The lithium ion-conductive solid electrolyte in the oxide systems of Li2O-TiO2-SiO2-P2O5 and Li2O-TiO2-Al2O3-P2O5 was prepared by solid-state reaction. The electrolyte pellets by cold-pressing method is 13 mm in diame...The lithium ion-conductive solid electrolyte in the oxide systems of Li2O-TiO2-SiO2-P2O5 and Li2O-TiO2-Al2O3-P2O5 was prepared by solid-state reaction. The electrolyte pellets by cold-pressing method is 13 mm in diameter, about 1 mm in thickness. Phase identification and surface morphology of the products were carried out by X-ray diffraction and scanning electron microscopy. Ionic conductivity of the pellets was investigated through AC impedance. The results show that adulterate other cations can improve the ionic conductivity of the solid electrolyte. The maximum ionic conductivity in the samples is 9.912 × 10-4 S·cm-1 in the Li2O-TiO2-SiO2-P2O5 system.展开更多
The title compound (C5N5H41P2Mo5O30.5) was synthesized under hydrothermal condition and its crystal structure was determined by X-ray diffraction. It belongs to triclinic system, space group P , with a=9.9645(6), b=10...The title compound (C5N5H41P2Mo5O30.5) was synthesized under hydrothermal condition and its crystal structure was determined by X-ray diffraction. It belongs to triclinic system, space group P , with a=9.9645(6), b=10.8666(7), c=15.814(1)? α=71.482(3), β=88.528(2), γ=78.448(2)°, V=1589.4(2)3, Dc=2.510g/cm3, Z=2,μ=2.138mm-1,λ(MoKα) = 0.71073 ? F(000)=1180. The final R and wR were 0.0396 and 0.1052 for 6626 observed reflections with I ≥2σ(I), respectively. The result of the structure analysis indicates that the [Mo5O15(PO4) (HPO4)]5- anion in the title compound consists of five edge-sharing or corner-sharing MoO6 octahedra and two corner-sharing PO4 tetrahedra. Each MoO6 octahedron adopts distorted octahedral geometry.展开更多
文摘The lithium ion-conductive solid electrolyte in the oxide systems of Li2O-TiO2-SiO2-P2O5 and Li2O-TiO2-Al2O3-P2O5 was prepared by solid-state reaction. The electrolyte pellets by cold-pressing method is 13 mm in diameter, about 1 mm in thickness. Phase identification and surface morphology of the products were carried out by X-ray diffraction and scanning electron microscopy. Ionic conductivity of the pellets was investigated through AC impedance. The results show that adulterate other cations can improve the ionic conductivity of the solid electrolyte. The maximum ionic conductivity in the samples is 9.912 × 10-4 S·cm-1 in the Li2O-TiO2-SiO2-P2O5 system.
基金The paper is financially supported by NSF of Fujian Province (JA00137) by FPNSFC(E0110013)
文摘The title compound (C5N5H41P2Mo5O30.5) was synthesized under hydrothermal condition and its crystal structure was determined by X-ray diffraction. It belongs to triclinic system, space group P , with a=9.9645(6), b=10.8666(7), c=15.814(1)? α=71.482(3), β=88.528(2), γ=78.448(2)°, V=1589.4(2)3, Dc=2.510g/cm3, Z=2,μ=2.138mm-1,λ(MoKα) = 0.71073 ? F(000)=1180. The final R and wR were 0.0396 and 0.1052 for 6626 observed reflections with I ≥2σ(I), respectively. The result of the structure analysis indicates that the [Mo5O15(PO4) (HPO4)]5- anion in the title compound consists of five edge-sharing or corner-sharing MoO6 octahedra and two corner-sharing PO4 tetrahedra. Each MoO6 octahedron adopts distorted octahedral geometry.