Novel porous Mn2O3 with good crystallinity was synthesized via hard-template method. Hb-Mn2O3 na-nocomposite was prepared and used for biosensor construction. The Hb-Mn2O3-Nafion modified electrode shows fast direct e...Novel porous Mn2O3 with good crystallinity was synthesized via hard-template method. Hb-Mn2O3 na-nocomposite was prepared and used for biosensor construction. The Hb-Mn2O3-Nafion modified electrode shows fast direct electron transfer and displays good electrocatalytic response to the reduction of H2O2. The response time is less than 5 s, the sensitivity is as high as 493 μA·L·mmol-1·cm-2 in a linear range of 1-100 μmol/L, and the detection limit is 0.16 μmol/L. This modified electrode also shows good stability and reproducibility. This indicates that the porous Mn2O3 provides a good matrix for enzyme immobilization and biosensor construction.展开更多
Nanosized orthorhombic LiMnO2 was successfully synthesized using Mn2O3 and LiOH.H2O as starting materials.Not only the reaction temperature was lower, but the reaction time for synthesizing was notably shortened to 1 ...Nanosized orthorhombic LiMnO2 was successfully synthesized using Mn2O3 and LiOH.H2O as starting materials.Not only the reaction temperature was lower, but the reaction time for synthesizing was notably shortened to 1 h.In this hydrothermal process, the cations of the starting materials were capable of mixing and interacting in ionic scale, which resulted in the rapid formation of o-LiMnO2 powders at relatively low temperature. The particle size conformed by transmission electron microscopy is around 50-150 nm. Benefiting from its small particle size and good uniformity, the obtained o-LiMnO2 can reach the maximum discharge capacity of 163 mA-h.g^-1 at 0.1 C rate after several cycles. X-ray diffraction data and electrochemical properties suggested the phase transformation from orthorhombic LiMnO2 to defect-type spinel LiMn204 with minor Li2MnO3, which resulted in the capacity fading during cycling.展开更多
基金Supported by the National Basic Research Program of China(No.2011CB935700)the National Natural Science Foundation of China(No.U0734002)
文摘Novel porous Mn2O3 with good crystallinity was synthesized via hard-template method. Hb-Mn2O3 na-nocomposite was prepared and used for biosensor construction. The Hb-Mn2O3-Nafion modified electrode shows fast direct electron transfer and displays good electrocatalytic response to the reduction of H2O2. The response time is less than 5 s, the sensitivity is as high as 493 μA·L·mmol-1·cm-2 in a linear range of 1-100 μmol/L, and the detection limit is 0.16 μmol/L. This modified electrode also shows good stability and reproducibility. This indicates that the porous Mn2O3 provides a good matrix for enzyme immobilization and biosensor construction.
基金supported by the National Natural Science Foundation of China under grant No.50372058.
文摘Nanosized orthorhombic LiMnO2 was successfully synthesized using Mn2O3 and LiOH.H2O as starting materials.Not only the reaction temperature was lower, but the reaction time for synthesizing was notably shortened to 1 h.In this hydrothermal process, the cations of the starting materials were capable of mixing and interacting in ionic scale, which resulted in the rapid formation of o-LiMnO2 powders at relatively low temperature. The particle size conformed by transmission electron microscopy is around 50-150 nm. Benefiting from its small particle size and good uniformity, the obtained o-LiMnO2 can reach the maximum discharge capacity of 163 mA-h.g^-1 at 0.1 C rate after several cycles. X-ray diffraction data and electrochemical properties suggested the phase transformation from orthorhombic LiMnO2 to defect-type spinel LiMn204 with minor Li2MnO3, which resulted in the capacity fading during cycling.