Mg−1Mn−0.5Al−0.5Ca−0.5Zn(wt.%)alloy was fabricated by conventional extrusion at 673 K with an extrusion ratio of 25:1,followed by aging at 473 K.The microstructure was characterized by scanning electron microscopy,ele...Mg−1Mn−0.5Al−0.5Ca−0.5Zn(wt.%)alloy was fabricated by conventional extrusion at 673 K with an extrusion ratio of 25:1,followed by aging at 473 K.The microstructure was characterized by scanning electron microscopy,electron back-scattered diffraction,and transmission electron microscopy.The mechanical properties were determined by the tensile test.The peak-aged sample shows fine recrystallized grains with an average grain size of 1.7μm.Area fraction of Al−Ca particles in the alloy increases significantly after peak aging.Meanwhile,botháañandác+añdislocations were observed to remain in the alloy after hot extrusion.Thus,the peak-aged sample exhibits simultaneously high strength and good ductility with the ultimate tensile stress,tensile yield stress,and tension fracture elongation of 320 MPa,314 MPa,and 19.0%,respectively.展开更多
To investigate the effect of separate Al_(2)Ca and Mg_(2)Ca phases on the corrosion properties of Mg−Al−Ca−Mn alloys,OM,SEM,immersion and electrochemical tests were conducted on the as-cast and ECAP Al_(2)Ca-containin...To investigate the effect of separate Al_(2)Ca and Mg_(2)Ca phases on the corrosion properties of Mg−Al−Ca−Mn alloys,OM,SEM,immersion and electrochemical tests were conducted on the as-cast and ECAP Al_(2)Ca-containing(2Ca)and Mg_(2)Ca-containing(4Ca)alloys.At the beginning of corrosion,the two as-cast alloys are corroded slowly compared with ECAP alloys.With prolonging the corrosion time,the corrosion of ECAP alloys becomes slighter than that of as-cast alloys,which is mainly ascribed to the dispersion and refinement of the second phase in ECAP alloys.Moreover,the corrosion degree of 2Ca alloys is always slighter than that of 4Ca alloys,suggesting that Al_(2)Ca phase is more beneficial to the enhancement of corrosion resistance of Mg−Al−Ca−Mn based alloys than Mg_(2)Ca phase.Finally,based on the examinations of corrosion surface and electrochemical testing results,different corrosion mechanisms caused by the distributions and morphology of Al_(2)Ca and Mg_(2)Ca phases are discussed.展开更多
以不同脱氧方式熔炼的海洋工程用钢为研究对象,利用SEM、EDS及Image-Pro Plus 6.0软件对钢中夹杂物形貌、组成及尺寸分布等进行表征,通过3.5%NaCl溶液中阳极极化及腐蚀实验对钢中夹杂物诱发点蚀的行为进行探究。结果表明,与Al-Mg脱氧钢...以不同脱氧方式熔炼的海洋工程用钢为研究对象,利用SEM、EDS及Image-Pro Plus 6.0软件对钢中夹杂物形貌、组成及尺寸分布等进行表征,通过3.5%NaCl溶液中阳极极化及腐蚀实验对钢中夹杂物诱发点蚀的行为进行探究。结果表明,与Al-Mg脱氧钢相比,Ti-Mg脱氧钢中形成了含有TiO_x的复合氧化物,夹杂数量更多且平均尺寸更小(小于1μm),有利于MnS的异质形核析出及弥散分布;低腐蚀活性的含TiOx复合氧化物及高度分散、异质局部析出MnS夹杂具有较低的点蚀敏感性及自腐蚀催化作用,降低了点蚀的诱发及扩展,有效提高了钢的抗点蚀性能。展开更多
New Al4C3-containing Al-Ti-C master alloys (Al-0.6Ti-1C and Al-1Ti-1C) were developed by introducing Ti element into Al-C melt using melt reaction method,in which most of the TiC particles distribute around Al4C3 part...New Al4C3-containing Al-Ti-C master alloys (Al-0.6Ti-1C and Al-1Ti-1C) were developed by introducing Ti element into Al-C melt using melt reaction method,in which most of the TiC particles distribute around Al4C3 particles. It is believed that most of the C firstly reacts with Al melt and form Al4C3 particles by the reaction Al(l)+C(s)→Al4C3(s),and after adding Ti into the Al-C melt,the size of Al4C3 particles is decreased and the distribution of Al4C3 is improved through the reaction Ti(solute)+Al4C3(s)→ TiC(s)+Al(l). With the addition of 1% Al-1Ti-1C master alloy,the average grain size of AZ31 is reduced sharply from 850 μm to 200 μm,and the grain morphology of α-Mg transits from a fully-developed equiaxed dendritic structure to a petal-like shape. Al-C-O-Mn-Fe compounds are proposed to be potent nucleating substrates for primary Mg. Appropriate addition of Ti is believed to increase the grain refinement efficiency of Al4C3-containing Al-Ti-C master alloys in AZ31 alloy.展开更多
基金the financial supports from the Fundamental Research Funds for the Central Universities,China(Nos.2019CDCGCL316,2020CDJDPT001)Chongqing Research Program of Basic Research and Frontier Technology,China(No.cstc2019jcjy-msxmX0539)。
文摘Mg−1Mn−0.5Al−0.5Ca−0.5Zn(wt.%)alloy was fabricated by conventional extrusion at 673 K with an extrusion ratio of 25:1,followed by aging at 473 K.The microstructure was characterized by scanning electron microscopy,electron back-scattered diffraction,and transmission electron microscopy.The mechanical properties were determined by the tensile test.The peak-aged sample shows fine recrystallized grains with an average grain size of 1.7μm.Area fraction of Al−Ca particles in the alloy increases significantly after peak aging.Meanwhile,botháañandác+añdislocations were observed to remain in the alloy after hot extrusion.Thus,the peak-aged sample exhibits simultaneously high strength and good ductility with the ultimate tensile stress,tensile yield stress,and tension fracture elongation of 320 MPa,314 MPa,and 19.0%,respectively.
基金financial supports from the National Natural Science Foundation of China (Nos.51901068,51979099)the Key Research and Development Project of Jiangsu Province,China (No.BE2021027)+1 种基金the Opening Project of Jiangsu Key Laboratory of Advanced Structural Materials and Application Technology,China (No.ASMA202102)the Research Fund from Key Laboratory for Light-weight Materials of Jiangsu Province,China。
文摘To investigate the effect of separate Al_(2)Ca and Mg_(2)Ca phases on the corrosion properties of Mg−Al−Ca−Mn alloys,OM,SEM,immersion and electrochemical tests were conducted on the as-cast and ECAP Al_(2)Ca-containing(2Ca)and Mg_(2)Ca-containing(4Ca)alloys.At the beginning of corrosion,the two as-cast alloys are corroded slowly compared with ECAP alloys.With prolonging the corrosion time,the corrosion of ECAP alloys becomes slighter than that of as-cast alloys,which is mainly ascribed to the dispersion and refinement of the second phase in ECAP alloys.Moreover,the corrosion degree of 2Ca alloys is always slighter than that of 4Ca alloys,suggesting that Al_(2)Ca phase is more beneficial to the enhancement of corrosion resistance of Mg−Al−Ca−Mn based alloys than Mg_(2)Ca phase.Finally,based on the examinations of corrosion surface and electrochemical testing results,different corrosion mechanisms caused by the distributions and morphology of Al_(2)Ca and Mg_(2)Ca phases are discussed.
文摘以不同脱氧方式熔炼的海洋工程用钢为研究对象,利用SEM、EDS及Image-Pro Plus 6.0软件对钢中夹杂物形貌、组成及尺寸分布等进行表征,通过3.5%NaCl溶液中阳极极化及腐蚀实验对钢中夹杂物诱发点蚀的行为进行探究。结果表明,与Al-Mg脱氧钢相比,Ti-Mg脱氧钢中形成了含有TiO_x的复合氧化物,夹杂数量更多且平均尺寸更小(小于1μm),有利于MnS的异质形核析出及弥散分布;低腐蚀活性的含TiOx复合氧化物及高度分散、异质局部析出MnS夹杂具有较低的点蚀敏感性及自腐蚀催化作用,降低了点蚀的诱发及扩展,有效提高了钢的抗点蚀性能。
基金Project(50625101) supported by the National Natural Science Foundation for Distinguished Young Scholars of ChinaProject(106103) supported by Key Project of Science and Technology Research of Ministry of Education of China
文摘New Al4C3-containing Al-Ti-C master alloys (Al-0.6Ti-1C and Al-1Ti-1C) were developed by introducing Ti element into Al-C melt using melt reaction method,in which most of the TiC particles distribute around Al4C3 particles. It is believed that most of the C firstly reacts with Al melt and form Al4C3 particles by the reaction Al(l)+C(s)→Al4C3(s),and after adding Ti into the Al-C melt,the size of Al4C3 particles is decreased and the distribution of Al4C3 is improved through the reaction Ti(solute)+Al4C3(s)→ TiC(s)+Al(l). With the addition of 1% Al-1Ti-1C master alloy,the average grain size of AZ31 is reduced sharply from 850 μm to 200 μm,and the grain morphology of α-Mg transits from a fully-developed equiaxed dendritic structure to a petal-like shape. Al-C-O-Mn-Fe compounds are proposed to be potent nucleating substrates for primary Mg. Appropriate addition of Ti is believed to increase the grain refinement efficiency of Al4C3-containing Al-Ti-C master alloys in AZ31 alloy.