The 10Ni5CrMoV steel examined was a 16 mm thick plate. Specimens measuring 12 mm×12 mm×120 mm were thermally cycled using DM-100A weld simulator with various parameters. The main results are summarized as fo...The 10Ni5CrMoV steel examined was a 16 mm thick plate. Specimens measuring 12 mm×12 mm×120 mm were thermally cycled using DM-100A weld simulator with various parameters. The main results are summarized as follaws. In the coarse-grained austenitized region（ Tm = 1 300℃ ＋ 1300℃ ） ,the microstructure is in good toughness. At the condition of Tm = 1 300℃ ＋ 850℃ and t8/5=43 s, the toughness decreases heavily because M-A constituent and twin martensite appear at the prior aastenite grain boundaries. When Tm= 1300℃ ＋ 850℃ or 1300℃ ＋ 730℃ and t8/5 = 85 s, local brittle zone is formed because of relatively coarse granular bainite.展开更多
文摘The 10Ni5CrMoV steel examined was a 16 mm thick plate. Specimens measuring 12 mm×12 mm×120 mm were thermally cycled using DM-100A weld simulator with various parameters. The main results are summarized as follaws. In the coarse-grained austenitized region（ Tm = 1 300℃ ＋ 1300℃ ） ,the microstructure is in good toughness. At the condition of Tm = 1 300℃ ＋ 850℃ and t8/5=43 s, the toughness decreases heavily because M-A constituent and twin martensite appear at the prior aastenite grain boundaries. When Tm= 1300℃ ＋ 850℃ or 1300℃ ＋ 730℃ and t8/5 = 85 s, local brittle zone is formed because of relatively coarse granular bainite.