To address the issues of reduced performance and shortened lifespan during the low-carbonizating process of Al_(2)O_(3)-C refractories,nano-crystalline ZrC modified graphite was prepared using Zr powder and flake grap...To address the issues of reduced performance and shortened lifespan during the low-carbonizating process of Al_(2)O_(3)-C refractories,nano-crystalline ZrC modified graphite was prepared using Zr powder and flake graphite as raw materials,with NaCl and NaF mixed salt serving as the medium.The flake graphite was gradually replaced by ZrC modified graphite in the preparation of Al_(2)O_(3)-C refractories,and its impact on the material’s structure and properties was investigated.The results indicate that,compared to samples with only flake graphite,the introduction of 1 mass%to 5 mass%nano-crystalline ZrC modified graphite can significantly enhance the mechanical performance of low-carbon Al_(2)O_(3)-C refractories.When 5 mass%ZrC modified graphite is added,the mechanical properties of the samples are optimal,with the cold modulus of rupture and elastic modulus reaching 22.5 MPa and 65.0 GPa,respectively.展开更多
Cr_(2)O_(3)-bearing castables bonded with reactive MgO(RM)or calcium aluminate cement(CAC)were studied to evaluate the binder effect on their performance in corrosive environments.The properties of the as-prepared cas...Cr_(2)O_(3)-bearing castables bonded with reactive MgO(RM)or calcium aluminate cement(CAC)were studied to evaluate the binder effect on their performance in corrosive environments.The properties of the as-prepared castables were compared with respect to the differences in phase composition and microstructure.The corrosion behavior of the as-prepared castables by CaO-Al_(2)O_(3)-Fe_(2)O_(3)-SiO_(2)-based slag was systematically compared viarefractory cup testing at 1600℃with respect to the differences in phase composition and microstructure.The analysis indicates that RM bonded castables show higher apparent porosity,lower bulk density and strengths after drying at 110℃and firing at 1300℃,and higher permanent linear change after firing at 1300℃,but better slag corrosion and infiltration resistance compared with CAC bonded castables.展开更多
文摘To address the issues of reduced performance and shortened lifespan during the low-carbonizating process of Al_(2)O_(3)-C refractories,nano-crystalline ZrC modified graphite was prepared using Zr powder and flake graphite as raw materials,with NaCl and NaF mixed salt serving as the medium.The flake graphite was gradually replaced by ZrC modified graphite in the preparation of Al_(2)O_(3)-C refractories,and its impact on the material’s structure and properties was investigated.The results indicate that,compared to samples with only flake graphite,the introduction of 1 mass%to 5 mass%nano-crystalline ZrC modified graphite can significantly enhance the mechanical performance of low-carbon Al_(2)O_(3)-C refractories.When 5 mass%ZrC modified graphite is added,the mechanical properties of the samples are optimal,with the cold modulus of rupture and elastic modulus reaching 22.5 MPa and 65.0 GPa,respectively.
基金the Joint Founds of R&D Program of Henan Province (222301420034)National Natural Science Foundation of China (51802287)Collaborative Innovation Major Special Project of Zhengzhou (No. 20XTZX12025) for the financial support
文摘Cr_(2)O_(3)-bearing castables bonded with reactive MgO(RM)or calcium aluminate cement(CAC)were studied to evaluate the binder effect on their performance in corrosive environments.The properties of the as-prepared castables were compared with respect to the differences in phase composition and microstructure.The corrosion behavior of the as-prepared castables by CaO-Al_(2)O_(3)-Fe_(2)O_(3)-SiO_(2)-based slag was systematically compared viarefractory cup testing at 1600℃with respect to the differences in phase composition and microstructure.The analysis indicates that RM bonded castables show higher apparent porosity,lower bulk density and strengths after drying at 110℃and firing at 1300℃,and higher permanent linear change after firing at 1300℃,but better slag corrosion and infiltration resistance compared with CAC bonded castables.