A TIA1N/MoS2-Ti coating was developed to improve the tribological characteristics of a single TiAlN coating. The MoS2-Ti layer was deposited by a DC magnetron sputtering system on the hard TiAIN coated SKD-11 steel su...A TIA1N/MoS2-Ti coating was developed to improve the tribological characteristics of a single TiAlN coating. The MoS2-Ti layer was deposited by a DC magnetron sputtering system on the hard TiAIN coated SKD-11 steel substrate. The titanium content in the MoS2-Ti layer was 11.3 at.% determined by EPMA. The surface morphology was observed by FE-SEM. The TiAlN layer exhibited excellent adhesion and hardness. However, the deposition of an MoS2-Zi layer on the TRAIN led to a significant improvement in tribological properties without affecting the adhesion to the substrate. The MoS2-Ti layer significantly decreased the friction coefficient of the TiAIN coating, and the drop was 48% after MoS2-Ti deposition. Also, the MoS2-Ti layer remarkably decreased the wear rate of the TtA1N coating.展开更多
With constant enlargement of the application areas of the spherical plain bearings,higher quality lubrication of the bearings is required.To solve the lubricating problems of spherical plain bearings under high temper...With constant enlargement of the application areas of the spherical plain bearings,higher quality lubrication of the bearings is required.To solve the lubricating problems of spherical plain bearings under high temperature,high vacuum,high speed,heavy loads and strong oxidation conditions,it is urgent for us to develop more excellent self-lubricating technologies.In this paper,the bonded solid lubricant coatings,which use inorganic phosphate as the binder,the mixture of MoS2 and graphite with two different weight proportions as the solid lubricant,are prepared by spraying under three different spray gun pressures.The bonding strength tests on the coatings show that the best spraying pressure is 0.2 MPa and the better mixing proportion of MoS2 to Graphite is 3:1.Then for the radial spherical plain bearings with steel/steel friction pair,after the coatings are made on the inner ring outer surfaces,the friction coefficient,the wear loss and the friction temperature of the bearings under four oscillating frequencies are investigated by a self-made tribo-tester.The test results,SEM of the worn morphologies and EDS of worn areas show that tribological properties of the bearing are obviously improved by the bonded solid lubricant coatings.When sprayed under the spray gun pressure of 0.2 MPa,the bearings have better anti-friction and anti-wear properties than those sprayed under 0.1 MPa and 0.3 MPa.Further as proved from the XPS analysis,between the coating with 3:1 mixing ratio of MoS2 to Graphite and the coating with 1:1 ratio,the former has less oxidation occurred on the surface and therefore has better tribological characteristics than the latter.This paper provides a reference to developing a new product of the radial spherical plain bearings with high bonding strength,oxidation resistance and abrasion resistance.展开更多
MoS 2-based composite coatings were deposited with the nano-compound unbalanced plasma plating technique. The effects of processing parameters and working environments on the tribological properties of the coatings w...MoS 2-based composite coatings were deposited with the nano-compound unbalanced plasma plating technique. The effects of processing parameters and working environments on the tribological properties of the coatings were examined by the drilling experiments and XPS. The distances between substrate and Ti target, Ti content and deposition pressure were varied in order to determine the optimum conditions for producing lubricious, long-lasting MoS 2-based coatings. It is found that the tribological performance of TiN-MoS 2 coating decreases rapidly in humid air but the humid-resistant property of TiN-MoS 2/Ti coating improves evidently.It is indicated that the humid-resistantance property and the abrasion durability of MoS 2-based coatings can be enhanced markedly by adding Ti with a certain contents.展开更多
文摘A TIA1N/MoS2-Ti coating was developed to improve the tribological characteristics of a single TiAlN coating. The MoS2-Ti layer was deposited by a DC magnetron sputtering system on the hard TiAIN coated SKD-11 steel substrate. The titanium content in the MoS2-Ti layer was 11.3 at.% determined by EPMA. The surface morphology was observed by FE-SEM. The TiAlN layer exhibited excellent adhesion and hardness. However, the deposition of an MoS2-Zi layer on the TRAIN led to a significant improvement in tribological properties without affecting the adhesion to the substrate. The MoS2-Ti layer significantly decreased the friction coefficient of the TiAIN coating, and the drop was 48% after MoS2-Ti deposition. Also, the MoS2-Ti layer remarkably decreased the wear rate of the TtA1N coating.
基金Supported by National Natural Science Foundation of China(Grant No.51275155)Henan Provincial Science and Technology Innovation Outstanding Talent Project of China(Grant No.154200510013)Henan Provincial Innovation and Research Team of Science and Technology in Universities of China(Grant No.13IRTSTHN025)
文摘With constant enlargement of the application areas of the spherical plain bearings,higher quality lubrication of the bearings is required.To solve the lubricating problems of spherical plain bearings under high temperature,high vacuum,high speed,heavy loads and strong oxidation conditions,it is urgent for us to develop more excellent self-lubricating technologies.In this paper,the bonded solid lubricant coatings,which use inorganic phosphate as the binder,the mixture of MoS2 and graphite with two different weight proportions as the solid lubricant,are prepared by spraying under three different spray gun pressures.The bonding strength tests on the coatings show that the best spraying pressure is 0.2 MPa and the better mixing proportion of MoS2 to Graphite is 3:1.Then for the radial spherical plain bearings with steel/steel friction pair,after the coatings are made on the inner ring outer surfaces,the friction coefficient,the wear loss and the friction temperature of the bearings under four oscillating frequencies are investigated by a self-made tribo-tester.The test results,SEM of the worn morphologies and EDS of worn areas show that tribological properties of the bearing are obviously improved by the bonded solid lubricant coatings.When sprayed under the spray gun pressure of 0.2 MPa,the bearings have better anti-friction and anti-wear properties than those sprayed under 0.1 MPa and 0.3 MPa.Further as proved from the XPS analysis,between the coating with 3:1 mixing ratio of MoS2 to Graphite and the coating with 1:1 ratio,the former has less oxidation occurred on the surface and therefore has better tribological characteristics than the latter.This paper provides a reference to developing a new product of the radial spherical plain bearings with high bonding strength,oxidation resistance and abrasion resistance.
基金FundedbytheNationalNaturalScienceFoundationofChi na (No .90 2 0 6 0 2 2 )
文摘MoS 2-based composite coatings were deposited with the nano-compound unbalanced plasma plating technique. The effects of processing parameters and working environments on the tribological properties of the coatings were examined by the drilling experiments and XPS. The distances between substrate and Ti target, Ti content and deposition pressure were varied in order to determine the optimum conditions for producing lubricious, long-lasting MoS 2-based coatings. It is found that the tribological performance of TiN-MoS 2 coating decreases rapidly in humid air but the humid-resistant property of TiN-MoS 2/Ti coating improves evidently.It is indicated that the humid-resistantance property and the abrasion durability of MoS 2-based coatings can be enhanced markedly by adding Ti with a certain contents.
基金supported by the the National NaturalScience Foundation of China(No.51205001)Foundation for Young Talents in College of Anhui Province(No.2012SQRL083ZD)the Talent Innovation Fund of An-hui Polytechnic University(No.S05305)