to the initial microstructure change of various Mg-Sr master alloys.展开更多
To discuss the feasibility of the application of porous Mg-Sr alloy combined with Mg-Sr alloy membrane in the repair of mandibular defects in dogs.The second and third mandibular premolars on both sides were extracted...To discuss the feasibility of the application of porous Mg-Sr alloy combined with Mg-Sr alloy membrane in the repair of mandibular defects in dogs.The second and third mandibular premolars on both sides were extracted from six dogs.The model of mandible buccal fenestration bone defects were prepared after the sockets healed.Twelve bone defects were randomly divided into groups A and B,then Mg-Sr alloy was implanted in bone defects of group A and covered by Mg-Sr alloy membrane while Mg-Sr alloy was implanted in bone defects of group B and covered by mineralized collagen membrane.Bone defects observed on cone beam computed tomographic images and comparing the gray value of the two groups after 4,8 and 12 weeks.After 12 weeks,the healing of bone defects were evaluated by gross observation,X-ray microscopes and histological observation of hard tissue.Bone defects in each group were repaired.At 8 and 12 weeks,the gray value of group A was higher than that of group B(P<0.05).At 12 weeks,the bone volume fraction of group A was higher than that of group B(P<0.05).The newly woven bone in group A is thick and arranged staggered,which was better than that of group B.Porous Mg-Sr alloy combined with Mg-Sr alloy membrane could further promote the repair of mandibular defects,and obtain good osteogenic effect.展开更多
文摘The electrochemical process of Mg-Sr codeposition was studied in MgCl2-SrCl2-KCl melts containing different MgCl2 concentrations at 700 ℃ by cyclic voltammetry, chronopotentiometry and chronoamperometry. The results show that the actual precipitation potential of Sr reduces by nearly 0.5 V because of the depolarization effects of Sr activity reduced by forming Mg-Sr alloy. The codeposition potential condition of Mg and Sr to form Mg-Sr alloy is as follows： When electrode potential is more negative than -1.5 V, the magnesium will precipitate; when electrode potential is more negative than -2.0 V, the magnesium and strontium will both deposit. The control step of codeposition process of Mg and Sr is not diffusion control step. The codeposition current condition of Mg and Sr to form Mg-Sr alloy by chronoptentiometry is as follows： cathode current densities are higher than 0.71, 1.57 and 2.83 A/cm^2 in MgCl2-SrCl2-KCl melts with MgCl2 concentrations of 2%, 5% and 10% （mass fraction）, respectively. Key words：
基金Project(50725413)supported by the National Natural Science Foundation of China for Distinguished Young ScholarProject(2007CB613704)supported by the National Basic Research Program of China
文摘The effects of various Mg-Sr master alloys(conventional as-cast,rapidly-solidified,rolled and solutionized) on microstructural refinement of ZK60 magnesium alloy were investigated.The results indicate that the refinement efficiency of various Mg-Sr master alloys in ZK60 alloy is different.The rolled Mg-Srmaster alloy is found to have relatively higher refinement efficiency than the conventional as-cast,solutionized and rapidly-solidified Mg-Sr master alloys.After being treated with the rolled Mg-Sr master alloy,the ZK60 alloy obtains the minimum average grain size of 33μm.The difference of various Mg-Sr master alloys in refinement efficiency might be related to the initial microstructure change of various Mg-Sr master alloys.
基金supported by Science and Technology Fund of Liaoning Province(20180530071).
文摘To discuss the feasibility of the application of porous Mg-Sr alloy combined with Mg-Sr alloy membrane in the repair of mandibular defects in dogs.The second and third mandibular premolars on both sides were extracted from six dogs.The model of mandible buccal fenestration bone defects were prepared after the sockets healed.Twelve bone defects were randomly divided into groups A and B,then Mg-Sr alloy was implanted in bone defects of group A and covered by Mg-Sr alloy membrane while Mg-Sr alloy was implanted in bone defects of group B and covered by mineralized collagen membrane.Bone defects observed on cone beam computed tomographic images and comparing the gray value of the two groups after 4,8 and 12 weeks.After 12 weeks,the healing of bone defects were evaluated by gross observation,X-ray microscopes and histological observation of hard tissue.Bone defects in each group were repaired.At 8 and 12 weeks,the gray value of group A was higher than that of group B(P<0.05).At 12 weeks,the bone volume fraction of group A was higher than that of group B(P<0.05).The newly woven bone in group A is thick and arranged staggered,which was better than that of group B.Porous Mg-Sr alloy combined with Mg-Sr alloy membrane could further promote the repair of mandibular defects,and obtain good osteogenic effect.