含无机类富勒烯(IF)过渡族金属硫化物纳米复合涂层的环境摩擦磨损特性

采用固—气相反应、反应沉淀和溶剂热诱导法实现了IF-MoS2、IF-WS2纳米粉体的宏观量制备。分别用化学共沉积方法在硬铝基体上制备Ni-P-(IF-WS2)复合镀层,磁控溅射和激光溅射技术在硬铝合金和钛合金基体上制备(Ni,Mo)/IF-(Mo,W)S2梯度纳米复合涂层和IF-(Mo,W)S2/(Ni,Mo)-IF-(Mo,W)S2多层纳米复合涂层。用划痕仪、球—盘式摩擦仪评估纳米涂层的结合力及其在真空(10-2Pa)和大气中的摩擦磨损性能。Ni-P-(IF-MoS2)化学复合镀层的硬度、摩擦因数和磨损率明显低于Ni-P化学镀层。梯度和多层复合结构有利于涂层与合金基体结合力的提高。(Ni,Mo)/IF-(Mo,W)S2纳米梯度复合涂层和(Ni,Mo)-IF-(Mo,W)S2/IF-(Mo,W)S2纳米多层复合涂层在不同环境下都有低的摩擦因数和磨损率。含无机类富勒烯(IF-)WS2或MoS2的纳米复合涂层具有优良的环境稳定性。

Tribological performance of MoS2 coating on slipper pair in axial piston pump

This study investigates tribological performance of MoS2 coating on slipper pair in axial piston pump.Firstly,the MoS2 coating on the surface of slipper pair was prepared by atmospheric plasma spraying treatment technology.Secondly,the tribological characteristics of slipper pair under various working conditions were evaluated on ring-on-block tester in oil lubrication.The original and worn surfaces of the specimens were analyzed with scanning electron microscope and energy dispersive spectrometer,and then the wear morphologies of the MoS2 coatings were imaged by X-ray photoelectron spectroscopy.The experimental results showed that the friction coefficients of Cu-based materials with MoS2 coating decreased by about 0.05 at 800 N.Especially,when the external load was set to 800 N,the wear rate of the ZY331608 decreased by about 16.4%after the substrates were treated by the MoS2 coating,which exhibited excellent anti-friction and wear resistance.The formation of the MoS2 lubricating film could be classified into four stages,including the initial friction stage,anchoring stage of MoS2 on friction surface,covering stage of the sliding surface by MoS2 and the formation stage of MoS2 film.The dominating wear mechanisms of Cu-based materials with MoS2 coating were adhesive wear and abrasive wear accompanied with oxidative wear.

Effects of copper-coated MoS_(2) on friction performance of bronze-graphite-MoS_(2) self-lubricating materials

Two kinds of bronze-graphite-MoS_(2) self-lubricating materials with copper-coated MoS_(2) and uncoated MoS_(2) were prepared by powder metallurgy.Friction and wear experiments were carried out under 4 N and 10 N loads respectively,and the effects of copper-coated MoS_(2) on the friction performances of the materials were studied.Results showed that the way of copper-coated on the surface of MoS_(2) could reinforce the bonding between MoS_(2) and matrix,and inhibited the formation of MoO_(2).Moreover,both materials formed a MoS_(2) lubricating film on the surface during the friction process.While the lubricating film formed after copper coating on MoS_(2) was thicker and had uneven morphology,it was more conducive to improving the friction performance of the material.Compared with conventional materials,the wear rate of copper-coated materials was reduced by one order of magnitude,and the friction coefficient was also reduced by 22.44% and 22.53%,respectively,when sliding under 4 N and 10 N loads.It shows that copper-coated MoS_(2)can improve friction properties of bronze-graphite-MoS_(2)self-lubricating materials furtherly.

Effects of combined additions of SiO2 and MoS2 nanoparticles as lubricant additive on the tribological properties of AZ31 magnesium alloy

The tribological properties of combinative addition of nano-MoS2 and nano-SiO2 to the base oil have been investigated with a reciprocating ball-on-plate tribotester for magnesium alloy-steel contacts. The results demonstrate that the optimum mass ratio of nano-SiO2 to nano-MoS2 is 0.25：0.75. The optimum combinative addition into the base oil reduces the friction coefficient by 43.8% and the surface roughness （Sa） by 31.7% when compared to that found with the base oil. Meanwhile, the combinative addition of nano-MoS2 and nano-SiO〉 in comparison with single nanoparticles addition, is more pronounced in terms of the lubrication film stability. The excellent tribological properties of the SiO2/MoS2 combinations are attributed to the formation of physical adsorption films and tribochemical products during the rubbing process and the micro-cooperation of various nano- particles with different shapes and lubrication mechanisms.