Microstructure and mechanical properties of AZ31-Mg_2Si in situ composite fabricated by repetitive upsetting

AZ31-4.6% Mg2Si （mass fraction） composite was prepared by conventional casting method. Repetitive upsetting （RU） was applied to severely deforming the as-cast composite at 400 ℃ for 1, 3, and 5 passes. Finite element analysis of the material flow indicates that deformation concentrates in the bottom region of the sample after 1 pass, and much more uniform deformation is obtained after 5 passes. During multi-pass RU process, both dendritic and Chinese script type Mg2Si phases are broken up into smaller particles owing to the shear stress forced by the matrix. With the increasing number of RU passes, finer grain size and more homogeneous distribution of Mg2Si particles are obtained along with significant enhancement in both strength and ductility. AZ31-4.6%Mg2Si composite exhibits tensile strength of 284 MPa and elongation of 9.8%after 5 RU passes at 400 ℃ compared with the initial 128 MPa and 5.4%of original AZ31-4.6%Mg2Si composite.

Microstructure evolution,mechanical properties and fracture behavior of Al-xSi/AZ91D bimetallic composites prepared by a compound casting

In this paper,the effect of the Si content on microstructure evolution,mechanical properties,and fracture behavior of the Al-xSi/AZ91D bimetallic composites prepared by compound casting was investigated systematically.The obtained results showed that all the Al-xSi/AZ91D bimetallic composites had a metallurgical reaction layer(MRL),whose thickness increased with increasing Si content for the hypoeutectic Al-Si/AZ91D composites,while the hypereutectic Al-Si/AZ91D composites were opposite.The MRL included eutectic layer(E layer),intermetallic compound layer(IMC layer)and transition region layer(T layer).In the IMC layer,the hypereutectic Al-Si/AZ91D composites contained some Si solid solution and flocculent Mg_(2)Si+Al-Mg IMCs phases not presented in the hypoeutectic Al-Si/AZ91D composites.Besides,increasing Si content,the thickness proportion of the T layer increased,forming an inconsistent preferred orientation of the MRL.The shear strengths of the Al-xSi/AZ91D bimetallic composites enhanced with increasing Si content,and the Al-15Si/AZ91D composite obtained a maximum shear strength of 58.6 MPa,which was 73.4% higher than the Al-6Si/AZ91D composite.The fractures of the Al-xSi/AZ91D bimetallic composites transformed from the T layer into the E layer with the increase of the Si content.The improvement of the shear strength of the Al-xSi/AZ91D bimetallic composites was attributed to the synergistic action of the Mg_(2)Si particle reinforcement,the reduction of oxidizing inclusions and the ratio of Al-Mg IMCs as well as the orientation change of the MRL.

Influence of solution treatment on microstructure and properties of in-situ Mg_2Si/AZ91D composites

The influence of solution treatment on the microstructure and properties of Mg2Si/AZ91D composites fabricated from Mg-SiO2 system via in-situ processing method was investigated.The results show that coarse Chinese script shape Mg2Si phases can be formed by adding SiO2 into AZ91D magnesium alloy with Si content up to 1.5% of the alloy melt.During solution treatment,the morphology and distribution of the coarse Chinese script shape Mg2Si phases are modified.Meanwhile,the β-Mg17Al12 phase is dissolved into the magnesium matrix.With increasing holding time,the coarse Mg2Si phases tend to dissolve,break and spheroidize.After solution treatment at 420 ℃ for 16 h,Mg2Si phases become the finest and relatively well-distributed phase.The tensile strength and elongation are increased by 14.9% and 38.9%,respectively.It is believed that the Mg2Si phases continuously dissolve and break,and finally the spheroidized Mg2Si particles are obtained due to the interface tension of Mg2Si/Mg interface.

选区激光熔化成形TiB_(2)/Al-Si-Mg大尺寸复杂构件

选区激光熔化(SLM)成形大尺寸复杂构件厚度多样、成形高度较高、方向复杂,需要研究构件微观组织均匀性和力学性能稳定性。本文以SLM成形TiB_(2)/Al-Si-Mg复合材料为研究对象,分析复合材料多级微观组织,对比不同成形厚度、高度、方向下复合材料的力学性能。结果表明:复合材料表现出熔池特征结构,细小等轴晶粒组织均匀分布且随机取向,纳米TiB_(2)颗粒在材料内部弥散分布。随成形厚度增加,复合材料伸长率保持稳定,抗拉强度受本征热处理影响略微增大;在不同成形高度下,复合材料抗拉强度和伸长率保持稳定;在不同成形方向下,复合材料抗拉强度保持稳定,伸长率受熔池结构影响在水平方向略高。基于以上结果,成功制备大飞机舱门铰链臂(588 mm×318 mm×470 mm)复杂结构件。

Laser Cladding Al-Si/Al_2O_3-TiO_2 Composite Coatings on AZ31B Magnesium Alloy

To improve the wear resistance and corrosion resistance of magnesium alloys, a 5 kW continuous wave CO2 laser was used to investigate the laser surface cladding on AZ31 B magnesium alloys with Al-Si/Al2O3-TiO2 composite powders. A detailed microstructure, chemical composition, and phase analysis of the composite coatings were studied by scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, and X-ray diffraction （XRD）. The laser cladding shows good metallurgical bonding with the substrate. The composite coatings are composed of Mgl7Al12, Al3Mg2, Mg2Si, Al2O3, and TiO2 phases. Compared to the average microhardness （50HV0.05） of the AZ3 1 B substrate, that of the composite coatings （230HV0.05） is improved significantly. The wear resistances of the surface layers were evaluated in detail. The results demonstrate that the wear resistances of the laser surface-modified samples are considerably improved compared to the substrate. It also show that the composite coatings exhibit better corrosion resistance than that of the substrate in 3.5wt% NaCI solution.

Effect of ultrasonic on morphology of primary Mg_2Si in in-situ Mg_2Si/Al composite

Effects of ultrasonic on morphologies of primary Mg2Si crystals in in-situ Mg2Si/A1 composite were investigated by metallographic microscopy and field emission scanning electron microscopy. The results show that the mean grain size of primary MgESi crystals is refined from 150 to 20 μm by high intensity ultrasonic, and the morphologies of primary MgESi crystals are changed as well. Optical microscopy reveals that primary MgESi crystals without ultrasonic vibration exhibit coarse particles with cavities, in which eutectic structures grow. However, primary Mg2Si crystals with ultrasonic vibration appear fine grains without any cavity. Three-dimensional morphologies of primary Mg2Si without ultrasonic vibration display octahedron and tetrakaidecahedron with hopper-like hole in the crystals. After ultrasonic vibration, primary Mg2Si particles become solid crystals with rounded comers and edges.

AZ31B镁合金表面火焰喷涂Al-Mg_2Si涂层的耐腐蚀性能

为提高AZ31B镁合金表面的耐腐蚀性能,用火焰喷涂方法在镁合金表面制备Al-Mg_2Si复合涂层。采用XRD、SEM和EDS分析涂层的物相组成、微观组织及元素分布;通过电化学试验测试样品在3.5%NaCl溶液中的腐蚀电位、腐蚀电流密度;通过3.5%NaCl溶液浸泡试验测试样品的腐蚀速率;并测试涂层的显微硬度。结果表明:涂层中的主要物相有Mg_2Si、Al,组织比较致密,元素分布均匀。Tafel极化曲线测试表明,Al-Mg_2Si涂层样品与AZ31B镁合金样品相比腐蚀电位从-1.489 V正移到-1.366 V,腐蚀电流密度从2.817×10^(-3) A/cm^2降低到1.198×10^(-3) A/cm^2。浸泡试验结果表明,喷涂Al-Mg_2Si的镁合金的腐蚀速率明显低于没有喷涂的镁合金。显微硬度测试表明,涂层的显微硬度集中分布在259~308 HV0.05之间,镁合金为50~60 HV0.05。因此在AZ31B镁合金表面火焰喷涂Al-Mg_2Si涂层可以提高其耐腐蚀性能,表面硬度显著提高。

多道次闭式模锻对Mg2Si/AZ31复合材料微观组织和性能的影响

采用常规铸造方法制备了Mg2Si/AZ31复合材料,然后在400℃进行5道次闭式模锻加工,研究复合材料的微观组织、拉伸力学性能和耐磨性能。结果表明:模锻过程中基体施加的剪切应力将树枝状和汉字状的Mg2Si相破碎成细小颗粒,随着模锻道次的增加,复合材料晶粒尺寸逐渐细化,Mg2Si颗粒分布更加均匀,同时强度、塑性和耐磨性显著提高,模锻5道次后,复合材料的抗拉强度、伸长率从铸态的98 N/mm2、3.3%分别提高到175 N/mm2、18.2%。

Microstructure and dry sliding wear behavior of cast Al-Mg_2Si in-situ metal matrix composite modified by Nd

The microstructure and dry sliding wear behav- ior of cast Al-18 wt% MgaSi in-situ metal matrix com- posite modified by Nd were investigated. Experimental results show that, after introducing a proper amount of Nd, both primary and eutectic Mg2Si in the Al-18 wt% Mg2Si composite are well modified. The morphology of primary Mg2Si is changed from irregular or dendritic to polyhedral shape, and its average particle size is signifi- cantly decreased. Moreover, the morphology of the eutectic MgzSi phase is altered from flake-like to very short fibrous or dot-like. The wear rates and friction coefficient of the composites with Nd are lower than those without Nd. Furthermore, the addition of 0.5 wt% Nd changes the wear mechanism of the composite from the combination of abrasive, adhesive, and delamination wear without Nd into a single mild abrasion wear with 0.5 wt% Nd.

Characteristics of two Al based functionally gradient composites reinforced by primary Si particles and Si/in situ Mg_2Si particles in centrifugal casting

Two kinds of Al based functionally gradient composite tubes reinforced by primary Si particles alone and primary Si/in situ Mg2Si particles jointly were successfully prepared by centrifugal casting,and their structural and mechanical characters were compared.It is found that the composite reinforced with primary Si particles takes a characteristic of particles distribution both in the inner and outer layers.However,composite reinforced with primary Si/Mg2Si particles jointly takes a characteristic of particles distribution only in the inner layer and shows a sudden change of particles distribution across the section of inner and outer layers.The hardness and wear resistance of Al-19Si-5Mg tube in the inner layer are greatly higher than that in the other layers of Al-19Si-5Mg tube and Al-19Si tube.Theoretical analysis reveals that the existence of Mg2Si particles is the key factor to form this sudden change of gradient distribution of two kinds of particles.Because Mg2Si particles with a lower density have a higher centripetal moving velocity than primary Si particles,in a field of centrifugal force,they would collide with primary Si particles and then impel the later to move together forward to the inner layer of the tube.

Effect of Bi modification treatment on microstructure,tensile properties,and fracture behavior of cast Al-Mg_2Si metal matrix composite

Bi has a good modification effect on the hypoeutectic Al-Si alloy, and the morphology of eutectic Si changes from coarse acicular to fine fibrous. Based on the similarity between Mg2Si and Si phases in crystalline structure and crystallization process, the present study investigated the effects of different concentrations of Bi on the microstructure, tensile properties, and fracture behavior of cast Al-15wt.%Mg2Si in-situ metal matrix composite. The results show that the addition of the proper amount of Bi has a significant modification effect on both primary and eutectic Mg2Si in the Al-15wt.%Mg2Si composite. With an increase in Bi content from 0 to lwt.%, the morphology of the primary Mg2Si is changed from irregular or dendritic to polyhedral shape; and its average particle size is significantly decreased from 70 to 6 μm. Moreover, the morphology of the eutectic Mg2Si phase is altered from flake-like to very short fibrous or dot-like. When the Bi addition exceeds 4.0wt.%, the primary Mg2Si becomes coarse again. However, the eutectic Mg2Si still exhibits the modified morphology. Tensile tests reveal that the Bi addition can improve the tensile strength and ductility of the material. Compared with those of the unmodified composite, the ultimate tensile strength and percentage elongation after fracture with 1.0wt.% Bi increase 51.2% and 100%, respectively. At the same time, the Bi addition changes the fracture behavior from brittle to ductile.

Effect of SiC particle addition on microstructure of Mg_2Si/Al composite

In the present study, by adding SiC particles into AI-Si-Mg melt, Mg2Si and SiC particles hybrid reinforced AI matrix composites were fabricated through the Mg2Si in situ synthesis in melt combined with the SiC ex situ stir casting. The as-cast microstructure containing primary Mg2Si and SiC particles that distribute homogenously in AI matrix was successfully achieved. The effects of SiC particle addition on the microstructure of Mg2Si/AI composites were investigated by using scanning electron microscopy （SEM） and XRD. The results show that, with increasing the fraction of the SiC particles from 5wt.% to 10wt.%, the morphologies of the primary Mg2Si particulates in the prepared samples remain polygonal, but the size of the primary phase decreases slightly. However, when the SiC particle addition reaches 15wt.%, the morphologies of the primary Mg2Si particulates change partially from polygonal to quadrangular with a decrease in size from 50 pm to 30 μm. The size of primary AI dendrites decreases with increasing fraction of the SiC particles from 0wt.% to 15wt.%. The morphology of the eutectic Mg2Si phase changes from a fiber-form to a short fiber-form and/or a dot-like shape with increasing fraction of the SiC particles. Furthermore, no significant change in dendrite arm spacing （DAS） was observed in the presence of SiC particles.

Microstructure and Mechanical Behavior of in Situ Primary Si/Mg_2Si Locally Reinforced Aluminum Matrix Composites Piston by Centrifugal Casting

Al-Si pistons are frequently damaged by burning piston top surface due to elevated combustion temperature, and by rubbing the first ring groove against the engine cylinder liner. To prevent piston from these damages, some technologies were invented, such as mounting high Ni cast iron ring around the first ring groove in Al alloy piston body and thermal resistant steel on piston top surface, and fabricating Al composite pistons by squeeze casting for enhancing the whole or local piston performance. In this paper, composite pistons locally reinforced with in situ primary Si and primary Mg2Si particles are fabricated by centrifugal casting. The microstructure characteristics, hardness and wear resistance of the composite piston are investigated and the motion characteristic of the in situ particles in centrifugal field is analyzed. The results of the experiments show that primary Si and Mg2Si particles mix up with each other in melt and segregate at the regions of piston top and piston ring grooves under the effect of centrifugal force. Particulate reinforced regions have a higher hardness and better wear resistance compared with the unreinforced regions and this performance increases after heat treatment. The analysis result of particle movement shows that, primary Si and primary Mg2Si particles move at approximately the same velocity in the centrifugal field, because of the growth of primary Si and fusion after colliding between primary Si particles, which compromised the velocity difference of primary Si and primary Mg2Si particles caused by the difference of their densities. Research results have some theory significance and applicative value of project in development of new aluminum matrix composites piston products.

Effect of Sb on microstructure and mechanical properties of Mg_2Si/Al-Si composites

The effect of Sb on the microstructure and mechanical properties of Mg2Si/Al-Si composites was investigated.The results show that Sb can improve the microstructure and mechanical properties of Mg2Si/Al-Si composites.When the content of Sb is 0.4%,the morphology of primary Mg2Si changes from dendrites to fine particles,the average size of Mg2Si particles is refined from 52 to 25μm,and the ultimate tensile strength and elongation of the composites increase from 102.1 MPa and 0.26% to 138.6 MPa and 0.36%,respectively.The strengthening mechanism can be attributed to the fine-grain strengthening.However,excessive Sb is disadvantageous to the modification of the composites.

Rheological behavior of semi-solid Mg_2Si/AM60 magnesium matrix composites at steady state

The microstructure and rheological behavior of semi-solid Mg2Si/AM60 magnesium matrix composite at steady state were investigated.The results show that the primary α-Mg phases are knapped by mechanical stirring and the Chinese script type reinforced Mg2Si phases exist in liquid phase and grain boundary.The analysis of apparent viscosity indicates that the apparent viscosity of semi-solid Mg2Si/AM60 magnesium matrix composite at steady state increases with increasing the volume fraction of Mg2Si and solid fraction of primary α-Mg,but decreases with increasing the shearing rate and shearing time,and the apparent viscosity keeps stable when shearing time reaches 300 s.

Structure and Mechanical Properties of Al-based Gradient Composites Reinforced with Primary Si and Mg_2Si Particles through Centrifugal Casting

The structure and mechanical properties of a new type of Al-based discontinuous gradient composites prepared by using the ternary AI-19Si-5Mg alloys as the raw material adopting the centrifugal casting method were investigated. Structurally, the composites are divided into two zones： a reinforced zone with the high volume fraction of primary Si and Mg2Si particles and an unreinforced zone with no or a few particles. In the reinforced zone, the primary particles are evenly distributed, with the sizes of the primary Si particles 80-120 μm, and that of primary Mg2Si particles 20-50 μm. The properties test results show the reinforced zone has higher Rockwell hardness and better wear resistance than the unreinforced zone, due to the complementary reinforcement relationship between the primary Si and Mg2Si particles and their high volume fraction.

Influence of Sb modification on microstructures and mechanical properties of Mg2 Si/AM60 composites

The refining effect and mechanism of Sb on Mg2Si and the microstructure of the matrix were investigated.The results indicate that there are Mg3Sb2 particles in the composites with the addition of Sb,and Mg3Sb2 can promote the formation of fine polygonal type Mg2Si by providing nucleation site.Meanwhile,the grain size of Sb modified alloy is finer than that of the matrix. The improved microstructure results in the improvement of mechanical properties.The ultimate tensile strength is increased by 12.2%with the addition of 0.8%Sb.

Modii cation ef ect of calcium-magnesia phosphate fertilizer on microstructure and mechanical properties of Mg_2Si/Mg-4Si composite

In order to modify in-situ synthesized Mg_2Si particles in Mg_2Si/Mg-4Si composite, the modif ication effect of calcium-magnesia phosphate fertilizer on primary Mg_2Si phase in Mg_2Si/Mg-4Si composite was investigated by means of X-ray diffraction(XRD), optical microscopy(OM), scanning electron microscopy(SEM) and energy dispersive spectroscopy(EDS) analysis. The results indicate that the morphology of the primary Mg_2Si phase apparently changes from coarse dendrites to f ine dispersive polygonal particles, and the mean size is decreased from 277 μm to 17 μm. With the addition of 4.0wt.% calcium-magnesia phosphate fertilizer as a modif ier, the ultimate tensile strength and elongation of the Mg_2Si/Mg-4Si composite are increased from 78.7 MPa and 2.1% to 105.2 MPa and 2.6%, as compared to those of the base composite, which is probably attributed to the formation of the phosphorous compound and the cluster of Ca compounds that acted as the heterogeneous nucleation substrates of the primary Mg_2Si particles, resulting in a ref ined distribution of these precipitates.

The evolution of microstructure and mechanical properties during high-speed direct-chill casting in different Al–Mg_2Si in situ composites

The effect of high-speed direct-chill(DC) casting on the microstructure and mechanical properties of Al–Mg_2Si in situ composites and AA6061 alloy was investigated. The microstructural evolution of the Al–Mg_2Si composites and AA6061 alloy was examined by optical microscopy, field-emission scanning electron microscopy(FE-SEM) and transmission electron microscopy(TEM). The results revealed that an increase of the casting speed substantially refined the primary Mg_2Si particles(from 28 to 12 μm), the spacing of eutectic Mg_2Si(from 3 to 0.5 μm), and the grains of AA6061 alloy(from 102 to 22 μm). The morphology of the eutectic Mg_2Si transformed from lamellar to rod-like and fibrous with increasing casting speed. The tensile tests showed that the yield strength, tensile strength, and elongation improved at higher casting speeds because of refinement of the Mg_2Si phase and the grains in the Al–Mg_2Si composites and the AA6061 alloy. High-speed DC casting is demonstrated to be an effective method to improve the mechanical properties of Al–Mg_2Si composites and AA6061 alloy billets.

Microstructure evolution of semi-solid Mg2Si/A356 composites during remelting process

The semi-solid processed Mg2Si/A356 composites were fabricated using a sloping plate,and the phase and morphology evolution of the semi-solid Mg2Si/A356 slurry during the remelting process was investigated.Results indicate that compared to as-cast microstructure,the size of primaryα-Al phase and Mg2Si phase of semi-solid microstructure fabricated by using a sloping plate decreases and the morphology ofα-Al phase becomes fine and globular.With increasing the reheating temperature and prolonging the holding time,the primaryα-Al phase spheroidizes,the liquid fraction in semi-solid microstructure increases,and the Chinese script Mg2Si phase embedded in the primaryα-Al phase cannot be observed.The Chinese script Mg2Si phase is distributed in the secondaryα-Al phase and becomes smaller.The net-shaped eutectic phase also becomes finer after reheating.The optimum remelting parameters suitable for thixoforming in this study are remelting at 580℃for 30 min.