A series of nominal compositions MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)(x=0,0.04,0.08,0.12,0.16,and 0.20)ceramics were successfully prepared via the conventional solid-state reaction route.The phase compositions,micros...A series of nominal compositions MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)(x=0,0.04,0.08,0.12,0.16,and 0.20)ceramics were successfully prepared via the conventional solid-state reaction route.The phase compositions,microstructures,and microwave dielectric properties were investigated.The results of x-ray diffraction(XRD)and scanning electron microscopy(SEM)showed that a single phase of MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)ceramics with a spinel structure was obtained at x≤0.12,whereas the second phase of MgTi_(2)O_(5)appeared when x>0.12.The cell parameters were obtained by XRD refinement.As the x values increased,the unit cell volume kept expanding.This phenomenon could be attributed to the partial substitution of(Li_(1/3)Ti_(2/3))^(3+)for Al^(3+).Results showed that(Li_(1/3)Ti_(2/3))^(3+)doping into MgAl_(2)O_(4)spinel ceramics effectively reduced the sintering temperature and improved the quality factor(Q_f)values.Good microwave dielectric properties were achieved for a sample at x=0.20 sintering at 1500℃in air for 4 h:dielectric constantε_(r)=8.78,temperature coefficient of resonant frequencyτ_(f)=-85 ppm/℃,and Q_(f)=62300 GHz.The Q_(f)value of the x=0.20 sample was about 2 times higher than that of pure MgAl_(2)O_(4)ceramics(31600 GHz).Thus,MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)ceramics with excellent microwave dielectric properties can be applied to 5G communications.展开更多
SiC-MgAl_(2)O_(4) composites with SiAlON polytypoids(12H and 21R)as the bonding phases were prepared using SiC fine powder,MgAl_(2)O_(4)fine powder and Al powder as raw materials.The effects of the firing temperature ...SiC-MgAl_(2)O_(4) composites with SiAlON polytypoids(12H and 21R)as the bonding phases were prepared using SiC fine powder,MgAl_(2)O_(4)fine powder and Al powder as raw materials.The effects of the firing temperature and the mass ratio of SiC to MgAl_(2)O_(4) on the formation of SiAlON polytypoids as well as on the properties of samples were studied.The formation mechanism of SiAlON polytypoids was discussed.The results show that firing at 1650℃in the nitrogen atmosphere,SiC-MgAl_(2)O_(4) composites with SiAlON polytypoids can be obtained.With the gradual increase of the mass ratio of SiC to MgAl_(2)O_(4) in the raw materials,12H forms first,and then coexists with 21H,finally,all 12H converts into 21R in samples.Both phases are plate crystals with flat and smooth edges.Compared with 21R,12H is conducive to improving the density and the cold mechanical properties of materials.After firing at 1650℃in the nitrogen atmosphere,with the mass ratio of SiC to MgAl_(2)O_(4) of 6:4,the sample has the cold modulus of rupture of 27 MPa,showing the optimal performance.展开更多
基金Project(SKL-SPM-202021) supported by the State Key Laboratory of Advanced Technologies for Comprehensive Utilization of Platinum Metals,ChinaProject(2023YFQ0082) supported by Sichuan Science and Technology Program,ChinaProject(EFMD2022005Z) supported by Guangdong Provincial Key Laboratory of Electronic Functional Materials and Devices,China。
基金the Chengdu University of Technology(Grant No.KYQD201907728)。
文摘A series of nominal compositions MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)(x=0,0.04,0.08,0.12,0.16,and 0.20)ceramics were successfully prepared via the conventional solid-state reaction route.The phase compositions,microstructures,and microwave dielectric properties were investigated.The results of x-ray diffraction(XRD)and scanning electron microscopy(SEM)showed that a single phase of MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)ceramics with a spinel structure was obtained at x≤0.12,whereas the second phase of MgTi_(2)O_(5)appeared when x>0.12.The cell parameters were obtained by XRD refinement.As the x values increased,the unit cell volume kept expanding.This phenomenon could be attributed to the partial substitution of(Li_(1/3)Ti_(2/3))^(3+)for Al^(3+).Results showed that(Li_(1/3)Ti_(2/3))^(3+)doping into MgAl_(2)O_(4)spinel ceramics effectively reduced the sintering temperature and improved the quality factor(Q_f)values.Good microwave dielectric properties were achieved for a sample at x=0.20 sintering at 1500℃in air for 4 h:dielectric constantε_(r)=8.78,temperature coefficient of resonant frequencyτ_(f)=-85 ppm/℃,and Q_(f)=62300 GHz.The Q_(f)value of the x=0.20 sample was about 2 times higher than that of pure MgAl_(2)O_(4)ceramics(31600 GHz).Thus,MgAl_(2-x)(Li_(1/3)Ti_(2/3))_(x)O_(4)ceramics with excellent microwave dielectric properties can be applied to 5G communications.
文摘SiC-MgAl_(2)O_(4) composites with SiAlON polytypoids(12H and 21R)as the bonding phases were prepared using SiC fine powder,MgAl_(2)O_(4)fine powder and Al powder as raw materials.The effects of the firing temperature and the mass ratio of SiC to MgAl_(2)O_(4) on the formation of SiAlON polytypoids as well as on the properties of samples were studied.The formation mechanism of SiAlON polytypoids was discussed.The results show that firing at 1650℃in the nitrogen atmosphere,SiC-MgAl_(2)O_(4) composites with SiAlON polytypoids can be obtained.With the gradual increase of the mass ratio of SiC to MgAl_(2)O_(4) in the raw materials,12H forms first,and then coexists with 21H,finally,all 12H converts into 21R in samples.Both phases are plate crystals with flat and smooth edges.Compared with 21R,12H is conducive to improving the density and the cold mechanical properties of materials.After firing at 1650℃in the nitrogen atmosphere,with the mass ratio of SiC to MgAl_(2)O_(4) of 6:4,the sample has the cold modulus of rupture of 27 MPa,showing the optimal performance.
基金National Natural Science Foundation of China(12175254,U1832119)National Key R&D Program of China(2021YFE0104800)+2 种基金International Partnership Program of Chinese Academy of Sciences(121631KYSB20200039)International Cooperation Project of Shanghai Science and Technology Commission(20520750200)National Centre for Research and Development(WPC2/1/SCAPOL/2021)。