Fatigue damage increases with the applied loading cycles in a cumulative manner and the material deteriorates with the corrosion time. A cumulative fatigue damage rule under the alternative of corrosion or cyclic load...Fatigue damage increases with the applied loading cycles in a cumulative manner and the material deteriorates with the corrosion time. A cumulative fatigue damage rule under the alternative of corrosion or cyclic loading was proposed. The specimens of aluminum alloy LY12-CZ soaked in corrosive liquid for different times were tested under the constant amplitude cyclic loading to obtain S-N curves. The test was carried out to verify the proposed cumulative fatigue damage rule under the different combinations among corrosion time, loading level, and the cycle numbers. It was shown that the predicted residual fatigue lives showed a good agreement with the experimental results and the proposed rule was simple and can be easily adopted.展开更多
In this paper,stress states under corresponding condition of an aero-engine fan blade using finite element stress-strain analysis for three work cycles in the 900 h load spectrum are obtained.Through the nominal stres...In this paper,stress states under corresponding condition of an aero-engine fan blade using finite element stress-strain analysis for three work cycles in the 900 h load spectrum are obtained.Through the nominal stress method,we calculated the fatigue notch factor and combined the material characteristics of TC6 to correct the material curve to the fan blades curve. Finally,the fatigue life of a fan blade was estimated using the linear cumulative damage rule and nonlinear cumulative damage theory.展开更多
基金supported by the National Natural Science Foundation of China(No.10377007)
文摘Fatigue damage increases with the applied loading cycles in a cumulative manner and the material deteriorates with the corrosion time. A cumulative fatigue damage rule under the alternative of corrosion or cyclic loading was proposed. The specimens of aluminum alloy LY12-CZ soaked in corrosive liquid for different times were tested under the constant amplitude cyclic loading to obtain S-N curves. The test was carried out to verify the proposed cumulative fatigue damage rule under the different combinations among corrosion time, loading level, and the cycle numbers. It was shown that the predicted residual fatigue lives showed a good agreement with the experimental results and the proposed rule was simple and can be easily adopted.
文摘In this paper,stress states under corresponding condition of an aero-engine fan blade using finite element stress-strain analysis for three work cycles in the 900 h load spectrum are obtained.Through the nominal stress method,we calculated the fatigue notch factor and combined the material characteristics of TC6 to correct the material curve to the fan blades curve. Finally,the fatigue life of a fan blade was estimated using the linear cumulative damage rule and nonlinear cumulative damage theory.