The effects of vanadium(V)on the microstructures and mechanical properties of the TiC cermet fusion welding interface were studied by adjusting the content of V in the self-developed flux-cored wires using metal inert...The effects of vanadium(V)on the microstructures and mechanical properties of the TiC cermet fusion welding interface were studied by adjusting the content of V in the self-developed flux-cored wires using metal inert gas arc(MIG)welding for surfacing on the TiC cermet.The results show that the increase in V content promotes the element diffusion between TiC cermet and weld metal.There are no de-fects observed in the interface,and the diffusion of elements refers to excellent metallurgical bonding.The shear strength of the fusion zone initially decreases and then increases with the increase in V content.The maximum shear strength of the TiC cermet/weld interface,reaching 552 MPa,occurred when the V content reached 0.65%.Meanwhile,the average hardness in the transition zone reached 488.2 HV0.2.展开更多
Effect of Mo and Mo2 C on the microstructure and properties of Ti(C,N)-based cermets was investigated in this article. The results have indicated that the weight percentage of Mo from 5 to 10 can reduce Ti(C,N) gr...Effect of Mo and Mo2 C on the microstructure and properties of Ti(C,N)-based cermets was investigated in this article. The results have indicated that the weight percentage of Mo from 5 to 10 can reduce Ti(C,N) grain diameter and thickness of the rim, and Ti(C,N) grain can be wetted by Ni-Cu-Mo liquid so as to get small contiguity of Ti(C,N) grain. In that way, the transverse rupture strength of Ti(C,N)-based cermets has reached 1800-1900 MPa; the fracture toughness has been due to 16-18 MPa.m1/2. But 15 wt pct Mo was not more effective on Ti(C,N)-based cermets, because the thickness of the rim becomes larger. In the circumstance of Mo2 C, 5 wt pct Mo2 C was good for microstructure and properties of Ti(C,N)-based cermets, but 11 wt pct Mo2C has resulted in larger contiguity of Ti(C,N) grain and big Ti(C,N) grain diameter so as to reduce transverse rupture strength and fracture toughness. So that, the effect of Mo on Ti(C,N)-based cermets is better than Mo2C.展开更多
The effects of Mo on the microstructure and mechanical properties of Ti(C,N)-based cermets with low Ni have been studied systematically. Different contents of Mo (4-12 wt.%) were added into Tl(C,N)-based cermets...The effects of Mo on the microstructure and mechanical properties of Ti(C,N)-based cermets with low Ni have been studied systematically. Different contents of Mo (4-12 wt.%) were added into Tl(C,N)-based cermets. Specimens were fabricated by conventional powder metallurgy and vacuum sintered at temperatures of 1440, 1450, and 1460℃ individually. The microstructure and fracture morphology were investigated by scanning electron microscope, and the mechanical properties such as transverse strength and hardness were measured. The results show that the microstructure is uniform and the thickness of rim phase is moderate when the content of Mo is 8 wt.%; the mechanical properties of the specimens sintered at 1450℃ are better than those sintered at 1440 and 1460℃. The integrated properties of transverse strength and hardness are the best when the content of Mo is 8 wt.% and the sintering temperature is 1450℃.展开更多
基金supported by Henan Province Key Research and Development and Promotion Project(Grant No.201ZP20220010).
文摘The effects of vanadium(V)on the microstructures and mechanical properties of the TiC cermet fusion welding interface were studied by adjusting the content of V in the self-developed flux-cored wires using metal inert gas arc(MIG)welding for surfacing on the TiC cermet.The results show that the increase in V content promotes the element diffusion between TiC cermet and weld metal.There are no de-fects observed in the interface,and the diffusion of elements refers to excellent metallurgical bonding.The shear strength of the fusion zone initially decreases and then increases with the increase in V content.The maximum shear strength of the TiC cermet/weld interface,reaching 552 MPa,occurred when the V content reached 0.65%.Meanwhile,the average hardness in the transition zone reached 488.2 HV0.2.
基金This work was supported by the National Natural Science Foundation of China (No.50074017/EO408)
文摘Effect of Mo and Mo2 C on the microstructure and properties of Ti(C,N)-based cermets was investigated in this article. The results have indicated that the weight percentage of Mo from 5 to 10 can reduce Ti(C,N) grain diameter and thickness of the rim, and Ti(C,N) grain can be wetted by Ni-Cu-Mo liquid so as to get small contiguity of Ti(C,N) grain. In that way, the transverse rupture strength of Ti(C,N)-based cermets has reached 1800-1900 MPa; the fracture toughness has been due to 16-18 MPa.m1/2. But 15 wt pct Mo was not more effective on Ti(C,N)-based cermets, because the thickness of the rim becomes larger. In the circumstance of Mo2 C, 5 wt pct Mo2 C was good for microstructure and properties of Ti(C,N)-based cermets, but 11 wt pct Mo2C has resulted in larger contiguity of Ti(C,N) grain and big Ti(C,N) grain diameter so as to reduce transverse rupture strength and fracture toughness. So that, the effect of Mo on Ti(C,N)-based cermets is better than Mo2C.
基金This work was financially supported by the National Natural Science Foundation of China (No. 50074017) the Natural Science Foundation of Hubei Province, China (No. 2003ABA092).
文摘The effects of Mo on the microstructure and mechanical properties of Ti(C,N)-based cermets with low Ni have been studied systematically. Different contents of Mo (4-12 wt.%) were added into Tl(C,N)-based cermets. Specimens were fabricated by conventional powder metallurgy and vacuum sintered at temperatures of 1440, 1450, and 1460℃ individually. The microstructure and fracture morphology were investigated by scanning electron microscope, and the mechanical properties such as transverse strength and hardness were measured. The results show that the microstructure is uniform and the thickness of rim phase is moderate when the content of Mo is 8 wt.%; the mechanical properties of the specimens sintered at 1450℃ are better than those sintered at 1440 and 1460℃. The integrated properties of transverse strength and hardness are the best when the content of Mo is 8 wt.% and the sintering temperature is 1450℃.