Mo-based alloys are widely used for their excellent wear and corrosion resistance as well as high temperature resistance.Mo-NiCrBSi and Mo-Ni alloy coatings were prepared on 1020 water wall tube by laser cladding tech...Mo-based alloys are widely used for their excellent wear and corrosion resistance as well as high temperature resistance.Mo-NiCrBSi and Mo-Ni alloy coatings were prepared on 1020 water wall tube by laser cladding technology in the present study.The microstructure and phase compositions were analyzed by means of the scanning electron microscopy(SEM),energy-dispersive spectroscopy(EDS)and X-ray diffractometry(XRD).The corrosion properties of the coatings were evaluated by an electrochemical experiment at room temperature in 3.5 wt.%NaCl electrolyte.With increasing content of Mo,the structure homogeneity in Mo-Ni coatings deteriorated,the grain size increased,the average hardness and the corrosion resistance declined,due to the more content of harmful phases.Compared to the Mo-Ni coatings,the overall performance was better for the Mo-NiCrBSi,which had the higher hardness contributed by the element B and Si as well as the better corrosion resistance due to the addition of Cr.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.11372110and 51101056)+1 种基金the National Science and Technology Support Program(Grant No.2011BAE12B03)the Fundamental Research Funds for the Central Universities(Grant No.12MS07)
文摘Mo-based alloys are widely used for their excellent wear and corrosion resistance as well as high temperature resistance.Mo-NiCrBSi and Mo-Ni alloy coatings were prepared on 1020 water wall tube by laser cladding technology in the present study.The microstructure and phase compositions were analyzed by means of the scanning electron microscopy(SEM),energy-dispersive spectroscopy(EDS)and X-ray diffractometry(XRD).The corrosion properties of the coatings were evaluated by an electrochemical experiment at room temperature in 3.5 wt.%NaCl electrolyte.With increasing content of Mo,the structure homogeneity in Mo-Ni coatings deteriorated,the grain size increased,the average hardness and the corrosion resistance declined,due to the more content of harmful phases.Compared to the Mo-Ni coatings,the overall performance was better for the Mo-NiCrBSi,which had the higher hardness contributed by the element B and Si as well as the better corrosion resistance due to the addition of Cr.