In：Fe：Mn：LiNbO3（LN） crystals were grown in air atmosphere by Czochralski method with different concentration of In （0, 1, 2, 3 mol%） in the melts, while the contents of Fe2O3 and MnO were 0.1 and 0.5 mol%, resp...In：Fe：Mn：LiNbO3（LN） crystals were grown in air atmosphere by Czochralski method with different concentration of In （0, 1, 2, 3 mol%） in the melts, while the contents of Fe2O3 and MnO were 0.1 and 0.5 mol%, respectively. The location of doping ions was analyzed by Ultravioletvisible absorption spectra and differential thermal analysis. The diffraction efficiency （η）, writing time （τw） and erasure time （τe） of the crystals were measured by two-beam coupling experiment. The dynamic range and photorefractive sensitivity have also been calculated. The results showed that with the increase of In ions in the melt, the absorption edge of In：Fe：Mn：LN crystal shifts to the violet firstly and then makes the Einstein shift, the Curie temperature of crystal increases firstly and then decreases, the storage ratio speeds up, diffraction efficiency decreases, and dynamic range and photorefractive sensitivity increase. The mechanism of holographic storage properties of In：Fe： Mn：LN crystal with different doping concentration of In^3＋ was investigated, suggesting the In： Fe：Mn：LN crystals are excellent holographic storage materiel with better synthetical properties than Fe：Mn：LN crystals.展开更多
The congruent tri-doped Mg:Mn:Fe:LiNbO 3 crystal has been grown by Czochralski method. Some crystal samples are reduced in Li 2CO 3 powder at 500 ℃ for 24 hours or oxidized for 10 hours at 1100 ℃ in Nb 2O 5 powder. ...The congruent tri-doped Mg:Mn:Fe:LiNbO 3 crystal has been grown by Czochralski method. Some crystal samples are reduced in Li 2CO 3 powder at 500 ℃ for 24 hours or oxidized for 10 hours at 1100 ℃ in Nb 2O 5 powder. Compared with As-grown Mg:Mn:Fe:LiNbO 3, the absorption edge in UV-Vis. absorption spectrum of the oxidized sample and the reduced shifts to the violet and the red, respectively. Reduction increases the absorption of crystals in visible light region. In two-wave coupling experiments, the writing time, maximum diffraction efficiency and the erasure time of crystal samples in the same conditions are determined. The results indicate that oxidation and reduction disposing has great effect on the holographic recording properties of these crystals. The reduced crystal exhibits the fastest response time of 160 s among the crystal series. The mechanism of post-disposing effect on the holographic recording properties of Mg:Mn:Fe:LiNbO 3 crystals are investigated.展开更多
Photorefractive properties of Hf：Fe：LiNbO3 crystals with various [Li]/[Nb] ratios have been investigated at 488 nm wavelength based on the two-wave coupling experiment. High diffraction efficiency and large recordin...Photorefractive properties of Hf：Fe：LiNbO3 crystals with various [Li]/[Nb] ratios have been investigated at 488 nm wavelength based on the two-wave coupling experiment. High diffraction efficiency and large recording sensitivity are observed and explained. The decrease in Li vacancies is suggested to be the main contributor to the increase in the photoconductivity and subsequently to the induction of the improvement of recording sensitivity. The saturation diffraction efficiency is measured up to 80.2%, and simultaneously the recording sensitivity of 0.91 cm/J is achieved to in the Hf：Fe：LiNbO3 crystal grown from the melt with the [Li]/[Nb] ratio of 1.20, which is significantly enhanced as compared with those of the Hf：Fe：LiNbO3 crystal with the [Li]/[Nb] ratio of 0.94 in melt under the same experimental conditions. Experimental results definitely show that increasing the [Li]/[Nb] ratio in crystal is an effective method＇for Hf：Fe：LiNbO3 crystal to improve its photorefractive properties.展开更多
Mg：Ru：Fe：LiN-bO3 crystals with various concentrations of MgO （in mole） and fixed content of RuO2 and Fe203 （in mass） are grown with the Czochralski method from the congruent melt. Their infrared transmission sp...Mg：Ru：Fe：LiN-bO3 crystals with various concentrations of MgO （in mole） and fixed content of RuO2 and Fe203 （in mass） are grown with the Czochralski method from the congruent melt. Their infrared transmission spectra are mea- sured and discussed to investigate the defect structure. With the increase of Mg2＋ concentration the blue nonvolatile holographic storage capability is enhanced. The nonvolatile holographic storage properties of dual-wavelength recording of Mg（7 mol%）：Ru：Fe：LiNbO3 nonvolatile diffraction efficiency, response time, and nonvolatile sensitivity reach 59.8%, 70 s, and 1.04 cm/J, respectively. Comparing Mg（7 mol%）：Ru：Fe：LiNbO3 with Ru：Fe：LiNbO3 crystal, the response time is shortened apparently. The nonvolatile diffraction efficiency and sensitivity are raised largely. The mechanism in blue photorefractive nonvolatile holographic storage is discussed.展开更多
A series of Mg：In：Fe：LiNbO3 crystals were grown by Czochralski technique; their absorption spectra and photo scattering resistance ability after oxidation or reduction treatment were measured by light spot distorti...A series of Mg：In：Fe：LiNbO3 crystals were grown by Czochralski technique; their absorption spectra and photo scattering resistance ability after oxidation or reduction treatment were measured by light spot distortion method, and their response time and exponential gain coefficient were tested by two-beam coupling experiment. Besides, the effective carrier concentration has been calculated. The results showed that the absorption edges of reduced and oxidized crystals are respectively shifted to violet and Einstein compared with those of the growth state crystal. From oxidation state to growth state to reduction state of the samples, the photo scattering resistance ability and response time decrease while the exponential gain coefficient and concentration of effective carriers increase. The reduction treatment was necessary for the Mg：In：Fe：LiNbO3 crystals to enhance their photorefractive properties.展开更多
Fe（0.2 mol%）：Cu（0.04 mol%）：LiNbO3 crystals with different doping concentration of In^3＋ （0, 1.0, 2.0, 3.0mol%） were grown by Czochralski method, and then oxidized and reduced. The infrared transmittance spect...Fe（0.2 mol%）：Cu（0.04 mol%）：LiNbO3 crystals with different doping concentration of In^3＋ （0, 1.0, 2.0, 3.0mol%） were grown by Czochralski method, and then oxidized and reduced. The infrared transmittance spectra of crystals were measured to investigate the location of doping ion and its threshold concentration. The photorefractive properties of the crystals were tested by two beam coupling experiment. The results showed that the threshold concentration of In ions is 2.0～ 3.0 mol% and In ions take the place of NbLi^4＋ to form （ InLi^2＋） before reaching its threshold concentration, and then the location of normal Nb ions. In the （2.0 mol%）：Fe：Cu：LiNbO3 crystal with the oxidation treatment having the highest diffraction efficiency （η = 45.8%）, the photo-damage resistance threshold value R of In（3.0 mol%）：Fe：Cu：LiNbO3 was 3.67×10^4 W/cm^2 which was two orders of magnitude higher than that of Fe：Cu：LiNbO3 crystal （4.30×10^2 W/cm^2）. And the photo-damage resistance ability was enhanced by oxidized treatment. The In（2.0～3.0 mol%）：Fe：Cu：LiNbO3 crystals with oxidized treatment have the best photorefractive properties.展开更多
基金Harbin Science and Technology Project (No. 2005AA5CG058)Natural Science Foundation of Heilongjiang Province (No. A0203)
文摘In：Fe：Mn：LiNbO3（LN） crystals were grown in air atmosphere by Czochralski method with different concentration of In （0, 1, 2, 3 mol%） in the melts, while the contents of Fe2O3 and MnO were 0.1 and 0.5 mol%, respectively. The location of doping ions was analyzed by Ultravioletvisible absorption spectra and differential thermal analysis. The diffraction efficiency （η）, writing time （τw） and erasure time （τe） of the crystals were measured by two-beam coupling experiment. The dynamic range and photorefractive sensitivity have also been calculated. The results showed that with the increase of In ions in the melt, the absorption edge of In：Fe：Mn：LN crystal shifts to the violet firstly and then makes the Einstein shift, the Curie temperature of crystal increases firstly and then decreases, the storage ratio speeds up, diffraction efficiency decreases, and dynamic range and photorefractive sensitivity increase. The mechanism of holographic storage properties of In：Fe： Mn：LN crystal with different doping concentration of In^3＋ was investigated, suggesting the In： Fe：Mn：LN crystals are excellent holographic storage materiel with better synthetical properties than Fe：Mn：LN crystals.
基金The subject has been supported by Chinese National Advanced Technology 863 Project(Grant No.8632001AA31304)Chinese National 973 Project(Grant No.G19990330).
文摘The congruent tri-doped Mg:Mn:Fe:LiNbO 3 crystal has been grown by Czochralski method. Some crystal samples are reduced in Li 2CO 3 powder at 500 ℃ for 24 hours or oxidized for 10 hours at 1100 ℃ in Nb 2O 5 powder. Compared with As-grown Mg:Mn:Fe:LiNbO 3, the absorption edge in UV-Vis. absorption spectrum of the oxidized sample and the reduced shifts to the violet and the red, respectively. Reduction increases the absorption of crystals in visible light region. In two-wave coupling experiments, the writing time, maximum diffraction efficiency and the erasure time of crystal samples in the same conditions are determined. The results indicate that oxidation and reduction disposing has great effect on the holographic recording properties of these crystals. The reduced crystal exhibits the fastest response time of 160 s among the crystal series. The mechanism of post-disposing effect on the holographic recording properties of Mg:Mn:Fe:LiNbO 3 crystals are investigated.
基金supported by the Fundamental Research Foundation of Commission of Science Technology,Industry for National Defense of China (Grant No.2320060089)and National Basic Research and Development Program of China (Grant No.2007CB3070001)Program of Excellent Team in Harbin Institute of Technology,China
文摘Photorefractive properties of Hf：Fe：LiNbO3 crystals with various [Li]/[Nb] ratios have been investigated at 488 nm wavelength based on the two-wave coupling experiment. High diffraction efficiency and large recording sensitivity are observed and explained. The decrease in Li vacancies is suggested to be the main contributor to the increase in the photoconductivity and subsequently to the induction of the improvement of recording sensitivity. The saturation diffraction efficiency is measured up to 80.2%, and simultaneously the recording sensitivity of 0.91 cm/J is achieved to in the Hf：Fe：LiNbO3 crystal grown from the melt with the [Li]/[Nb] ratio of 1.20, which is significantly enhanced as compared with those of the Hf：Fe：LiNbO3 crystal with the [Li]/[Nb] ratio of 0.94 in melt under the same experimental conditions. Experimental results definitely show that increasing the [Li]/[Nb] ratio in crystal is an effective method＇for Hf：Fe：LiNbO3 crystal to improve its photorefractive properties.
基金Project supported by the Fundamental Research Funds for the Central Universities of China (Grant No. DL12AB03)the National Natural Science Founda-tion of China (Grant No. 60777006)
文摘Mg：Ru：Fe：LiN-bO3 crystals with various concentrations of MgO （in mole） and fixed content of RuO2 and Fe203 （in mass） are grown with the Czochralski method from the congruent melt. Their infrared transmission spectra are mea- sured and discussed to investigate the defect structure. With the increase of Mg2＋ concentration the blue nonvolatile holographic storage capability is enhanced. The nonvolatile holographic storage properties of dual-wavelength recording of Mg（7 mol%）：Ru：Fe：LiNbO3 nonvolatile diffraction efficiency, response time, and nonvolatile sensitivity reach 59.8%, 70 s, and 1.04 cm/J, respectively. Comparing Mg（7 mol%）：Ru：Fe：LiNbO3 with Ru：Fe：LiNbO3 crystal, the response time is shortened apparently. The nonvolatile diffraction efficiency and sensitivity are raised largely. The mechanism in blue photorefractive nonvolatile holographic storage is discussed.
基金This work was supported by the Harbin Science and Technic Project (No. 2005AA5CG058)
文摘A series of Mg：In：Fe：LiNbO3 crystals were grown by Czochralski technique; their absorption spectra and photo scattering resistance ability after oxidation or reduction treatment were measured by light spot distortion method, and their response time and exponential gain coefficient were tested by two-beam coupling experiment. Besides, the effective carrier concentration has been calculated. The results showed that the absorption edges of reduced and oxidized crystals are respectively shifted to violet and Einstein compared with those of the growth state crystal. From oxidation state to growth state to reduction state of the samples, the photo scattering resistance ability and response time decrease while the exponential gain coefficient and concentration of effective carriers increase. The reduction treatment was necessary for the Mg：In：Fe：LiNbO3 crystals to enhance their photorefractive properties.
基金This work was supported by Harbin Science and Technology Project (No. 2005AA5CG058)Natural Science Foundation of Heilongjiang Province (No. A0203)
文摘Fe（0.2 mol%）：Cu（0.04 mol%）：LiNbO3 crystals with different doping concentration of In^3＋ （0, 1.0, 2.0, 3.0mol%） were grown by Czochralski method, and then oxidized and reduced. The infrared transmittance spectra of crystals were measured to investigate the location of doping ion and its threshold concentration. The photorefractive properties of the crystals were tested by two beam coupling experiment. The results showed that the threshold concentration of In ions is 2.0～ 3.0 mol% and In ions take the place of NbLi^4＋ to form （ InLi^2＋） before reaching its threshold concentration, and then the location of normal Nb ions. In the （2.0 mol%）：Fe：Cu：LiNbO3 crystal with the oxidation treatment having the highest diffraction efficiency （η = 45.8%）, the photo-damage resistance threshold value R of In（3.0 mol%）：Fe：Cu：LiNbO3 was 3.67×10^4 W/cm^2 which was two orders of magnitude higher than that of Fe：Cu：LiNbO3 crystal （4.30×10^2 W/cm^2）. And the photo-damage resistance ability was enhanced by oxidized treatment. The In（2.0～3.0 mol%）：Fe：Cu：LiNbO3 crystals with oxidized treatment have the best photorefractive properties.