热处理温度对纳米Mn-Zn铁氧体微粒的M_s、H_c的影响

采用柠檬酸盐自燃烧法制备纳米锰锌(Mn-Zn)铁氧体微粒,研究后续热处理温度对产物的饱和磁化强度(Ms)、矫顽力(Hc)的影响。结果表明,纳米Mn-Zn铁氧体微粒的Ms、Hc随着热处理温度的升高,变化趋势都是先增大后减小。Ms在热处理温度为450℃时,达到最大值(46.8Am2/g);Hc在热处理温度为400℃时,达到最大值(2.7×105A/m)。纳米Mn-Zn铁氧体微粒的单畴临界尺寸大约为58nm。

Ferromagnetism of Mn-doped ZnO nanoparticles prepared by sol-gel process at room temperature

Mn-doped ZnO diluted magnetic semiconductor nanoparticles are prepared by an ultrasonic assisted sol-gel process.Transmission electron microscopy shows pseudo-hexagonal nanoparticles with an average size of about 24 nm.From the analysis of X-ray diffraction,the Mn-doped ZnO nanoparticles are identified to be a wurtzite structure without any impurity phases.The magnetic properties are measured by using superconducting quantum interference device.For the ZnO with 2% Mn doping concentration,a good hysteresis loop indicates fine ferromagnetism with a Curie temperature higher than 350 K.

纳米ZnS基白光发射材料的制备和表征

利用溶胶凝胶法,通过直接掺杂Mn2+获得白光发射且操作工艺简单的纳米ZnS∶Mn荧光粉,使用XRD、UV、PL及FT IR等方法研究了ZnS∶Mn纳米微粒的粒径、结构及荧光特性。结果表明:ZnS∶Mn纳米微粒的平均粒径约为7nm,为闪锌矿晶体结构;所制备样品的荧光发射光谱有强度相当的两个峰,一个是峰值位于480nm的基质发光,另一个是峰值位于590nm的橙色光,样品总体发白光;Mn2+的掺杂量对ZnS∶Mn纳米白光荧光粉发光性能的影响很大;在纳米微粒的形成过程中,聚甲基丙烯酸将该纳米粒子包覆。

白光发射材料的制备和光学性能研究

用溶胶- 凝胶法,在ZnS基质中直接掺杂过渡金属元素Cu ,Mn ,并适当调整Cu ,Mn的掺杂量,获得白光发射且操作工艺简单的纳米ZnS :Cu ,Mn荧光粉,使用XRD ,UV和PL等方法研究了粉粒的粒径、结构及荧光特性。