TiO_(2)@C catalyzed hydrogen storage performance of Mg-Ni-Y alloy with LPSO and ternary eutectic structure

A designed Mg_(88.7)Ni_(6.3)Y_(5)hydrogen storage alloy containing 14H type LPSO(long-period stacking ordered)and ternary eutectic structure was prepared by regulating the alloy composition and casting.The hydrogen storage performance of the alloy was improved by adding nano-flower-like TiO_(2)@C catalyst.The decomposition of the LPSO structure during hydrogenation led to the formation of plenty of nanocrystals which provided abundant interphase boundaries and activation sites.The nanoscale TiO_(2)@C catalyst was uniformly dispersed on the surface of alloy particles,and the"hydrogen overflow''effect of TiO_(2)@C accelerated the dissociation and diffusion of hydrogen on the surface of the alloy particles.As a result,the in-situ endogenous nanocrystals of the LPSO structure decomposition and the externally added flower-like TiO_(2)@C catalyst uniformly dispersed on the surface of the nanoparticles played a synergistic catalytic role in improving the hydrogen storage performance of the Mg-based alloy.With the addition of the TiO_(2)@C catalyst,the beginning hydrogen desorption temperature was reduced to 200℃.Furthermore,the saturated hydrogen absorption capacity of the sample was 5.32 wt.%,and it reached 4.25 wt.%H_(2) in 1 min at 200℃and 30 bar.

Enhanced hydrogen storage kinetics of nanocrystalline and amorphous Mg_2N-type alloy by substituting Ni with Co

In order to improve the hydrogen storage kinetics of the Mg2Ni-type alloys, Ni in the alloy was partially substituted with element Co. The Mg2Ni-type Mg2Ni1-xCox （x=0, 0.1, 0.2, 0.3, 0.4） alloys were fabricated by melt-spinning technique. The structures of the as-spun alloys were characterized by XRD and TEM. The gaseous and electrochemical hydrogen storage kinetics of the alloys was measured. The results show that the substitution of Co for Ni notably enhances the glass forming ability of the Mg2Ni-type alloy. The amorphization degree of the alloys visibly increases with rising of Co content. Furthermore, the substitution of Co for Ni significantly improves the hydrogen storage kinetics of the alloys. With an increase in the amount of Co substitution from 0 to 0.4, the hydrogen absorption saturation ratio of the as-spun （15 m/s） alloy increases from 81.2% to 84.9%, the hydrogen desorption ratio from 17.60% to 64.79%, the hydrogen diffusion coefficient increases from 1.07×10-11 to 2.79×10-11 cm2/s and the limiting current density increases from 46.7 to 191.7 mA/g, respectively.

Electrochemical hydrogen storage characteristics of nanocrystalline and amorphous Mg_2Ni-type alloys prepared by melt-spinning

The nanocrystalline and amorphous Mg2Ni-type alloys with nominal compositions of Mg2Ni1-xMnx （x=0, 0.1, 0.2, 0.3, 0.4） were synthesized by melt-spinning technique. The spun alloy ribbons with a continuous length, a thickness of about 30 μm and a width of about 25 mm are obtained. The structures of the as-spun alloy ribbons were characterized by XRD and HRTEM. The electrochemical hydrogen storage characteristics of the as-spun alloy ribbons were measured by an automatic galvanostatic system. The electrochemical impedance spectrums （EIS） were plotted by an electrochemical workstation. The hydrogen diffusion coefficients （D） in the alloys were calculated by virtue of potential-step measurement. The results show that all the as-spun （x=0） alloys hold a typical nanocrystalline structure, whereas the as-spun （x=0.4） alloy displays a nanocrystalline and amorphous structure, confirming that the substitution of Mn for Ni facilitates the glass formation in the Mg2Ni-type alloy. The substitution of Mn for Ni significantly improves the electrochemical hydrogen storage performances of the alloys, involving the discharge capacity and the electrochemical cycle stability. With an increase in the amount of Mn substitution from 0 to 0.4, the discharge capacity of the as-spun （20 m/s） alloy increases from 96.5 to 265.3 mA·h/g, and its capacity retaining rate （S20） at the 20th cycle increases from 31.3% to 70.2%. Furthermore, the high rate dischargeability （HRD）, electrochemical impedance spectrum and potential-step measurements all indicate that the electrochemical kinetics of the alloy electrodes first increases then decreases with raising the amount of Mn substitution.

Electrochemical hydrogen storage characteristics of as-cast and annealed La_(0.8-x)Nd_xMg_(0.2)Ni_(3.15)Co_(0.2)Al_(0.1)Si_(0.05)(x=0-0.4)alloys

The La-Mg-Ni-based A2B7-type La0.8-xNdxMg0.2Ni3.15Co0.2Al0.15 （x=0, 0.1, 0.2, 0.3, 0.4） electrode alloys were prepared by casting and annealing. The influences of partial substitution of Nd for La on the structure and electrochemical performance of the as-cast and annealed alloys were investigated. It was found that the experimental alloys consist of two major phases, （La, Mg）2Ni7 phase with the hexagonal Ce2Ni7-type structure and LaNi5 phase with the hexagonal CaCu5-type structure, as well as some residual phase LaNi3 and NdNi5. The discharge capacity and high rate discharge ability （HRD） of the as-cast and annealed alloys first increase and then decrease with Nd content growing. The as-cast and annealed alloys （x=0.3） yield the largest discharge capacities of 380.3 and 384.3 mA·h/g, respectively. The electrochemical cycle stability of the as-cast and annealed alloys markedly grows with Nd content rising. As the Nd content increase from 0 to 0.4. The capacity retaining rate （S100） at the 100th charging and discharging cycle increases from 64.98% to 85.17% for the as-cast alloy, and from 76.60% to 96.84% for the as-annealed alloy.

Key technology and application of AB_(2) hydrogen storage alloy in fuel cell hydrogen supply system

At present,there is limited research on the application of fuel cell power generation system technology using solid hydrogen storage materials,especially in hydrogen-assisted two-wheelers.Considering the disadvantages of low hydrogen storage capacity and poor kinetics of hydrogen storage materials,our primary focus is to achieve smooth hydrogen ab-/desorption over a wide temperature range to meet the requirements of fuel cells and their integrated power generation systems.In this paper,the Ti_(0.9)Zr_(0.1)Mn_(1.45)V_(0.4)Fe_(0.15) hydrogen storage alloy was successfully prepared by arc melting.The maximum hydrogen storage capacity reaches 1.89 wt% at 318 K.The alloy has the capability to absorb 90% of hydrogen storage capacity within 50 s at 7 MPa and release 90% of hydrogen within 220 s.Comsol Multiphysics 6.0 software was used to simulate the hydrogen ab-/desorption processes of the tank.The flow rate of cooling water during hydrogen absorption varied in a gradient of(0.02 t x)m s^(-1)(x=0,0.02,0.04,0.06,0.08,0.1,0.12).Cooling water flow rate is positively correlated with the hydrogen absorption rate but negatively correlated with the cost.When the cooling rate is 0.06 m s^(-1),both simulation and experimentation have shown that the hydrogen storage tank is capable of steady hydrogen desorption for over 6 h at a flow rate of 2 L min^(-1).Based on the above conclusions,we have successfully developed a hydrogen-assisted two-wheeler with a range of 80 km and achieved regional demonstration operations in Changzhou and Shaoguan.This paper highlights the achievements of our team in the technological development of fuel cell power generation systems using solid hydrogen storage materials as hydrogen storage carriers and their application in twowheelers in recent years.

Comparative study on the hydrogen storage performance of as-milled MgRENi rapid quenched alloy catalyzed by metal sulfides

The composites of Mg_(20)Pr_(1)Sm_(3)Y_(1)Ni_(10)as-quenched alloy and 3 wt.%M(M=CoS,CoS_(2),MoS_(2))catalyst were prepared by high-speed vibration ball mill.The effects of metal sulfides on the hydrogenation and dehydrogenation dynamics of alloys were compared.The results show that the as-milled composites contain a large number of amorphous embedded by a small amount of nanocrystals,and there are many point defects.After ball milling,the crystal grain size in the composites containing CoS is relatively larger,followed by CoS_(2)and MoS_(2)again.After hydrogenation,the amorphous phase is crystallized to form Mg_(2)NiH_(4),YH_(3),Pr_(8)H_(18.96),Sm_(3)H_7,Mg,Co or Mo phases,however,Mg_(2)Ni,YH_(2),PrH_(2)and Ni_(3)Y phases appeared after dehydrogenation.The maximum hydrogenation capacity of the composites containing CoS,CoS_(2)and MoS_(2)are 3.939,4.265 and 4.507 wt.%,respectively.The hydrogenation saturation ratio of composite containing MoS_(2)is higher than that of the composites containing CoS and CoS_(2).The dehydrogenation activation energy of the composites containing CoS,CoS_(2)and MoS_(2)is 107.76,68.43 and 63.28 kJ.mol^(-1).H_(2).On the improvement of hydrogen storage performance of Mg_(20)Pr_(1)Sm_(3)Y_(1)Ni_(10)alloy,the catalytic effect of MoS_(2)sulfide is better than that of CoS_(2)sulfide,and which is better than CoS sulfide.

Hydrogen storage behaviours of nanocrystalline and amorphous Mg_(20)Ni_(10-x)Co_x(x=0-4) alloys prepared by melt spinning

The Mg2Ni-type alloys with nominal compositions of Mg20Ni10-xCox(x=0,1,2,3,4,%,mass fraction) were prepared by melt-spinning technology.The structures of the alloys were studied by XRD,SEM and HRTEM.The hydrogen absorption/desorption kinetics and the electrochemical performances of the alloys were measured.The results show that no amorphous phase forms in the as-spun Co-free alloy,but the as-spun alloys containing Co show a certain amount of amorphous phase.The hydrogen absorption capacities of the as-cast alloys first increase and then decrease with the incremental change of Co content.The hydrogen desorption capacities of as-cast and spun alloys rise with increasing Co content.The melt spinning significantly improves the hydrogenation and dehydrogenation capacities and kinetics of the alloys.The substitution of Co for Ni clearly enhances the discharge capacities of the alloys and the cycle stability of the as-spun alloys.

Influences of melt spinning on electrochemical hydrogen storage performance of nanocrystalline and amorphous Mg_2Ni-type alloys

In order to improve the electrochemical hydrogen storage performance of the Mg2Ni-type electrode alloys, Mg in the alloy was partially substituted by La, and the nanocrystalline and amorphous Mg2Ni-type Mg20-xLaxNi10 （x-=0, 2） alloys were synthesized by melt-spinning technique. The microstructures of the as-spun alloys were characterized by X-ray diffraction （XRD）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The electrochemical hydrogen storage properties of the experimental alloys were tested. The results show that no amorphous phase is detected in the as-spun Mg20Ni10 alloy, but the as-spun Mg18La2Ni10 alloy holds a major amorphous phase. As La content increases from 0 to 2, the maximum discharge capacity of the as-spun （20 m/s） alloys rises from 96.5 to 387.1 mA.h/g, and the capacity retaining rate （S20） at the 20th cycle grows from 31.3% to 71.7%. Melt-spinning engenders an impactful effect on the electrochemical hydrogen storage performances of the alloys. With the increase in the spinning rate from 0 to 30 m/s, the maximum discharge capacity increases from 30.3 to 135.5 mA.h/g for the Mg20Ni10 alloy, and from 197.2 to 406.5 mA-h/g for the Mg18La2Ni10 alloy. The capacity retaining rate （S20） of the Mg2oNi10 alloy at the 20th cycle slightly falls from 36.7% to 27.1%, but it markedly mounts up from 37.3% to 78.3% for the Mg18La2Ni10 alloy.

Gaseous and Electrochemical Hydrogen Storage Kinetics of As-quenched Nanocrystalline and Amorphous Mg_2Ni-type Alloys

The nanocrystalline and amorphous Mg2Ni-type Mg2Ni1-xCox （x = 0, 0.1, 0.2, 0.3, 0.4） alloys were synthesized by melt quenching technology. The structures of the as-cast and quenched alloys were characterized by XRD, SEM and HRTEM. The gaseous hydrogen storage kinetics of the alloys was measured using an automatically controlled Sieverts apparatus. The alloy electrodes were charged and discharged with a constant current density in order to investigate the electrochemical hydrogen storage kinetics of the alloys. The results demonstrate that the substitution of Co for Ni results in the formation of secondary phases MgCo2 and Mg instead of altering the major phase Mg2Ni. No amorphous phase is detected in the as-quenched Co- ffee alloy, however, a certain amount of amorphous phase is clearly found in the as-quenched alloys substituted by Co. Furthermore, both the rapid quenching and the Co substitution significantly improve the gaseous and electrochemical hydrogen storage kinetics of the alloys, for which the notable increase of the hydrogen diffusion coefficient （D） along with the limiting current density （IL） and the obvious decline of the electrochemical impedance generated by both the Co substitution and the rapid quenching are basically responsible.

Characteristics of Hydrogen Storage Alloy Mg_2Ni Produced by Hydriding Combustion Synthesis

A high activity and large capacity of hydrogen storage alloy Mg2Ni by hydriding combustion synthesis was investigated by means of pressure composition isotherms, X-ray diffraction and scanning electron microscopy. The results showed that the maximum hydrogen absorption capacity of Mg2Ni is 3.25 mass fraction at 523 K, just after synthesis without any activation. The relationships between the equilibrium plateau pressure and the temperature for Mg2Ni were lgp (0.1 MPa)=-3026/T+5.814 (523 K≤T≤623 K) for hydriding and Igp (0.1 MPa)=-3613/T+6.715 (523 K≤T ≤623 K) for dehydriding. The kinetic equation is [-ln(1-a)]3/2 = kt and the apparent activation energy for the nucleation and growth-controlled hydrogen absorption and desorption were determined to be 64.3±2.31kJ/(mol.H2) and 59.9±2.99kJ/(mol.H2)respectively.

Influences of substituting Ni with M(M=Cu,Co,Mn)on gaseous and electrochemical hydrogen storage kinetics of Mg_(20)Ni_(10) alloys

In this work,a comprehensive comparison regarding the impacts of M(M=Cu,Co,Mn)substitution for Ni on the structures and the hydrogen storage kinetics of the nanocrystalline and amorphous Mg20Ni10-xMx(M=Cu,Co,Mn; x=0-4)alloys prepared by melt spinning has been carried out.The analysis of XRD and TEM reveals that the as-spun(M=None,Cu)alloys display an entire nanocrystalline structure,whereas the as-spun(M=Co,Mn)alloys hold a mixed structure of nanocrystalline and amorphous structure when M content x=4,indicating that the substitution of M(M=Co,Mn)for Ni facilitates the glass formation in the Mg2Ni-type alloy.Besides,all the as-spun alloys have a major phase of Mg2Ni but M(M=Co,Mn)substitution brings on the formation of some secondary phases,MgCo2 and Mg phases for M=Co as well as MnNi and Mg phases for M=Mn.Based upon the measurements of the automatic Sieverts apparatus and the automatic galvanostatic system,the impacts engendered by M(M=Cu,Co,Mn)substitution on the gaseous and electrochemical hydrogen storage kinetics of the alloys appear to be evident.The gaseous hydriding kinetics of the alloys first rises and then declines with the growing of M(M=Cu,Co,Mn)content.Particularly,the M(M= Mn)substitution results in a sharp drop in the hydriding kinetics when x=4.The M(M=Cu,Co,Mn)substitution ameliorates the dehydriding kinetics dramatically in the order(M=Co)>(M=Mn)>(M=Cu).The electrochemical kinetics of the alloys visibly grows with M content rising for(M=Cu,Co),while it first increases and then declines for(M=Mn).

Structure and Electrochemical Properties of A_2B_7-Type La-Mg-Ni Hydrogen Storage Alloys

Investigation of alloy structure shows that La2-xMgxNi7 （x = 0.3 - 0.8） alloys are mainly com- posed of Ce/Ni7-type, Gd2Co7-type and PuNi3-type phase. The influence of Mg content in alloys on the phase structure is great, resulting in a linear decrease of the unit cell parameters of main phases and increase of hydrogen absorption/desorption plateau as Mg content increases. Electrochemical measurements show that as the Mg content increases, the discharge capacity of alloy electrodes first increases and then decreases. The cyclic stability presents a deteriorative trend. La1.4Mg0.6 Ni7 alloy electrode exhibits the maximum electrochemical discharge capacity （378 mAh·g^-1）, and the La1.6Mg0.4Ni7 alloy electrode shows the best cyclic stability （S270 = 81%）.

Effect of praseodymium substitution for lanthanum on structure and properties of La_(0.65-x)Pr_xNd_(0.12)Mg_(0.23)Ni_(3.4)Al_(0.1)(x=0.00–0.20) hydrogen storage alloys

In order to investigate the effect of substituting La with Pr on structural and hydrogen storage properties of La-Mg-Ni system （AB3.5-type） hydrogen storage alloys, a series of La0.65-xPrxNd0.12Mg0.23Ni3.4Al0.1（x=0, 0.10, 0.15, 0.2） hydrogen storage alloys were prepared. X-ray diffraction （XRD）, scanning electron microscopy （SEM） and energy dispersive spectrometer （EDS） analyses revealed that two alloys （x=0.0 and 0.10） were composed of （La,Mg）2（Ni,Al）7 phase, La（Ni,A1）5 phase and （La,Mg）Ni2 phase, while other alloys （x=0.15 and 0.20） consisted of （La,Mg）2（Ni,A1）7 phase, La（Ni,A1）5 phase, （La,Mg）Ni2 phase and （La,Mg）（Ni,A1）3 phase. All alloys showed, however, only one pressure plateau in P-C isotherms. The Pr/La ratio in alloy composition influenced hydrogen storage capacity and kinetics properties. Electrochemical studies showed that the discharge capacity decreased from 360 mAh/g （x=-0.00） to 335 mAh/g （x=-0.20） as x increased. But the high-rate dischargeability （HRD） of alloy electrodes increased from 26% （x=0.00） to 56% （x=-0.20） at a discharge current density of Id=1800 mA/g. Anode polarization measurements were done to further understand the electrochemical kinetics properties after Pr substitution.

Hydrogen storage properties of Mg-doped Ti_(1.2)Fe alloys synthesized by mechanical alloying

Hydrogen storage properties and phase components of Mg doped TiFe alloys, that were prepared by Ti, Fe and Mg metal powders using a mechanical alloying technique, were studied. XRD analyses show that the main phase of all the Mg doped Ti 1.2 Fe alloys is the TiFe phase. Some TiFe 2 phase and α Ti phase exist as secondary phases and Mg is dispersed in the alloy matrix. 3% Mg doped and 5% Mg doped Ti 1.2 Fe alloy samples can be fully activated within three hydriding/dehydriding cycles at room temperature and the hydrogen storage capacities of the alloys can reach 222 mL/g and 198 mL/g, respectively. Both two samples exhibit only one plateau region in their P C T curves with a low hydrogen absorption/desorption pressure hysteresis. The effect and mechanism of Mg addition as well as overstoichiometric Ti on the activation properties and hydrogen storage capacities of the alloys was also discussed.

Influence of rapid quenching on hydrogen storage characteristics of nanocrystalline Mg_2Ni-type alloys

Nanocrystalline Mg2Ni-type alloys with nominal compositions of Mg20Ni10–xCux(x=0,1,2,3,4,mass fraction,%) were synthesized by rapid quenching technique.The microstructures of the as-cast and quenched alloys were characterized by XRD,SEM and HRTEM.The electrochemical hydrogen storage performances were tested by an automatic galvanostatic system.The hydriding and dehydriding kinetics of the alloys were measured using an automatically controlled Sieverts apparatus.The results show that all the as-quenched alloys hold the typical nanocrystalline structure and the rapid quenching does not change the major phase Mg2Ni.The rapid quenching significantly improves the electrochemical hydrogen storage capacity of the alloys,whereas it slightly impairs the cycling stability of the alloys.Additionally,the hydrogen absorption and desorption capacities of the alloys significantly increase with rising quenching rate.

Influences of stoichiometric ratio B/A on structures and electrochemical behaviors of La_(0.75)Mg_(0.25)Ni_(3.5)M_x (M=Ni,Co;x=0-0.6) hydrogen storage alloys

In order to investigate the influences of the stoichiometric ratio of B/A (A: gross A-site elements, B: gross B-site elements) and the substitution of Co for Ni on the structures and electrochemical performances of the AB3.5-4.1-type electrode alloys, the La-Mg-Ni-Co system La0.75Mg0.25Ni3.5Mx (M=Ni, Co; x= 0, 0.2, 0.4, 0.6) alloys were prepared by induction melting in a helium atmosphere. The structures and electrochemical performances of the alloys were systemically measured. The results show that the structures and electrochemical performances of the alloys are closely relevant to the B/A ratio. All the alloys exhibit a multiphase structure, including two major phases, (La, Mg)2Ni7 and LaNi5, and a residual phase LaNi2, and with rising ratio B/A, the (La,Mg)2Ni7 phase decreases and the LaNi5 phase increases significantly. When ratio B/A=3.7, the alloys obtain the maximum discharge capacities. The high rate discharge(HRD) capability of the alloy (M=Ni) monotonously rises with growing B/A ratio, but that of the alloy (M=Co) first mounts up then declines. The cycle stability of the alloy (M=Co) monotonously increases with rising B/A ratio, but it first decreases slightly then increases for the alloy (M=Ni). The discharge potential of the alloy (M=Ni) declines with increasing B/A ratio (x>0.2), but for the alloy (M=Co), the result is contrary. The substitution of Co for Ni significantly ameliorates the electrochemical performances. For a fixed ratio B/A=3.7, the Co substitution enhances the discharge capacity from 365.7 to 401.8 mA·h/g, the capacity retention ratio (S100) after 100 charging-discharging cycles from 50.32% to 53.26% and the HRD from 88.65% to 90.69%.

Preparation of ZrMn_2 hydrogen storage alloy by electro-deoxidation in molten calcium chloride

ZrMn2 alloy was electro-synthesized directly from cathode pellets compacted with powdered mixture of MnO2 and ZrO2 in molten calcium chloride. Sintering temperature, cell voltage and electrolysis time were the dominant factors that affected the characteristics of the final product. The results confirmed the formation of pure ZrMn2 alloy through the electro-deoxidation of the mixed oxide pellets at 3.1 V for 12 h in 900 °C CaCl2 melt. The X-ray diffraction（XRD） and cyclic voltammetry analysis suggested that the electro-deoxidation proceeded from the reduction of manganese oxides to Mn, followed by ZrO2 or CaZrO3 reduction on the pre-formed Mn to ZrMn2 alloy. The cyclic voltammetry measurements using powder microelectrode showed that the prepared ZrMn2 alloy has a good electrochemical hydrogen storage property.

Effect of melt spinning on gaseous hydrogen storage characteristics of nanocrystalline and amorphous Nd-added Mg_2Ni-type alloys

Nanocrystalline and amorphous Mg-Nd-Ni-Cu quaternary alloys with a composition of(Mg_(24)Ni_(10)Cu_2)_(100-x)Nd_x(x=0, 5, 10, 15, 20) were prepared by melt spinning technology and their structures as well as gaseous hydrogen storage characteristics were investigated. The XRD, TEM and SEM linked with EDS detections reveal that the as-spun Nd-free alloy holds an entire nanocrystalline structure but a nanocrystalline and amorphous structure for the as-spun Nd-added alloy, implying that the addition of Nd facilitates the glass forming in the Mg_2Ni-type alloy. Furthermore, the degree of amorphization of the as-spun Nd-added alloy and thermal stability of the amorphous structure clearly increase with the spinning rate rising. The melt spinning ameliorates the hydriding and dehydriding kinetics of the alloys dramatically. Specially, the rising of the spinning rate from 0(the as-cast was defined as the spinning rate of 0 m/s) to 40 m/s brings on the hydrogen absorption saturation ratio(R_5~a)(a ratio of the hydrogen absorption quantity in 5 min to the saturated hydrogen absorption capacity) increasing from 36.9% to 91.5% and the hydrogen desorption ratio(R_(1 0)~d)(a ratio of the hydrogen desorption quantity in 10 min to the saturated hydrogen absorption capacity) rising from 16.4% to 47.7% for the(x=10) alloy, respectively.

Influence of addition of Cu(OH)_2 to KOH alkaline electrolyte on electrochemical properties of La_2Mg_(0.9)Al_(0.1)Ni_(7.5)Co_(1.5) hydrogen storage alloy electrode

The influence of the addition of Cu(OH)2 to 6 mol/L KOH alkaline electrolyte on the electrochemical properties of La2Mg0.9Al0.1Ni7.5Co1.5 hydrogen storage alloy electrode was investigated by electron probe X-ray microanalysis(EPMA),X-ray diffraction(XRD) and electrochemical measurements. EPMA micrographs and XRD patterns show that the surface of the hydride electrode is plated by metal copper film. The thickness and compactness of Cu film increase with the increment of charge-discharge cycle number. The copper film of the hydride electrode surface can keep the hydrogen storage alloy particle in the electrode interior from oxidizing availably. The addition of Cu(OH)2 to alkaline electrolyte lowers the activation property and the high rate dischargeability of the La2Mg0.9Al0.1Ni7.5Co1.5 hydride electrode,but has no negative effect on the maximum discharge capacity of the hydride electrode. Moreover,it is effective to improve the cyclic stability of the hydride electrode utilizing electrodeposit Cu film on the La2Mg0.9Al0.1Ni7.5Co1.5 hydride electrodes surface.

Geometric Effects of La_(1+x)Mg_(2-x)Ni_9 (x=0.0~1.0) Ternary Alloys on Their Hydrogen Storage Capacities

Structural analysis was made using X-ray diffraction (XRD) Rietveld refinement on a series of La1+xMg2-xNi9 (x=0.0-1.0) ternary alloys. Results showed that each of La1+xMg2-xNi9 alloys was a PuNi3-type structure stacked by LaNi5 and (La, Mg) Ni2 blocks. Electrochemical tests revealed that discharge abilities of these La-Mg-Ni ternary alloys mainly depended on their atomic distances between (La, Mg) and Ni, which could be modified by varying the atomic ratios of La/Mg.