Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part i...Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.展开更多
Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nano...Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nanocrystalline is in the range of 10\20 nm, the mean size is 16 nm.展开更多
A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5...A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5(3) nm, b=1.012 2(2) nm, c=1.832 5(4) nm, β=90.21°, V=2\^668 2(9) nm 3, Z=2, D c=2.112 g/cm 3, R=0.055, wR=0.149 7, S=1.037. The structure of 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] is characterized by P-V-O layers constructed by [(VO) 4(OH) 2(PO 4) 4] 6- non-symmetric units. The P-V-O layers are pillared by [Co(H 2O) 2] 2+ group, resulting in the channels within which the protonated diaminoethane and H 3O + are located.展开更多
A novel flower-like hydrated magnesium carbonate hydroxide, Mg5 （CO3 ）4 （OH）2·4H2O, with micro-structure composed of individual thin nano-sheets was synthesized using a facile solution route without the use o...A novel flower-like hydrated magnesium carbonate hydroxide, Mg5 （CO3 ）4 （OH）2·4H2O, with micro-structure composed of individual thin nano-sheets was synthesized using a facile solution route without the use of template or organic surfactant. Reaction time has an important effect on the final morphology of the product. The micro-structure and morphology of Mg5 （CO3）4 （OH）2·4H2O were characterized by means of X-ray diffractometry （XRD）, fieldemission scanning electron microscopy（FE-SEM）. Brunauer-Emmett-Teller（BET） surface areas of the samples were also measured. The probable formation mechanism of flower-like micro-structure was discussed. It was found that Mg5 （CO3）4（ OH）2·4H2O with flower-like micro-structure was a novel and efficient catalyst for the synthesis of diphenyl carbonate （DPC） by transesterification of dimethyl carbonate （DMC） with phenol.展开更多
A novel three dimensional fluorinated gallium phosphate has been hydrothermally synthesized by using diethylenetriamine as an organic structure directing agent. X ray single crystal structure analysis indicates this c...A novel three dimensional fluorinated gallium phosphate has been hydrothermally synthesized by using diethylenetriamine as an organic structure directing agent. X ray single crystal structure analysis indicates this compound crystallizes in the orthorhombic space group Pbca, a =1.605 6(7) nm, b = 1 011 4 (4) nm, c =1.854 6(5) nm, V =3.011 6(19) nm 3, Z =4. The three dimensional framework based on linkage of corner sharing polyhedron PO 4, GaO 4F and GaO 4F 2 delimit ten ring channels along b axis in which the triply protonated amines are located serving as charge compensating guests and supporters.展开更多
A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O c...A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O crystal crystallizes in the monoclinic system, space group C2/m , with M=128.13, a =0\^994 7(2) nm, b =1.321 7(3) nm; c =0.463 6(1) nm; β=104.80(3)°, V =0.589 3(2) nm 3, Z=2, R=0.027 2 and wR =0.057 5. The network structure consists of vertex sharing which results in the formation of undulating 4 ring chains and 8 ring sheets.展开更多
The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a=...The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a= 1.41999(2)nm, b=1.43467(2)nm, c=1.694610(10)nm, α=95.7250(10)°, β=92.2110(10)°, γ=92.6060(10)°, V=3.42829(7)nm3, Z=2, Dc=2.388g·cm-3, Mr=2465.10g·mol-1, μ=2.489mm-1, F(000)=2388, R1=0.0584, wR2=0.1461, S=1.164. The heteropolyanion is a bi capped pseudo Keggin complex. CCDC: 186645.展开更多
文摘Both whisker and nanometer MgSO4·5Mg(OH)2·3H2O(MOS) were prepared by hydrothermal method at 140℃for different times, using NaOH and MgSO4·7H2O as raw materials. The MgSO4·5Mg(OH)2·3H2O part icles were characterized by powder X ray diffraction(XRD),thermal analysis(TGA DSC), infrared spectroscopy(FT IR),transmission electron microscopy(SEM) and scanning electron microscopy(TEM). The size distribution in whisker like and nanocrystalline materials arein the range of 10～50μm and 10～20nm respectively. The whisker MOS is metastable phase in MgSO4 NaOH H2O system at 140℃,whereas nanometer MOS is stable phase.
文摘Nanocrystalline MgSO\-4·5Mg（OH）\-2·3H\-2O were prepared by the hydrothermal reaction at 140 ℃ for 24 h. Nanoparticle samples were characterized by FTIR, TG, DSC, XRD and TEM. The size distribution of nanocrystalline is in the range of 10\20 nm, the mean size is 16 nm.
文摘A new compound 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] has been hydrothermally synthesized. Single crystal X-ray analysis indicates that this compound crystallizes in a monoclinic system, space group P2 1/n with a=1.438 5(3) nm, b=1.012 2(2) nm, c=1.832 5(4) nm, β=90.21°, V=2\^668 2(9) nm 3, Z=2, D c=2.112 g/cm 3, R=0.055, wR=0.149 7, S=1.037. The structure of 2 6[Co(H 2O) 2(VO) 8(OH) 4(PO 4) 8] is characterized by P-V-O layers constructed by [(VO) 4(OH) 2(PO 4) 4] 6- non-symmetric units. The P-V-O layers are pillared by [Co(H 2O) 2] 2+ group, resulting in the channels within which the protonated diaminoethane and H 3O + are located.
基金Supported by the National Natural Science Foundation of China(Nos.20671011,20331010,90406002and90406024)the 111 Project(No.B07012)the Key Laboratory of Structural Chemistry Foundation(No.060017).
文摘A novel flower-like hydrated magnesium carbonate hydroxide, Mg5 （CO3 ）4 （OH）2·4H2O, with micro-structure composed of individual thin nano-sheets was synthesized using a facile solution route without the use of template or organic surfactant. Reaction time has an important effect on the final morphology of the product. The micro-structure and morphology of Mg5 （CO3）4 （OH）2·4H2O were characterized by means of X-ray diffractometry （XRD）, fieldemission scanning electron microscopy（FE-SEM）. Brunauer-Emmett-Teller（BET） surface areas of the samples were also measured. The probable formation mechanism of flower-like micro-structure was discussed. It was found that Mg5 （CO3）4（ OH）2·4H2O with flower-like micro-structure was a novel and efficient catalyst for the synthesis of diphenyl carbonate （DPC） by transesterification of dimethyl carbonate （DMC） with phenol.
文摘A novel three dimensional fluorinated gallium phosphate has been hydrothermally synthesized by using diethylenetriamine as an organic structure directing agent. X ray single crystal structure analysis indicates this compound crystallizes in the orthorhombic space group Pbca, a =1.605 6(7) nm, b = 1 011 4 (4) nm, c =1.854 6(5) nm, V =3.011 6(19) nm 3, Z =4. The three dimensional framework based on linkage of corner sharing polyhedron PO 4, GaO 4F and GaO 4F 2 delimit ten ring channels along b axis in which the triply protonated amines are located serving as charge compensating guests and supporters.
文摘A new two dimensional 8 ring network nickle phosphate Ni 3(PO 4) 2·8H 2O was synthesized hydrothermally and its structure was determined by means of single crystal X ray diffraction. The Ni 3(PO 4) 2·8H 2O crystal crystallizes in the monoclinic system, space group C2/m , with M=128.13, a =0\^994 7(2) nm, b =1.321 7(3) nm; c =0.463 6(1) nm; β=104.80(3)°, V =0.589 3(2) nm 3, Z=2, R=0.027 2 and wR =0.057 5. The network structure consists of vertex sharing which results in the formation of undulating 4 ring chains and 8 ring sheets.
文摘The novel polyoxometalate, 32[Mo8ⅣMo4ⅤV2ⅣO38(PO4)], was synthesized and characterized by elementary analysis, EPR, IR spectra and X ray diffraction. The compoundcrystallizes in triclinic system, space group with a= 1.41999(2)nm, b=1.43467(2)nm, c=1.694610(10)nm, α=95.7250(10)°, β=92.2110(10)°, γ=92.6060(10)°, V=3.42829(7)nm3, Z=2, Dc=2.388g·cm-3, Mr=2465.10g·mol-1, μ=2.489mm-1, F(000)=2388, R1=0.0584, wR2=0.1461, S=1.164. The heteropolyanion is a bi capped pseudo Keggin complex. CCDC: 186645.