A series of MnCeOx catalysts supported on cordierite honeycomb （Cord） were prepared by a combustion synthesis method using Mn（NO3）2 , Ce（NO3 ）2·6H2O and citric acid. The effect of the molar ratio of Mn/Ce, ...A series of MnCeOx catalysts supported on cordierite honeycomb （Cord） were prepared by a combustion synthesis method using Mn（NO3）2 , Ce（NO3 ）2·6H2O and citric acid. The effect of the molar ratio of Mn/Ce, calcination time, the amount of citric acid and the effect of water vapor on the catalytic properties for the complete oxidation of benzene were investigated. These catalysts were characterized by X-ray diffraction （XRD）, H 2 temperature-programmed reduction （H2 -TPR）, O2 temperature programmed desorption （O2 -TPD） and scanning electron microscopy （SEM） techniques. The results indicated that the MnCeOx /Cord catalyst with Mn/Ce molar ratio of 1：1, calcining for 7h and M n＋ /（citric acid） molar ratio of 6 exhibited the highest catalytic activity. When the concentration of benzene was 1500 ppm and the gaseous hourly space velocity was 20000h -1 , the conversion of toluene was 99.1% at the reaction temperature of 300 oC.展开更多
基金Project supported by National Natural Science Foundation of China(51172107,21106072)National Key Technology R&D Program of China(2012BAE01B03)+1 种基金R&D Project for Environmental Protection of Jiangsu(2011023)project funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions(PAPD)
文摘A series of MnCeOx catalysts supported on cordierite honeycomb （Cord） were prepared by a combustion synthesis method using Mn（NO3）2 , Ce（NO3 ）2·6H2O and citric acid. The effect of the molar ratio of Mn/Ce, calcination time, the amount of citric acid and the effect of water vapor on the catalytic properties for the complete oxidation of benzene were investigated. These catalysts were characterized by X-ray diffraction （XRD）, H 2 temperature-programmed reduction （H2 -TPR）, O2 temperature programmed desorption （O2 -TPD） and scanning electron microscopy （SEM） techniques. The results indicated that the MnCeOx /Cord catalyst with Mn/Ce molar ratio of 1：1, calcining for 7h and M n＋ /（citric acid） molar ratio of 6 exhibited the highest catalytic activity. When the concentration of benzene was 1500 ppm and the gaseous hourly space velocity was 20000h -1 , the conversion of toluene was 99.1% at the reaction temperature of 300 oC.