In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The...In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The microstructures,XRD patterns,FTIR spectra,UV-Vis-NIR spectra thermo-conductivity,thermo-stability and photothermal effects of these composite films were all characterized.These results indicated that Ti_(2)O_(3) particles were well dispersed throughout the polyvinyl alcohol(PVA)matrix in the PVA/Ti_(2)O_(3) composite films.And Ti_(2)O_(3) particles could also effectively improve the photothermal properties of the composite films which exhibited high light absorption and generated a high temperature(about 57.4℃for film with 15 wt%Ti_(2)O_(3) amount)on the surface when it was irradiated by a simulated sunlight source(1 kW/m^(2)).展开更多
To enhance the protective performance of ceramic composite armor,ballistic penetration experiments were conducted on Al_(2)O_(3) ceramic-ultra-high molecular weight polyethylene(UHMWPE)composite armor with different t...To enhance the protective performance of ceramic composite armor,ballistic penetration experiments were conducted on Al_(2)O_(3) ceramic-ultra-high molecular weight polyethylene(UHMWPE)composite armor with different thickness configurations.The damage and failure modes of hard projectiles and ceramic-fiber composite targets were analyzed.The recovered projectiles and ceramic fragments were sieved and weighed at multiple stages,revealing a positive correlation between the degree of fragmentation of the projectiles and ceramics and the overall ballistic resistance of the composite targets.Numerical simulations were performed using the LS-DYNA finite element software,and the simulation results showed high consistency with the experimental results,confirming the validity of the material parameters.The results indicate that the projectile heads primarily exhibited crushing and abrasive fragmentation.Larger projectile fragments mainly resulted from tensile and shear stress-induced failure.The failure modes of the composite targets included the formation of ceramic cones and radial cracks under high-velocity impacts.The UHMWPE laminated plates exhibited interlayer separation caused by tensile waves,permanent plastic deformation of the rear surface bulging,and perforation failure primarily due to shear forces.Through extended numerical simulations,while maintaining the same areal density and configuration of9 mm Al_(2)O_(3) ceramic+12 mm UHMWPE laminated composite armor,the thickness configurations of the Al_(2)O_(3) ceramic and UHMWPE laminated backplates were varied,and various thicknesses of UHMWPE laminates were simulated as the cover layer for the ceramic panels.The simulation results indicated that the composite armor configuration of 10 mm Al_(2)O_(3) ceramic+8 mm UHMWPE composite armor increased energy absorption by13.48%.When altering the cover layer thickness,a 4 mm UHMWPE+9 mm Al_(2)O_(3)+8 mm UHMWPE composite armor demonstrated a 27.11%improvement in energy absorption,showing a relatively significant enhancement.展开更多
The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increa...The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increases the hardness values of the matrix at both room and high temperature and improves the wear resistance of the material.The hardness values and the wear resistance of the composite rise with the increase of the particle volume fraction or the decrease of the particle size.The raising of test temperature results in a rapid descending of its hardness values.However, the addition of Al2O3P improves the property of high temperature resistance of Zn-Al alloys significantly.Moreover,the effect of quenching, tempering or cycling heat treatment on the hardness values of the composite is also studied.展开更多
A heat-resistant dispersion-strengthening nano-Al_2O_3/Cu composite with highstrength and high electric conductivity was fabricated in a multiplex medium. The internaloxidation product, microstructures and properties ...A heat-resistant dispersion-strengthening nano-Al_2O_3/Cu composite with highstrength and high electric conductivity was fabricated in a multiplex medium. The internaloxidation product, microstructures and properties of the composite, and the process flow weresystematically studied. It is confirmed that this new technique simplifies the process and improvesthe properties of the composite. X-ray analysis indicates that the alumina particles formed duringinternal oxidation consist of a large mount of gamma-Al_2O_3 and a certain amount of theta-Al_2O_3and alpha-Al_2O_3. TEM observation shows that the obtained gamma-Al_2O_3 nano-particles areuniformly distributed in the copper grains; their mean size and space between particles are 7 runand 30 nm, respectively. The main properties of the composite with 50 percent cold deformation areas follows: the electric conductivity is 51 MS/m (87 percent IACS), sigma_b = 628 MPa, and thehardness is HRB86. After annealing at 1273 K, all or most of the above properties remain, and themicrostructures are still dependent on elongated fiber-form grains.展开更多
The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel...The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel 45 was used as a reference material. Experimentalresults showed that the abrasive wear resistance of Al_2O_3/PA1010 composite coatings has a goodlinear relationship with the volume fraction of Al_2O_3 particles in Al_2O_3/PA1010 compositecoatings, and the linear correlative coefficient is 0.979. Under the experimental conditions, thesize of Al_2O_3 particles (40.5-161.0 μm) has little influence on the abrasive wear resistance ofAl_2O_3/PA1010 composite coatings. By treating the surface of Al_2O_3 particles with a suitablebonding agent, the distribution of Al_2O_3 particles in matrix PA1010 is more homogeneous and thebonding state between Al_2O_3 particles and matrix PA1010 is better. Therefore, the Al_2O_3particles in Al_2O_3/PA1010 composite coatings make the Al_2O_3/PA1010 composite coatings havebetter abrasive wear resistance than PA1010 coatings. The wear resistance of Al_2O_3/PA1010composite coatings is about 45% compared with that of steel 45.展开更多
The present study confers to the fabrication and its characterization of magnesium alloy(AZ91E)based nano composites with nano Al_(2)O_(3) particulate reinforcements.A novel Semi Solid stir casting technique was adopt...The present study confers to the fabrication and its characterization of magnesium alloy(AZ91E)based nano composites with nano Al_(2)O_(3) particulate reinforcements.A novel Semi Solid stir casting technique was adopted for the fabrication of the composite.An average particle size of 50 nm was used as reinforcement to disperse in matrix.The effects of change in weight fraction of reinforcements on the distribution of particles,particle–matrix interfacial reactions,physical as well as mechanical properties were reported.The SEM and EDS analysis has shown the uniform distribution of particles in the composite along with the presence of elements.The mechanical properties of reinforced and unreinforced composite were evaluated and presented.Fractography of tensile specimens was also discussed.展开更多
Nano-AlN and submicron-Al_(2)O_(3) particles were simultaneously utilized in a 6061 Al matrix composite to improve the high-temperature strength.According to the SEM and TEM characterization,nano-AlN and submicron-Al_...Nano-AlN and submicron-Al_(2)O_(3) particles were simultaneously utilized in a 6061 Al matrix composite to improve the high-temperature strength.According to the SEM and TEM characterization,nano-AlN and submicron-Al_(2)O_(3) particles are uniformly distributed in the Al matrix.Brinell hardness results indicate that different from the traditional 6061 Al matrix alloy,the aging kinetics of the composite is obviously accelerated by the reinforcement particles.The T6-treated composite exhibits excellent tensile properties at both room temperature and elevated temperature.Especially at 350℃,the T6-treated composite not only has a high yield strength of 121 MPa and ultimate tensile strength of 128 MPa,but also exhibits a large elongation of 11.6%.Different strengthening mechanisms of nano-AlN and submicron-Al_(2)O_(3) particles were also discussed in detail.展开更多
Based on the γ-Al2O3 support with large-size pores, impregnation-deposition method was adopted to prepare the nano CeO_2/γ-Al2O3 composite supports. The results of XRD showed that there was no CeO_2-Al2O3 mixture or...Based on the γ-Al2O3 support with large-size pores, impregnation-deposition method was adopted to prepare the nano CeO_2/γ-Al2O3 composite supports. The results of XRD showed that there was no CeO_2-Al2O3 mixture or solid solution, indicating that CeO_2 was only loaded on the surface of Al2O3. The CeO_2/γ-Al2O3 composite support had larger specific surface area (170 m2·g-1), while for the non-loaded nanosized CeO_2, the specific surface area was small(～50 m2·g-1). The influence of impregnation and drying methods on the surface properties, thermal stability and crystal structure of composite supports was characterized by XRD, DTA and BET. The CeO_2/γ-Al2O3 composite support prepared by vacuum impregnation and microwave drying was better than that prepared by conventional impregnation and drying.展开更多
Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxida...Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxidation test was performed at 1050℃ for 5, 50, 100,150, 200, and 400 h. The microstructure and phase composition of powders and coatings were characterized by scanning electron microscopy and X-ray diffraction, respectively. The bonding strength of the coatings was also evaluated. The results proved that with the increase in the percentage of nanoparticles(from 2wt% to 6wt%), the amount of porosity(from 1vol% to 4.7vol%), unmelted particles, and roughness of the coatings(from 4.8 to 8.8 μm) increased, and the bonding strength decreased from 71 to 48 MPa. The thicknesses of the thermally grown oxide layer of pure and composite coatings(2wt%, 4wt%, and 6wt%) after 400 h oxidation were measured as 6.5, 5.5, 7.6, and 8.1 μm, respectively.The CoNiCrAlY–2wt% Al_(2)O_(3)coating showed the highest oxidation resistance due to the diffusion barrier effect of well-dispersed nanoparticles. The CoNiCrAlY–6wt% Al_(2)O_(3)coating had the lowest oxidation resistance due to its rough surface morphology and porous microstructure.展开更多
Al_(2)O_(3)–SiO_(2)sols were synthesized by using aluminum chloride hex hydrate and tetraethoxysilane(TEOS)as precursors,deionized water and ethanol mixture as the solvent,and propylene oxide as the coagulant aids.Al...Al_(2)O_(3)–SiO_(2)sols were synthesized by using aluminum chloride hex hydrate and tetraethoxysilane(TEOS)as precursors,deionized water and ethanol mixture as the solvent,and propylene oxide as the coagulant aids.Alumina coatings were prepared on the surfaces of hollow quartz filament fiber,then a new lightweight and thermal insulating material were successfully prepared by impregnatingAl_(2)O_(3)–SiO_(2)sol into a needle fabric made by coated hollow quartz filament fiber.The coated quartz fiber,aerogels and composites were characterized by Fourier transform infrared spectroscopy(FTIR),X-ray diffraction(XRD),energy dispersive spectroscopy(EDS),nitrogen adsorption-desorption(BET),scanning electron microscopy(SEM),transmission electron microscopy(TEM),and tensile tests.The effects of different fiber and calcination temperatures on the microstructures and properties ofAl_(2)O_(3)–SiO_(2)composite aerogels were investigated.The test results indicate that the mechanical properties of the aerogels are improved by introducing quartz filament fabrics and the introduction of alumina coating improves the thermal stability of the material.Compared to other fibers,Al_(2)O_(3)-coated hollow quartz fiber has significant advantages as reinforcement for composite,and their tensile strength is well retained after high temperature heat treatment.展开更多
Al_(2)O_(3)/SiC composite ceramics were prepared fromα-Al_(2)O_(3) and SiC by a pressureless sinter method in this study.The effect of SiC contents on the mechanic properties,phase compositions and microstructure is ...Al_(2)O_(3)/SiC composite ceramics were prepared fromα-Al_(2)O_(3) and SiC by a pressureless sinter method in this study.The effect of SiC contents on the mechanic properties,phase compositions and microstructure is studied.Experimental results show that the vickers hardness,wear resistance and thermal conductivity of the samples increase with the increase in the SiC content,and the hardness of the sample reaches 16.22 GPa,and thermal conductivity of the sample reaches 25.41 W/(m.K)at room temperature when the SiC content is 20 wt%(B5)and the sintering temperature is at 1640℃.Higher hardness means higher scour resistance,and it indicates that the B5 material is expected to be used for the solar heat absorber of third generation solar thermal generation.The results indicate the mechanism of improving mechanical properties of Al_(2)O_(3)/SiC composite ceramics:SiC plays a role in grain refinement that the grain of SiC inhibits the grain growth of Al_(2)O_(3),while the addition of SiC changes the fracture mode from the intergranular to the intergranular-transgranular.展开更多
The composites were prepared by ball-milling ZrO_2(3%Y_2O_3) and γ-Al_2O_3 nanoparticles, pressing unidirectionally, cold-pressing isostatically and pressurelessly sintering in air. The phases of ZrO_2 in composites ...The composites were prepared by ball-milling ZrO_2(3%Y_2O_3) and γ-Al_2O_3 nanoparticles, pressing unidirectionally, cold-pressing isostatically and pressurelessly sintering in air. The phases of ZrO_2 in composites were examined by X-ray diffraction. The microstructure of Al_2O_3/3Y-TZP composites was observed by scanning electron microscope (SEM) and transmission electron microscopy (TEM) respectively. The X-ray analysis reveals that ZrO_2 of both surface and fracture surface is mainly t-ZrO_2. The SEM image shows that there are some intragranular particles in large granulars. The fracture toughness K_ 1c of Al_2O_3/70%ZrO_2(3%Y_2O_3(mole fraction)) composite tested by single-edge notched bending is 13.5 MPa·m 1/2. Being toughened by the ferroelastic domain switching and the intragranular microstructure explains high toughness of the composite.展开更多
The composition, microstructures and properties of SiC /Al-2O-3/Al-Si composites formed by reactive penetration of the molten aluminum into the preforms of SiO-2 and SiC were investigated. The composition of the compo...The composition, microstructures and properties of SiC /Al-2O-3/Al-Si composites formed by reactive penetration of the molten aluminum into the preforms of SiO-2 and SiC were investigated. The composition of the composites was measured by X-ray diffraction (XRD). The microstructures of the composites were also measured by scanning electron microscopy (SEM) and optical microscopy. In addition, the factors affecting the properties of the composites were discussed.The experiments show that the mechanical properties of the composites depend on their relative densities and the sizes of the fillers“SiC grains".The denser the SiC/Al-2O-3/Al-Si composites,the higher their bending strength.As the filler “SiC grains" become fine,the bending strength of the composites increases.展开更多
Alumina/aluminum-silicon alloy composite is manufactured by squeeze casting. The effect of the reinforcementon the morphology of the silicon phase in aluminum-silicon alloy is studied. The results indicate that an alu...Alumina/aluminum-silicon alloy composite is manufactured by squeeze casting. The effect of the reinforcementon the morphology of the silicon phase in aluminum-silicon alloy is studied. The results indicate that an alumina fiber canserve as propitious sites for the heterogeneous nucleation of the silicon phase, and the primary silicon in the compositecan nucleate on the surface of the fiber. The fiber in the composite can trigger twin during the coupled growth of thealuminum-silicon eutectic and lead to modification of the eutectic silicon near the fiber.展开更多
The mechanical properties and microstructures of Al_(2)O_(3)whiskers and graphene nano-platelets(GNPs)co-reinforced Cu-matrix composites were studied.Cu-matrix composites with a variation of GNPs amount were fabricate...The mechanical properties and microstructures of Al_(2)O_(3)whiskers and graphene nano-platelets(GNPs)co-reinforced Cu-matrix composites were studied.Cu-matrix composites with a variation of GNPs amount were fabricated by mechanical alloying followed by vacuum hot-pressing sintering and hot isostatic pressing.The Cu-matrix composite with 0.5 wt.%GNPs(GNPs-0.5)suggests a good interfacial bonding of both Cu/C and Cu/Al_(2)O_(3)interfaces.Both the hardness and compressive strength of Cu-matrix composites show a consistent tendency that firstly increases to a critical value and then decreases with increasing GNPs amount.It is suggested that the most possible strengthening mechanisms of both GNPs and Al_(2)O_(3)whisker working in the Cu-matrix composites involve energy dissipating and load transfer,as well as grain refinements for GNPs.The synergetic effect of GNPs and Al_(2)O_(3)whiskers is highlighted that the embedded GNPs would hinder the crack path generated at the Al_(2)O_(3)/Cu interface and enhance the already outstanding strengthening effect that Al_(2)O_(3)whiskers provide.展开更多
基金Funded by the Youth Backbone Teacher Training Plan in University of Henan Province(No.21220028)Science and Technology Research Project of Henan Province(No.242102321066)+2 种基金Natural Science Foundation of Henan Province(No.232300420312)Henan University of Technology Young Backbone Teacher Training Plan(No.21421260)the Innovation Training Program for College Students in Henan Province(No.202310463046)。
文摘In this work,flexible photothermal PVA/Ti_(2)O_(3) composite films with different amount(0 wt%,5 wt%,10 wt%,15 wt%)of Ti_(2)O_(3) particles modified by steric acid were prepared by a simple solution casting method.The microstructures,XRD patterns,FTIR spectra,UV-Vis-NIR spectra thermo-conductivity,thermo-stability and photothermal effects of these composite films were all characterized.These results indicated that Ti_(2)O_(3) particles were well dispersed throughout the polyvinyl alcohol(PVA)matrix in the PVA/Ti_(2)O_(3) composite films.And Ti_(2)O_(3) particles could also effectively improve the photothermal properties of the composite films which exhibited high light absorption and generated a high temperature(about 57.4℃for film with 15 wt%Ti_(2)O_(3) amount)on the surface when it was irradiated by a simulated sunlight source(1 kW/m^(2)).
基金supported by the National Natural Science Foundation of China(Grant Nos.12172179,U2341244,and 11772160)。
文摘To enhance the protective performance of ceramic composite armor,ballistic penetration experiments were conducted on Al_(2)O_(3) ceramic-ultra-high molecular weight polyethylene(UHMWPE)composite armor with different thickness configurations.The damage and failure modes of hard projectiles and ceramic-fiber composite targets were analyzed.The recovered projectiles and ceramic fragments were sieved and weighed at multiple stages,revealing a positive correlation between the degree of fragmentation of the projectiles and ceramics and the overall ballistic resistance of the composite targets.Numerical simulations were performed using the LS-DYNA finite element software,and the simulation results showed high consistency with the experimental results,confirming the validity of the material parameters.The results indicate that the projectile heads primarily exhibited crushing and abrasive fragmentation.Larger projectile fragments mainly resulted from tensile and shear stress-induced failure.The failure modes of the composite targets included the formation of ceramic cones and radial cracks under high-velocity impacts.The UHMWPE laminated plates exhibited interlayer separation caused by tensile waves,permanent plastic deformation of the rear surface bulging,and perforation failure primarily due to shear forces.Through extended numerical simulations,while maintaining the same areal density and configuration of9 mm Al_(2)O_(3) ceramic+12 mm UHMWPE laminated composite armor,the thickness configurations of the Al_(2)O_(3) ceramic and UHMWPE laminated backplates were varied,and various thicknesses of UHMWPE laminates were simulated as the cover layer for the ceramic panels.The simulation results indicated that the composite armor configuration of 10 mm Al_(2)O_(3) ceramic+8 mm UHMWPE composite armor increased energy absorption by13.48%.When altering the cover layer thickness,a 4 mm UHMWPE+9 mm Al_(2)O_(3)+8 mm UHMWPE composite armor demonstrated a 27.11%improvement in energy absorption,showing a relatively significant enhancement.
文摘The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increases the hardness values of the matrix at both room and high temperature and improves the wear resistance of the material.The hardness values and the wear resistance of the composite rise with the increase of the particle volume fraction or the decrease of the particle size.The raising of test temperature results in a rapid descending of its hardness values.However, the addition of Al2O3P improves the property of high temperature resistance of Zn-Al alloys significantly.Moreover,the effect of quenching, tempering or cycling heat treatment on the hardness values of the composite is also studied.
文摘A heat-resistant dispersion-strengthening nano-Al_2O_3/Cu composite with highstrength and high electric conductivity was fabricated in a multiplex medium. The internaloxidation product, microstructures and properties of the composite, and the process flow weresystematically studied. It is confirmed that this new technique simplifies the process and improvesthe properties of the composite. X-ray analysis indicates that the alumina particles formed duringinternal oxidation consist of a large mount of gamma-Al_2O_3 and a certain amount of theta-Al_2O_3and alpha-Al_2O_3. TEM observation shows that the obtained gamma-Al_2O_3 nano-particles areuniformly distributed in the copper grains; their mean size and space between particles are 7 runand 30 nm, respectively. The main properties of the composite with 50 percent cold deformation areas follows: the electric conductivity is 51 MS/m (87 percent IACS), sigma_b = 628 MPa, and thehardness is HRB86. After annealing at 1273 K, all or most of the above properties remain, and themicrostructures are still dependent on elongated fiber-form grains.
文摘The abrasive wear characteristics of Al_2O_3/PA1010 composite coatings on thesurface of quenched and low-temperature temper steel 45 were tested on the template abrasive weartesting machine and the same uncoated steel 45 was used as a reference material. Experimentalresults showed that the abrasive wear resistance of Al_2O_3/PA1010 composite coatings has a goodlinear relationship with the volume fraction of Al_2O_3 particles in Al_2O_3/PA1010 compositecoatings, and the linear correlative coefficient is 0.979. Under the experimental conditions, thesize of Al_2O_3 particles (40.5-161.0 μm) has little influence on the abrasive wear resistance ofAl_2O_3/PA1010 composite coatings. By treating the surface of Al_2O_3 particles with a suitablebonding agent, the distribution of Al_2O_3 particles in matrix PA1010 is more homogeneous and thebonding state between Al_2O_3 particles and matrix PA1010 is better. Therefore, the Al_2O_3particles in Al_2O_3/PA1010 composite coatings make the Al_2O_3/PA1010 composite coatings havebetter abrasive wear resistance than PA1010 coatings. The wear resistance of Al_2O_3/PA1010composite coatings is about 45% compared with that of steel 45.
文摘The present study confers to the fabrication and its characterization of magnesium alloy(AZ91E)based nano composites with nano Al_(2)O_(3) particulate reinforcements.A novel Semi Solid stir casting technique was adopted for the fabrication of the composite.An average particle size of 50 nm was used as reinforcement to disperse in matrix.The effects of change in weight fraction of reinforcements on the distribution of particles,particle–matrix interfacial reactions,physical as well as mechanical properties were reported.The SEM and EDS analysis has shown the uniform distribution of particles in the composite along with the presence of elements.The mechanical properties of reinforced and unreinforced composite were evaluated and presented.Fractography of tensile specimens was also discussed.
基金supported by the Key Program of National Natural Science Foundation of China(No.51731007)the National Natural Science Foundation of China(No.52071179)the Fundamental Research Funds for the Central Universities(No.30920021160).
文摘Nano-AlN and submicron-Al_(2)O_(3) particles were simultaneously utilized in a 6061 Al matrix composite to improve the high-temperature strength.According to the SEM and TEM characterization,nano-AlN and submicron-Al_(2)O_(3) particles are uniformly distributed in the Al matrix.Brinell hardness results indicate that different from the traditional 6061 Al matrix alloy,the aging kinetics of the composite is obviously accelerated by the reinforcement particles.The T6-treated composite exhibits excellent tensile properties at both room temperature and elevated temperature.Especially at 350℃,the T6-treated composite not only has a high yield strength of 121 MPa and ultimate tensile strength of 128 MPa,but also exhibits a large elongation of 11.6%.Different strengthening mechanisms of nano-AlN and submicron-Al_(2)O_(3) particles were also discussed in detail.
文摘Based on the γ-Al2O3 support with large-size pores, impregnation-deposition method was adopted to prepare the nano CeO_2/γ-Al2O3 composite supports. The results of XRD showed that there was no CeO_2-Al2O3 mixture or solid solution, indicating that CeO_2 was only loaded on the surface of Al2O3. The CeO_2/γ-Al2O3 composite support had larger specific surface area (170 m2·g-1), while for the non-loaded nanosized CeO_2, the specific surface area was small(～50 m2·g-1). The influence of impregnation and drying methods on the surface properties, thermal stability and crystal structure of composite supports was characterized by XRD, DTA and BET. The CeO_2/γ-Al2O3 composite support prepared by vacuum impregnation and microwave drying was better than that prepared by conventional impregnation and drying.
文摘Satellited CoNiCrAlY–Al_(2)O_(3)feedstocks with 2wt%, 4wt%, and 6wt% oxide nanoparticles and pure CoNiCrAlY powder were deposited by the high-velocity oxy fuel process on an Inconel738 superalloy substrate. The oxidation test was performed at 1050℃ for 5, 50, 100,150, 200, and 400 h. The microstructure and phase composition of powders and coatings were characterized by scanning electron microscopy and X-ray diffraction, respectively. The bonding strength of the coatings was also evaluated. The results proved that with the increase in the percentage of nanoparticles(from 2wt% to 6wt%), the amount of porosity(from 1vol% to 4.7vol%), unmelted particles, and roughness of the coatings(from 4.8 to 8.8 μm) increased, and the bonding strength decreased from 71 to 48 MPa. The thicknesses of the thermally grown oxide layer of pure and composite coatings(2wt%, 4wt%, and 6wt%) after 400 h oxidation were measured as 6.5, 5.5, 7.6, and 8.1 μm, respectively.The CoNiCrAlY–2wt% Al_(2)O_(3)coating showed the highest oxidation resistance due to the diffusion barrier effect of well-dispersed nanoparticles. The CoNiCrAlY–6wt% Al_(2)O_(3)coating had the lowest oxidation resistance due to its rough surface morphology and porous microstructure.
文摘Al_(2)O_(3)–SiO_(2)sols were synthesized by using aluminum chloride hex hydrate and tetraethoxysilane(TEOS)as precursors,deionized water and ethanol mixture as the solvent,and propylene oxide as the coagulant aids.Alumina coatings were prepared on the surfaces of hollow quartz filament fiber,then a new lightweight and thermal insulating material were successfully prepared by impregnatingAl_(2)O_(3)–SiO_(2)sol into a needle fabric made by coated hollow quartz filament fiber.The coated quartz fiber,aerogels and composites were characterized by Fourier transform infrared spectroscopy(FTIR),X-ray diffraction(XRD),energy dispersive spectroscopy(EDS),nitrogen adsorption-desorption(BET),scanning electron microscopy(SEM),transmission electron microscopy(TEM),and tensile tests.The effects of different fiber and calcination temperatures on the microstructures and properties ofAl_(2)O_(3)–SiO_(2)composite aerogels were investigated.The test results indicate that the mechanical properties of the aerogels are improved by introducing quartz filament fabrics and the introduction of alumina coating improves the thermal stability of the material.Compared to other fibers,Al_(2)O_(3)-coated hollow quartz fiber has significant advantages as reinforcement for composite,and their tensile strength is well retained after high temperature heat treatment.
基金Funded by the National Key Technology Research and Development Program of the Ministry of Science and Technology of China(No.2018YFB1501002)。
文摘Al_(2)O_(3)/SiC composite ceramics were prepared fromα-Al_(2)O_(3) and SiC by a pressureless sinter method in this study.The effect of SiC contents on the mechanic properties,phase compositions and microstructure is studied.Experimental results show that the vickers hardness,wear resistance and thermal conductivity of the samples increase with the increase in the SiC content,and the hardness of the sample reaches 16.22 GPa,and thermal conductivity of the sample reaches 25.41 W/(m.K)at room temperature when the SiC content is 20 wt%(B5)and the sintering temperature is at 1640℃.Higher hardness means higher scour resistance,and it indicates that the B5 material is expected to be used for the solar heat absorber of third generation solar thermal generation.The results indicate the mechanism of improving mechanical properties of Al_(2)O_(3)/SiC composite ceramics:SiC plays a role in grain refinement that the grain of SiC inhibits the grain growth of Al_(2)O_(3),while the addition of SiC changes the fracture mode from the intergranular to the intergranular-transgranular.
文摘The composites were prepared by ball-milling ZrO_2(3%Y_2O_3) and γ-Al_2O_3 nanoparticles, pressing unidirectionally, cold-pressing isostatically and pressurelessly sintering in air. The phases of ZrO_2 in composites were examined by X-ray diffraction. The microstructure of Al_2O_3/3Y-TZP composites was observed by scanning electron microscope (SEM) and transmission electron microscopy (TEM) respectively. The X-ray analysis reveals that ZrO_2 of both surface and fracture surface is mainly t-ZrO_2. The SEM image shows that there are some intragranular particles in large granulars. The fracture toughness K_ 1c of Al_2O_3/70%ZrO_2(3%Y_2O_3(mole fraction)) composite tested by single-edge notched bending is 13.5 MPa·m 1/2. Being toughened by the ferroelastic domain switching and the intragranular microstructure explains high toughness of the composite.
文摘The composition, microstructures and properties of SiC /Al-2O-3/Al-Si composites formed by reactive penetration of the molten aluminum into the preforms of SiO-2 and SiC were investigated. The composition of the composites was measured by X-ray diffraction (XRD). The microstructures of the composites were also measured by scanning electron microscopy (SEM) and optical microscopy. In addition, the factors affecting the properties of the composites were discussed.The experiments show that the mechanical properties of the composites depend on their relative densities and the sizes of the fillers“SiC grains".The denser the SiC/Al-2O-3/Al-Si composites,the higher their bending strength.As the filler “SiC grains" become fine,the bending strength of the composites increases.
文摘Alumina/aluminum-silicon alloy composite is manufactured by squeeze casting. The effect of the reinforcementon the morphology of the silicon phase in aluminum-silicon alloy is studied. The results indicate that an alumina fiber canserve as propitious sites for the heterogeneous nucleation of the silicon phase, and the primary silicon in the compositecan nucleate on the surface of the fiber. The fiber in the composite can trigger twin during the coupled growth of thealuminum-silicon eutectic and lead to modification of the eutectic silicon near the fiber.
基金the financial supports from the National Natural Science Foundation of China (No. 52101183)China Postdoctoral Science Foundation (Nos. 2017M623054, 2018T110993)
文摘The mechanical properties and microstructures of Al_(2)O_(3)whiskers and graphene nano-platelets(GNPs)co-reinforced Cu-matrix composites were studied.Cu-matrix composites with a variation of GNPs amount were fabricated by mechanical alloying followed by vacuum hot-pressing sintering and hot isostatic pressing.The Cu-matrix composite with 0.5 wt.%GNPs(GNPs-0.5)suggests a good interfacial bonding of both Cu/C and Cu/Al_(2)O_(3)interfaces.Both the hardness and compressive strength of Cu-matrix composites show a consistent tendency that firstly increases to a critical value and then decreases with increasing GNPs amount.It is suggested that the most possible strengthening mechanisms of both GNPs and Al_(2)O_(3)whisker working in the Cu-matrix composites involve energy dissipating and load transfer,as well as grain refinements for GNPs.The synergetic effect of GNPs and Al_(2)O_(3)whiskers is highlighted that the embedded GNPs would hinder the crack path generated at the Al_(2)O_(3)/Cu interface and enhance the already outstanding strengthening effect that Al_(2)O_(3)whiskers provide.