The microstructural evolution and Vickers hardness measurement in the welding heat-affected zone （HAZ） of HD15 Nil MnMoNbCu steel for nuclear power station were investigated by Gleeble-3180 thermal mechanical simula...The microstructural evolution and Vickers hardness measurement in the welding heat-affected zone （HAZ） of HD15 Nil MnMoNbCu steel for nuclear power station were investigated by Gleeble-3180 thermal mechanical simulator, and the simulated HAZ continuous cooling transformation curves （SH-CCT） were measured simultaneously. With ts/5 inereasing from 3.75 s to 15 000 s, the product was obtained martensite, bainite, ferrite and pearlite, successively. The result of microstructure and Vickers hardness in the heat-affected zone was in good agreement with those measured by SH-CCT diagram with the heat input 16. 2 kJ/cm as an example to weld the HD15Ni1MnMoNbCu steel pipe using TIG/SMAW/SAW welding methods.展开更多
文摘The microstructural evolution and Vickers hardness measurement in the welding heat-affected zone （HAZ） of HD15 Nil MnMoNbCu steel for nuclear power station were investigated by Gleeble-3180 thermal mechanical simulator, and the simulated HAZ continuous cooling transformation curves （SH-CCT） were measured simultaneously. With ts/5 inereasing from 3.75 s to 15 000 s, the product was obtained martensite, bainite, ferrite and pearlite, successively. The result of microstructure and Vickers hardness in the heat-affected zone was in good agreement with those measured by SH-CCT diagram with the heat input 16. 2 kJ/cm as an example to weld the HD15Ni1MnMoNbCu steel pipe using TIG/SMAW/SAW welding methods.