This study revealed the effect of Mn on the formation of hybrid zirconium-based conversion coatings(HZCC)on low carbon steel.The XPS results indicated that the Mn compounds on the surface of low carbon steel were main...This study revealed the effect of Mn on the formation of hybrid zirconium-based conversion coatings(HZCC)on low carbon steel.The XPS results indicated that the Mn compounds on the surface of low carbon steel were mainly MnO and Mn_(2)SiO_(4).Combined with the electrochemical measurements,the corrosion resistance of HZCC showed an increase followed by a decrease with increasing Mn concentration,which was related to the Mn_(2)SiO_(4) and SiO_(2) on the surface of low carbon steel.The excessive Mn concentration resulted in the loss of SiO_(2) and aggregation of Mn_(2)SiO_(4) on the low carbon steel surface,which caused the aggregation of Zr compounds on the surface and reduced the uniformity of the coating.Meanwhile,a moderate amount of Mn addition would be beneficial to increase the adhesion of organic coatings.展开更多
基金supported by the National Natural Science Foundation of China(Grant No.51974069)the National Key R&D Program of China(No.2019YFE0123900)the Special Fund for Basic Scientific Research of Central Colleges(N2125035).
文摘This study revealed the effect of Mn on the formation of hybrid zirconium-based conversion coatings(HZCC)on low carbon steel.The XPS results indicated that the Mn compounds on the surface of low carbon steel were mainly MnO and Mn_(2)SiO_(4).Combined with the electrochemical measurements,the corrosion resistance of HZCC showed an increase followed by a decrease with increasing Mn concentration,which was related to the Mn_(2)SiO_(4) and SiO_(2) on the surface of low carbon steel.The excessive Mn concentration resulted in the loss of SiO_(2) and aggregation of Mn_(2)SiO_(4) on the low carbon steel surface,which caused the aggregation of Zr compounds on the surface and reduced the uniformity of the coating.Meanwhile,a moderate amount of Mn addition would be beneficial to increase the adhesion of organic coatings.