The nano-Bi2O3 powders were prepared by a chemical precipitation method with Bi（NO3）3, HNO3 and NaOH as reactants. The structural characteristics and morphology of nano-Bi2O3 powders were investigated by X-ray diffr...The nano-Bi2O3 powders were prepared by a chemical precipitation method with Bi（NO3）3, HNO3 and NaOH as reactants. The structural characteristics and morphology of nano-Bi2O3 powders were investigated by X-ray diffraction and transmission electron microscopy, respectively. The results show that under the optimum condition that 300g/L Bi（NO3）3 reacts at 90℃ for 2h, the Bi2O3 powders with 60nm on the average and 99.5% in purity are obtained. The prepared nano-Bi2O3 powders contain a mixed crystal structure of monoclinic and triclinic instead of traditional structure of monoclinic α-Bi2O3. And the mixed crystal structure is stable in air. The reason for the appearance of the mixed crystal structure may be that the ionic radius ratio of Bi 3+ to O 2- changes easily during the formation of nano-Bi2O3 particles by a chemical precipitation method.展开更多
A new water-stable metal-organic framework,[Cu_2（bdc）_2（tpt）_3]·2H_2O（1,H_2 bdc = terephthalic acid,tpt = 2,4,6-tri（4-pyridinyl）-1,3,5-triazine）,has been synthesized and characterized by elemental analysi...A new water-stable metal-organic framework,[Cu_2（bdc）_2（tpt）_3]·2H_2O（1,H_2 bdc = terephthalic acid,tpt = 2,4,6-tri（4-pyridinyl）-1,3,5-triazine）,has been synthesized and characterized by elemental analysis,infrared（IR） spectrum,thermogravimetric analysis（TGA）,powder X-ray diffraction（PXRD） and single-crystal X-ray diffraction. Compund 1 crystalizes in monoclinic,space group C2/c with a = 30.147（5）,b = 11.0548（17）,c = 20.867（4） ？,β = 115.035（2）o,C_（70）H_（48）Cu_2N_（18）O_（10）,Mr = 1428.34,V = 6301.0（18） ？~3,Z = 8,D_c = 1.506 g/cm^3,μ = 0.754 mm^（–1）,F（000） = 2928,GOOF = 1.058,λ（MoK α） = 0.71073 ？,the final R = 0.0387 and wR = 0.1091 for 6230 observed reflections with I 〉 2σ（I）. In compound 1,the half metallacycles [Cu_2（tpt）_3] are linked by the bdc2-ligands to form a 1D bent ladder-like chain featured with a nano-sized channel,and these chains link each other via intermolecular hydrogen bonds and π-π stacking interactions to form a 3D supramolecular architecture with the voids filled with free water molecules. In addition,the water stability of 1 was investigated by PXRD patterns,which indicate that compound 1 keeps its structural integrity in boiling water for at least three days.展开更多
文摘The nano-Bi2O3 powders were prepared by a chemical precipitation method with Bi（NO3）3, HNO3 and NaOH as reactants. The structural characteristics and morphology of nano-Bi2O3 powders were investigated by X-ray diffraction and transmission electron microscopy, respectively. The results show that under the optimum condition that 300g/L Bi（NO3）3 reacts at 90℃ for 2h, the Bi2O3 powders with 60nm on the average and 99.5% in purity are obtained. The prepared nano-Bi2O3 powders contain a mixed crystal structure of monoclinic and triclinic instead of traditional structure of monoclinic α-Bi2O3. And the mixed crystal structure is stable in air. The reason for the appearance of the mixed crystal structure may be that the ionic radius ratio of Bi 3+ to O 2- changes easily during the formation of nano-Bi2O3 particles by a chemical precipitation method.
基金supported by the 973 key program of the Chinese Ministry of Science and Technology(MOST)(2012CB821705)
文摘A new water-stable metal-organic framework,[Cu_2（bdc）_2（tpt）_3]·2H_2O（1,H_2 bdc = terephthalic acid,tpt = 2,4,6-tri（4-pyridinyl）-1,3,5-triazine）,has been synthesized and characterized by elemental analysis,infrared（IR） spectrum,thermogravimetric analysis（TGA）,powder X-ray diffraction（PXRD） and single-crystal X-ray diffraction. Compund 1 crystalizes in monoclinic,space group C2/c with a = 30.147（5）,b = 11.0548（17）,c = 20.867（4） ？,β = 115.035（2）o,C_（70）H_（48）Cu_2N_（18）O_（10）,Mr = 1428.34,V = 6301.0（18） ？~3,Z = 8,D_c = 1.506 g/cm^3,μ = 0.754 mm^（–1）,F（000） = 2928,GOOF = 1.058,λ（MoK α） = 0.71073 ？,the final R = 0.0387 and wR = 0.1091 for 6230 observed reflections with I 〉 2σ（I）. In compound 1,the half metallacycles [Cu_2（tpt）_3] are linked by the bdc2-ligands to form a 1D bent ladder-like chain featured with a nano-sized channel,and these chains link each other via intermolecular hydrogen bonds and π-π stacking interactions to form a 3D supramolecular architecture with the voids filled with free water molecules. In addition,the water stability of 1 was investigated by PXRD patterns,which indicate that compound 1 keeps its structural integrity in boiling water for at least three days.