MnO_x/Al_2O_3 and MnO_x/ZrO_2-Al_2O_3 catalysts were prepared by incipientwetness impregnation of Mn(CH_3COO)_2 on the corresponding supports, followed by thecharacterization using X-ray diffraction (XRD), temperature...MnO_x/Al_2O_3 and MnO_x/ZrO_2-Al_2O_3 catalysts were prepared by incipientwetness impregnation of Mn(CH_3COO)_2 on the corresponding supports, followed by thecharacterization using X-ray diffraction (XRD), temperature programmed reduction (TPR) and BETsurface area techniques. The result shows the BET surface area of ZrO_2-Al_2O_3 is lower than thatof Al_2O_3 due to the loading of ZrO_2. However the resulted MnO_x/ZrO_2-Al_2O_3 catalyst exhibitshigher activity for methane combustion than MnO_x/Al_2O_3, because the addition of ZrO_2 ontoAl_2O_3 is beneficial for the dispersion of Mn species and the improvement of the lattice oxygenactivity in MnO_x, subsequently the activation of methane during combustion. The optimum loading ofZr in MnO_x/ZrO_2-Al_2O_3 is in the range of 5%-10% correlated with the calcination temperatures ofcatalyst supports.展开更多
Low-temperature selective catalytic reduction of NOx combined with dust removal technique due to its energy conservation characteristic has been attracted much attention for fume purification.In this work,the MnOx wra...Low-temperature selective catalytic reduction of NOx combined with dust removal technique due to its energy conservation characteristic has been attracted much attention for fume purification.In this work,the MnOx wrapped PTFE membrane with efficient dust removal and low-temperature NH3-SCR has been prepared with a facile route.MnOxwith different crystal structures was uniformly grown around the PTFE fibrils through water bath.The flower-sphere-like MnOx@PTFE(O-MnOx@PTFE)and lamellar-interlaced ripple-like MnOx@PTFE(W-MnOx@PTFE)have large specific surface area which is favorable for enhancing catalytic performance.Also,the uniformly wrapped W-MnOxaround the PTFE fibrils optimized the pore structure for ultrafine dust capture.The membrane can almost 100%reject particles that are smaller than 1.0μm with a low filtration resistance.Meanwhile,W-MnOx@PTFE with more surface chemisorbed oxygen has the best NO conversion efficiency of 100%at a comparatively low and wide activity temperature window of 160–210°C,which is far to the thermal limitation of the PTFE.Therefore,this efficient and energy conserving membrane has a bright application prospects for tail gas treatment compared to the original treatment process.展开更多
基金This work was financially supported by Shandong Provincial Department of Science and Technology(project number:981206403)and the State Key Laboratory of Coal Conversion at Institute of Coal Chemistry of CAS(2002-2003)
文摘MnO_x/Al_2O_3 and MnO_x/ZrO_2-Al_2O_3 catalysts were prepared by incipientwetness impregnation of Mn(CH_3COO)_2 on the corresponding supports, followed by thecharacterization using X-ray diffraction (XRD), temperature programmed reduction (TPR) and BETsurface area techniques. The result shows the BET surface area of ZrO_2-Al_2O_3 is lower than thatof Al_2O_3 due to the loading of ZrO_2. However the resulted MnO_x/ZrO_2-Al_2O_3 catalyst exhibitshigher activity for methane combustion than MnO_x/Al_2O_3, because the addition of ZrO_2 ontoAl_2O_3 is beneficial for the dispersion of Mn species and the improvement of the lattice oxygenactivity in MnO_x, subsequently the activation of methane during combustion. The optimum loading ofZr in MnO_x/ZrO_2-Al_2O_3 is in the range of 5%-10% correlated with the calcination temperatures ofcatalyst supports.
文摘Low-temperature selective catalytic reduction of NOx combined with dust removal technique due to its energy conservation characteristic has been attracted much attention for fume purification.In this work,the MnOx wrapped PTFE membrane with efficient dust removal and low-temperature NH3-SCR has been prepared with a facile route.MnOxwith different crystal structures was uniformly grown around the PTFE fibrils through water bath.The flower-sphere-like MnOx@PTFE(O-MnOx@PTFE)and lamellar-interlaced ripple-like MnOx@PTFE(W-MnOx@PTFE)have large specific surface area which is favorable for enhancing catalytic performance.Also,the uniformly wrapped W-MnOxaround the PTFE fibrils optimized the pore structure for ultrafine dust capture.The membrane can almost 100%reject particles that are smaller than 1.0μm with a low filtration resistance.Meanwhile,W-MnOx@PTFE with more surface chemisorbed oxygen has the best NO conversion efficiency of 100%at a comparatively low and wide activity temperature window of 160–210°C,which is far to the thermal limitation of the PTFE.Therefore,this efficient and energy conserving membrane has a bright application prospects for tail gas treatment compared to the original treatment process.