锂硫电池由于其高能量密度、低成本效益被认为是最有前途的下一代电池体系之一.然而多硫化物的穿梭效应大幅降低了锂硫电池的循环稳定性和寿命,严重阻碍其实际应用.无机金属化合物材料改性的隔膜不仅能抑制多硫化锂(LiPS)的穿梭效应,其...锂硫电池由于其高能量密度、低成本效益被认为是最有前途的下一代电池体系之一.然而多硫化物的穿梭效应大幅降低了锂硫电池的循环稳定性和寿命,严重阻碍其实际应用.无机金属化合物材料改性的隔膜不仅能抑制多硫化锂(LiPS)的穿梭效应,其部分特殊的晶面还能加速多硫化物的氧化还原反应动力学.本文在罗盘状ZnS表面原位生长球状的MoO_(2),制备MoO_(2)/ZnS复合材料.MoO_(2)对多硫化物有着较强的吸附作用,ZnS有着良好的电导率,两者的复合可加速电子传导效率和氧化还原速率.以所制备的MoO_(2)/ZnS作为隔膜改性材料,锂硫电池在5 C的大电流密度下,经过1000次循环后仍可以保持690 mAh g^(-1)的放电比容量,平均每圈的容量衰减率仅为0.014%,表现出优异的循环性能和倍率性能.展开更多
It is rather essential to design glorious system with high CO_(2) adsorption capacity and electron migration efficiency for improving selective and effective CO_(2) reduction into solar fuels.Here,as-synthesized pheno...It is rather essential to design glorious system with high CO_(2) adsorption capacity and electron migration efficiency for improving selective and effective CO_(2) reduction into solar fuels.Here,as-synthesized phenolic resin spheres via suspension polymerization were carbonized and activated by water vapor to obtain activated carbon spheres(ACSs).Subsequently,Bi_(2)MoO_(6)/ACSs were prepared via hydrothermal-impregnated method.The systematical characterizations of samples,including XRD,XPS,SEM,EDX,DRS,BET,PL,CO_(2) adsorption isotherm,EIS and transient photocurrent,were analyzed.The results clearly demonstrated that Bi_(2)MoO_(6) with suitable oxidation reduction potentials and bandgap and ACSs with admirable CO_(2) adsorption and electrical conductivity not only enhanced separation efficiency of photoindued electron-hole pair,but also displayed as 1.8 times CO_(2) reduction activity to CO as single Bi_(2)MoO_(6) sample under Xe-lamp irradiation.Finally,a concerned photocatalytic CO_(2) reduction mechanism was proposed and investigated.Our findings should provide innovative guidance for designing a series of photocatalytic CO_(2) reduction materials with highly efficient and selective ability.展开更多
Micrometer-sized MoO2 hollow spheres were synthesized hydrothermally with ammonium heptamolybdate tetrahydrate as molybdenum source, Cetyltrimethylammonium bromide as structure-directing agent and C2H5OH as reducing a...Micrometer-sized MoO2 hollow spheres were synthesized hydrothermally with ammonium heptamolybdate tetrahydrate as molybdenum source, Cetyltrimethylammonium bromide as structure-directing agent and C2H5OH as reducing agent, respectively. The products were investigated by X-ray diffraction, thermo gravimetry and differential thermal analysis, scanning electron microscopy, transmission electron micraseopy and X-ray photoelectron spectroscopy. A morphology transition of ＂blocks-solid spheres-hollow spheres＂ during the growth procfess was observed and the possible mechanism for the formation of MoO2 samples was proposed to be through a microscale Kirkendall effcct.展开更多
文摘锂硫电池由于其高能量密度、低成本效益被认为是最有前途的下一代电池体系之一.然而多硫化物的穿梭效应大幅降低了锂硫电池的循环稳定性和寿命,严重阻碍其实际应用.无机金属化合物材料改性的隔膜不仅能抑制多硫化锂(LiPS)的穿梭效应,其部分特殊的晶面还能加速多硫化物的氧化还原反应动力学.本文在罗盘状ZnS表面原位生长球状的MoO_(2),制备MoO_(2)/ZnS复合材料.MoO_(2)对多硫化物有着较强的吸附作用,ZnS有着良好的电导率,两者的复合可加速电子传导效率和氧化还原速率.以所制备的MoO_(2)/ZnS作为隔膜改性材料,锂硫电池在5 C的大电流密度下,经过1000次循环后仍可以保持690 mAh g^(-1)的放电比容量,平均每圈的容量衰减率仅为0.014%,表现出优异的循环性能和倍率性能.
基金The authors are thankful to the National Natural Science Foundation of China(No.21978196,21676178,21706179)Shanxi Province Science Foundation for Youths(201801D211008).
文摘It is rather essential to design glorious system with high CO_(2) adsorption capacity and electron migration efficiency for improving selective and effective CO_(2) reduction into solar fuels.Here,as-synthesized phenolic resin spheres via suspension polymerization were carbonized and activated by water vapor to obtain activated carbon spheres(ACSs).Subsequently,Bi_(2)MoO_(6)/ACSs were prepared via hydrothermal-impregnated method.The systematical characterizations of samples,including XRD,XPS,SEM,EDX,DRS,BET,PL,CO_(2) adsorption isotherm,EIS and transient photocurrent,were analyzed.The results clearly demonstrated that Bi_(2)MoO_(6) with suitable oxidation reduction potentials and bandgap and ACSs with admirable CO_(2) adsorption and electrical conductivity not only enhanced separation efficiency of photoindued electron-hole pair,but also displayed as 1.8 times CO_(2) reduction activity to CO as single Bi_(2)MoO_(6) sample under Xe-lamp irradiation.Finally,a concerned photocatalytic CO_(2) reduction mechanism was proposed and investigated.Our findings should provide innovative guidance for designing a series of photocatalytic CO_(2) reduction materials with highly efficient and selective ability.
文摘Micrometer-sized MoO2 hollow spheres were synthesized hydrothermally with ammonium heptamolybdate tetrahydrate as molybdenum source, Cetyltrimethylammonium bromide as structure-directing agent and C2H5OH as reducing agent, respectively. The products were investigated by X-ray diffraction, thermo gravimetry and differential thermal analysis, scanning electron microscopy, transmission electron micraseopy and X-ray photoelectron spectroscopy. A morphology transition of ＂blocks-solid spheres-hollow spheres＂ during the growth procfess was observed and the possible mechanism for the formation of MoO2 samples was proposed to be through a microscale Kirkendall effcct.