The melting temperature and critical transition temperature Tc of YBa2Cu3O7-δ with deferent content additives of PbO and BaPbO3 were studied. When PbO was doped in YBa2Cu3O7-δ, the melting temperature of YBa2Cu3O7-...The melting temperature and critical transition temperature Tc of YBa2Cu3O7-δ with deferent content additives of PbO and BaPbO3 were studied. When PbO was doped in YBa2Cu3O7-δ, the melting temperature of YBa2Cu3O7-δ was reduced, however its superconductivity was weakened. From the XRD pattern of the sintered mixture of YBa2Cu3O7-δ and PbO, it was known that there was a reaction between YBa2Cu3O7-δ and PbO, and the product was BaPbO3. Hence different contents of BaPbO3 (10mass%, 20mass% and 30mass%) were added in YBa2Cu3O7-δ. It was proved that there were no reactions between YBa2Cu3O7-δ and BaPbO3. And the superconductivity of the mixtures was much better than that of the samples with PbO additive.展开更多
ZrO2, TiO2 and P2O5 were doped in CaO-B2O3-SiO2 glass-ceramics as nucleating additives. Effects of different nucleating additives on the phase separation and crystalline behaviors were investigated by using gradient t...ZrO2, TiO2 and P2O5 were doped in CaO-B2O3-SiO2 glass-ceramics as nucleating additives. Effects of different nucleating additives on the phase separation and crystalline behaviors were investigated by using gradient temperature furnace, DTA and XRD. Then, sintering process of the glass-ceramics was investigated by testing sintering shrinkage, dielectric constant and loss. The experimental results shows that the glass-ceramics doped with nucleating additives represents higher crystallization, with ZrO2 as an exceptional effective dopant to promote the precipitation of wollastonite crystal. Finally, ZrO2 containing glass-ceramics was chosen to study the influence of sintering temperature and soaking time with the help of X-ray diffraction analysis and density measurement. The glass-ceramics can be well consolidated at 850 ℃ for 10 min, with low dielectric constant （5.87） and loss （3.21×10^-4）, which is desirable for LTCC application.展开更多
To improve the mechanical properties of WC-Al2O3 composites, the effects of trace amount of CeO2 additives on the microstructure and mechanical properties of the WC-Al2O3 composites prepared by hot pressing were inves...To improve the mechanical properties of WC-Al2O3 composites, the effects of trace amount of CeO2 additives on the microstructure and mechanical properties of the WC-Al2O3 composites prepared by hot pressing were investigated. The results revealed that the WC-Al2O3 composites doped with 0.1% CeOz possessed refined microstructure and enhanced mechanical properties compared with that of the undoped WC-Al2O3composites. Trace CeO2 suppressed the decarburization of WC, promoted the microstructural refinement, and improved the interface coherence of the WC matrix and Al2O3. When 0.1% CeO2 was added to the WC-Al2O3 composites, the effect of CeO2 resulted in the achievement of a relative density of 98.82% with an excellent Vickers hardness of 16.89 GPa, combining a fracture toughness of 9.85 MPa. m1/2 with an acceptable flexural strength of 1 024.05 MPa.展开更多
Michael addition of nitroalkanes to α,β-unsaturated carbonyl compounds occurs in the presence of KF/AI_2O_3/PEG4000 without solvent.Yields are fair to good and work-ups are easy.
The β-aminocarboxylic acid derivatives were synthesized by Michael addition reaction of alkyl amine and α,β-unsaturated carbonyl compounds in the presence of potassium fluoride on alumina.
Photodegradation has emerged as an environmentally friendly method of decomposing harmful dyes in wastewater. In this study, core-shell Fe3O4/SiO2/ TiO2 nanospheres with magnetic cores were obtained from synthesised m...Photodegradation has emerged as an environmentally friendly method of decomposing harmful dyes in wastewater. In this study, core-shell Fe3O4/SiO2/ TiO2 nanospheres with magnetic cores were obtained from synthesised magnetic Fe3O4 nanoparticles through the precipitation method, the surface of the magnetic Fe3O4 nanoparticles was coated with a silica (SiO2) layer by hydrolysis of tetramethoxysilane (TMOS) as a silica source, and finally, Fe3O4/SiO2 nanospheres were coated with titanium (TiO2) layer using tetrabutyltitanate (TBT) as a precursor through the sol-gel process. The morphology and structure of the prepared materials were characterised by X-ray diffraction (XRD) analysis, scanning electron microscopy (SEM), X-ray energy dispersive spectrometry (EDAX), Fourier transform infrared spectroscopy (FT-IR), and atomic force microscopy (AFM). The photocatalytic activities of the prepared core-shell nanospheres were studied using binary azo dyes, namely methyl orange (anionic dye, MO) and methylene blue (cationic dye, MB) in aqueous solution under UV light irradiation (365 nm), and UV-Vis spectrophotometer was utilised to monitor the amount of each dye in the mixture. It was found that 90.2% and 100% of binary MO and MB were removed for 5 h, respectively. The results revealed that the efficiency of the photocatalytic degradation of the core-shell nanospheres was not degreased after five runs that can be used as recyclable photocatalysts. The results show that the performance of the prepared core-shell nanospheres was better than that of commercial TiO2 nanoparticles. Moreover, the magnetic separation properties of the core-shell Fe3O4/SiO2/TiO2 nanospheres can enable the prepared materials to have wider application prospects.展开更多
In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and micro...In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and microstructures of the sintered composites were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). The process of synthesis was investigated using differential thermal analysis (DTA). The effects of processing parameters and additives on the microstructures of the composites and the development of whisker were examined. It is found that the morphology of the whisker is strongly influenced by the additives, the exothermal reaction process, and the processing parameters.展开更多
Nickel-alumina catalysts supported on cordierite monoliths of honeycomb structure surpass essentially the conventional granulated ones with respect to the output in carbon dioxide reforming of methane. Adjusting the s...Nickel-alumina catalysts supported on cordierite monoliths of honeycomb structure surpass essentially the conventional granulated ones with respect to the output in carbon dioxide reforming of methane. Adjusting the surface acid-base properties of catalysts by introduction of alkali metal （Na, K） oxides inhibits the carbonization and as a result, improves the operational stability of these catalysts. An effect of promotion of nickel-alumina based composite doped by lanthanum oxide is found. This effect, caused by an additional route for the CO2 activation on Ni-La2O3/Al2O3/cordierite catalyst, is displayed in increase of methane conversion under conditions of an oxidant excess.展开更多
Based on thelow temperaturecombustion synthesisof α Al2 O3 from aluminum nitrate,the effectsofthe additives on the formation and particle properties of α Al2 O3 werestudied by XRDand SEM,theinitialstudy on the manom...Based on thelow temperaturecombustion synthesisof α Al2 O3 from aluminum nitrate,the effectsofthe additives on the formation and particle properties of α Al2 O3 werestudied by XRDand SEM,theinitialstudy on the manometer α Al2 O3 synthesisby LCSwas done, α Al2 O3 withtheparticlesize50 ～80 NM wasgot under properconditions.展开更多
The effects of CuO and H3BO3 additions on the low-temperature sintering,microstructure,and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics were investigated.The addition of less amount of CuO （ 〈1 wt%） con...The effects of CuO and H3BO3 additions on the low-temperature sintering,microstructure,and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics were investigated.The addition of less amount of CuO （ 〈1 wt%） considerably facilitated the densification of Ba2Ti3Nb4O18 ceramics.Appropriate addition of H3BO3 （ 〈3.5 wt%） remarkably improved the microwave dielectric properties of ceramics.The addition of H3BO3 and CuO successfully reduced the sintering temperature of Ba2Ti3Nb4O18 ceramics from 1300 to 1050 ℃.Ba2Ti3Nb4O18 ceramics sintered at 1 050 ℃ for 4 h with the addition of 1.0 wt% CuO and 3.5 wt% H3BO3 exhibited good microwave dielectric properties：er=33.74,Q？f=13 812 GHz,and tf=-5.35 ppm/°C at about 5.0 GHz.展开更多
文摘The melting temperature and critical transition temperature Tc of YBa2Cu3O7-δ with deferent content additives of PbO and BaPbO3 were studied. When PbO was doped in YBa2Cu3O7-δ, the melting temperature of YBa2Cu3O7-δ was reduced, however its superconductivity was weakened. From the XRD pattern of the sintered mixture of YBa2Cu3O7-δ and PbO, it was known that there was a reaction between YBa2Cu3O7-δ and PbO, and the product was BaPbO3. Hence different contents of BaPbO3 (10mass%, 20mass% and 30mass%) were added in YBa2Cu3O7-δ. It was proved that there were no reactions between YBa2Cu3O7-δ and BaPbO3. And the superconductivity of the mixtures was much better than that of the samples with PbO additive.
基金Funded by the Shanghai Leading Academic Discipline Project (B502)Shanghai Key Laboratory Project (08DZ2230500)
文摘ZrO2, TiO2 and P2O5 were doped in CaO-B2O3-SiO2 glass-ceramics as nucleating additives. Effects of different nucleating additives on the phase separation and crystalline behaviors were investigated by using gradient temperature furnace, DTA and XRD. Then, sintering process of the glass-ceramics was investigated by testing sintering shrinkage, dielectric constant and loss. The experimental results shows that the glass-ceramics doped with nucleating additives represents higher crystallization, with ZrO2 as an exceptional effective dopant to promote the precipitation of wollastonite crystal. Finally, ZrO2 containing glass-ceramics was chosen to study the influence of sintering temperature and soaking time with the help of X-ray diffraction analysis and density measurement. The glass-ceramics can be well consolidated at 850 ℃ for 10 min, with low dielectric constant （5.87） and loss （3.21×10^-4）, which is desirable for LTCC application.
文摘To improve the mechanical properties of WC-Al2O3 composites, the effects of trace amount of CeO2 additives on the microstructure and mechanical properties of the WC-Al2O3 composites prepared by hot pressing were investigated. The results revealed that the WC-Al2O3 composites doped with 0.1% CeOz possessed refined microstructure and enhanced mechanical properties compared with that of the undoped WC-Al2O3composites. Trace CeO2 suppressed the decarburization of WC, promoted the microstructural refinement, and improved the interface coherence of the WC matrix and Al2O3. When 0.1% CeO2 was added to the WC-Al2O3 composites, the effect of CeO2 resulted in the achievement of a relative density of 98.82% with an excellent Vickers hardness of 16.89 GPa, combining a fracture toughness of 9.85 MPa. m1/2 with an acceptable flexural strength of 1 024.05 MPa.
文摘Michael addition of nitroalkanes to α,β-unsaturated carbonyl compounds occurs in the presence of KF/AI_2O_3/PEG4000 without solvent.Yields are fair to good and work-ups are easy.
文摘The β-aminocarboxylic acid derivatives were synthesized by Michael addition reaction of alkyl amine and α,β-unsaturated carbonyl compounds in the presence of potassium fluoride on alumina.
文摘Photodegradation has emerged as an environmentally friendly method of decomposing harmful dyes in wastewater. In this study, core-shell Fe3O4/SiO2/ TiO2 nanospheres with magnetic cores were obtained from synthesised magnetic Fe3O4 nanoparticles through the precipitation method, the surface of the magnetic Fe3O4 nanoparticles was coated with a silica (SiO2) layer by hydrolysis of tetramethoxysilane (TMOS) as a silica source, and finally, Fe3O4/SiO2 nanospheres were coated with titanium (TiO2) layer using tetrabutyltitanate (TBT) as a precursor through the sol-gel process. The morphology and structure of the prepared materials were characterised by X-ray diffraction (XRD) analysis, scanning electron microscopy (SEM), X-ray energy dispersive spectrometry (EDAX), Fourier transform infrared spectroscopy (FT-IR), and atomic force microscopy (AFM). The photocatalytic activities of the prepared core-shell nanospheres were studied using binary azo dyes, namely methyl orange (anionic dye, MO) and methylene blue (cationic dye, MB) in aqueous solution under UV light irradiation (365 nm), and UV-Vis spectrophotometer was utilised to monitor the amount of each dye in the mixture. It was found that 90.2% and 100% of binary MO and MB were removed for 5 h, respectively. The results revealed that the efficiency of the photocatalytic degradation of the core-shell nanospheres was not degreased after five runs that can be used as recyclable photocatalysts. The results show that the performance of the prepared core-shell nanospheres was better than that of commercial TiO2 nanoparticles. Moreover, the magnetic separation properties of the core-shell Fe3O4/SiO2/TiO2 nanospheres can enable the prepared materials to have wider application prospects.
基金This work was supported by the National Natural Science Foundation of China (No. 50432010, 50372037).
文摘In situ Al2O3 whiskers reinforced Ti-Al intermetallic composites were fabricated at ~1200℃ by reaction sintering of cold-consolidated fillets consisting mainly of Ti, Al, and different additives. The phases and microstructures of the sintered composites were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM) coupled with energy dispersive spectroscopy (EDS). The process of synthesis was investigated using differential thermal analysis (DTA). The effects of processing parameters and additives on the microstructures of the composites and the development of whisker were examined. It is found that the morphology of the whisker is strongly influenced by the additives, the exothermal reaction process, and the processing parameters.
文摘Nickel-alumina catalysts supported on cordierite monoliths of honeycomb structure surpass essentially the conventional granulated ones with respect to the output in carbon dioxide reforming of methane. Adjusting the surface acid-base properties of catalysts by introduction of alkali metal （Na, K） oxides inhibits the carbonization and as a result, improves the operational stability of these catalysts. An effect of promotion of nickel-alumina based composite doped by lanthanum oxide is found. This effect, caused by an additional route for the CO2 activation on Ni-La2O3/Al2O3/cordierite catalyst, is displayed in increase of methane conversion under conditions of an oxidant excess.
文摘Based on thelow temperaturecombustion synthesisof α Al2 O3 from aluminum nitrate,the effectsofthe additives on the formation and particle properties of α Al2 O3 werestudied by XRDand SEM,theinitialstudy on the manometer α Al2 O3 synthesisby LCSwas done, α Al2 O3 withtheparticlesize50 ～80 NM wasgot under properconditions.
文摘The effects of CuO and H3BO3 additions on the low-temperature sintering,microstructure,and microwave dielectric properties of Ba2Ti3Nb4O18 ceramics were investigated.The addition of less amount of CuO （ 〈1 wt%） considerably facilitated the densification of Ba2Ti3Nb4O18 ceramics.Appropriate addition of H3BO3 （ 〈3.5 wt%） remarkably improved the microwave dielectric properties of ceramics.The addition of H3BO3 and CuO successfully reduced the sintering temperature of Ba2Ti3Nb4O18 ceramics from 1300 to 1050 ℃.Ba2Ti3Nb4O18 ceramics sintered at 1 050 ℃ for 4 h with the addition of 1.0 wt% CuO and 3.5 wt% H3BO3 exhibited good microwave dielectric properties：er=33.74,Q？f=13 812 GHz,and tf=-5.35 ppm/°C at about 5.0 GHz.