Observation was carried out of the structure of sulphuric,oxalic or phosphoric film on Al after treatment of reanodizing and electrolytic depositing lubricant in (NH_4)_2MoS_4 solution,as well as of the deposited prod...Observation was carried out of the structure of sulphuric,oxalic or phosphoric film on Al after treatment of reanodizing and electrolytic depositing lubricant in (NH_4)_2MoS_4 solution,as well as of the deposited products by means of EMPA,TEM and energy spectro-scopic analysis.The deposited products are mixture of compounds of S and Mo rather than single MoS_2 and most of them dcposited near the surface layer of the film.Some regular long pores without barrier layer occurred in the film,but the regular fine channels without relation to the structural element parameters of original anodized film were found in the thickened barrier layer of phosphoric film.Sulphur may be remained as Mo sulphide in the film during heating under Ar protective environment.展开更多
Series of TiO 2-ZnO heterojunction composite films with different n（Zn）/n（Ti） ratios were prepared by UDP450 magnetron sputter ion plating equipment, and the mole ratio of Zn to Ti was controlled by adjusting the ...Series of TiO 2-ZnO heterojunction composite films with different n（Zn）/n（Ti） ratios were prepared by UDP450 magnetron sputter ion plating equipment, and the mole ratio of Zn to Ti was controlled by adjusting the current values of sputtering target. The effects of n（Zn）/n（Ti） on the microstructures of TiO2-ZnO films were investigated by SEM, AFM, Raman and XPS, and their photocatalytic decomposition of methyl orange solutions was evaluated. The results show that an increase in n（Zn）/n（Ti） typically results in a decrease in the grain size of composite films firstly and then an increase of grain size, while an increase in n（Zn）/n（Ti） leads to an increase in film roughness firstly and then a decrease in film roughness. Both grain size and roughness of TiO2-ZnO films reach the maximum and minimum at n（Zn）/n（Ti） of 1/9.3, respectively. The n（Zn）/n（Ti） shows little effect on the valences of Zn and Ti elements, which mainly exist in the form of TiO2 and ZnO phases. The n（Zn）/n（Ti） has influence on the amount of anatase/rutile TiO2 heterojunction in the film. With increase of the n（Zn）/n（Ti）, the absorption intensity of the composite film increases and the absorption region extends to 450 nm, which is redshifted as much as 150 nm in comparison with the pure TiO2 films. However, the photocatalytic abilities of heterogeneous composite films do not depend on the n（Zn）/n（Ti） but rather on the microstructures of the TiO2-ZnO composite films. Degradation rate of the film reaches the maximum and the photocatalytic decomposition of pollutants works best when n（Zn）/n（Ti）=1：9.3.展开更多
Slickwater-based fracturing fluid has recently garnered significant attention as the major fluid for volumetric fracturing;however,lots of challenges and limitations such as low viscosity,poor salt tolerance,and possi...Slickwater-based fracturing fluid has recently garnered significant attention as the major fluid for volumetric fracturing;however,lots of challenges and limitations such as low viscosity,poor salt tolerance,and possible formation damage hinder the application of the conventional simple slickwater-based fracturing fluid.In addition,nanomaterials have proven to be potential solutions or improvements to a number of challenges associated with the slickwater.In this paper,molybdenum disulfide(MoS_(2))nanosheets were chemically synthesized by hydrothermal method and applied to improve the performance of conventional slickwater-based fracturing fluid.Firstly,the microstructure characteristics and crystal type of the MoS_(2)nanosheets were analyzed by SEM,EDS,TEM,XPS,and Raman spectroscopy techniques.Then,a series of evaluation experiments were carried out to compare the performance of MoS_(2)nanosheet-modified slickwater with the conventional slickwater,including rheology,drag reduction,and sand suspension.Finally,the enhanced imbibition capacity and potential mechanism of the nanosheet-modified slickwater were systematically investigated.The results showed that the self-synthesized MoS_(2)nanosheets displayed a distinct ultrathin flake-like morphology and a lateral size in the range of tens of nanometers.In the nano-composites,each MoS_(2)nanosheet plays the role of cross-linking point,so as to make the spatial structure of the entire system more compact.Moreover,nanosheet-modified slickwater demonstrates more excellent properties in rheology,drag reduction,and sand suspension.The nanosheet-modified slickwater has a higher apparent viscosity after shearing 120 min under 90℃ and 170 s^(−1).The maximum drag reduction rate achieved 76.3%at 20℃,and the sand settling time of proppants with different mesh in the nano-composites was prolonged.Spontaneous imbibition experiments showed that the gel-breaking fluid of nanosheet-modified slickwater exhibited excellent capability of oil-detaching,and increase the oil recovery to∼35.43%.By observing and analyzing the interfacial behavior of MoS_(2)nanosheets under stimulated reservoir conditions,it was found that the presence of an interfacial tension gradient and the formation of a climbing film may play an essential role in the spontaneous imbibition mechanism.This work innovatively uses two-dimensional MoS_(2)nanosheets to modify regular slickwater and confirms the feasibility of flake-like nanomaterials to improve the performance of slickwater.The study also reveals the underlying mechanism of enhanced imbibition efficiency of the nano-composites.展开更多
In order to clarify the respective role of the UV light, catalyst, external bias as well as their combined effects on the photodegradation process and to clarify the photocatalytic mechanism under different experiment...In order to clarify the respective role of the UV light, catalyst, external bias as well as their combined effects on the photodegradation process and to clarify the photocatalytic mechanism under different experimental conditions, a series of experiments were conducted in a shallow pond photoreactor with an effective volume of 100 mL using TiO 2/Ti thin film prepared by anodization as photocatalyst. A 300W UV lamp( E max =365 nm)was used as side light source. The effect of light intensity on photocatalysis was also conducted. The results show that photocatalytic oxidation is an effective method for phenol removal from waters. The degradation rate can be improved by applying an anodic bias to the TiO 2/Ti film electrode, phenol can not be decomposed under only 365 nm UV light irradiation even in the presence of hydrogen peroxide. In the range of our research, the phenol removal rate can be described in terms of pseudo first order kinetics.展开更多
In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performanc...In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performance reliability was examined. The prepared TiO2/Ti composite films showed high photocatalytic activity in the degradation of methylene blue solution. It is obvious that? TiO2/Ti composite films have antibacterial activity under UV irradiation.展开更多
In order to prolong the service life of piston rings of heavy vehicle engine and decrease the friction and wear of piston rings and cylinder liner,CrMoN/MoS_2 multilayer films were deposited on the surface of rings by...In order to prolong the service life of piston rings of heavy vehicle engine and decrease the friction and wear of piston rings and cylinder liner,CrMoN/MoS_2 multilayer films were deposited on the surface of rings by magnetron sputtering and low temperature ion sulfuration.FESEM equipped with EDX was adopted to analyze the compositions and morphologies of surface,cross-section,and wear scars of the multilayer films.The nano-hardness and Young＇s modulus of the films were measured by a nano tester.Tribologicalproperties of the films were tested by an SRV~174;4 wear tester.The experimentalresults indicate that the structures of the multilayer films are dense and compact.The films possess nano hardness value of approximately 26.7 GPa and superior ability of plastic deformation resistance.The multilayer films can activate solid lubricating,and possess an excellent antifriction and wear resistance under the conditions of heavy load,high frequency,high temperature,and dynamic load.展开更多
文摘Observation was carried out of the structure of sulphuric,oxalic or phosphoric film on Al after treatment of reanodizing and electrolytic depositing lubricant in (NH_4)_2MoS_4 solution,as well as of the deposited products by means of EMPA,TEM and energy spectro-scopic analysis.The deposited products are mixture of compounds of S and Mo rather than single MoS_2 and most of them dcposited near the surface layer of the film.Some regular long pores without barrier layer occurred in the film,but the regular fine channels without relation to the structural element parameters of original anodized film were found in the thickened barrier layer of phosphoric film.Sulphur may be remained as Mo sulphide in the film during heating under Ar protective environment.
基金Project (2010JQ6008) supported by the Natural Science Foundation of Shaanxi Province,China
文摘Series of TiO 2-ZnO heterojunction composite films with different n（Zn）/n（Ti） ratios were prepared by UDP450 magnetron sputter ion plating equipment, and the mole ratio of Zn to Ti was controlled by adjusting the current values of sputtering target. The effects of n（Zn）/n（Ti） on the microstructures of TiO2-ZnO films were investigated by SEM, AFM, Raman and XPS, and their photocatalytic decomposition of methyl orange solutions was evaluated. The results show that an increase in n（Zn）/n（Ti） typically results in a decrease in the grain size of composite films firstly and then an increase of grain size, while an increase in n（Zn）/n（Ti） leads to an increase in film roughness firstly and then a decrease in film roughness. Both grain size and roughness of TiO2-ZnO films reach the maximum and minimum at n（Zn）/n（Ti） of 1/9.3, respectively. The n（Zn）/n（Ti） shows little effect on the valences of Zn and Ti elements, which mainly exist in the form of TiO2 and ZnO phases. The n（Zn）/n（Ti） has influence on the amount of anatase/rutile TiO2 heterojunction in the film. With increase of the n（Zn）/n（Ti）, the absorption intensity of the composite film increases and the absorption region extends to 450 nm, which is redshifted as much as 150 nm in comparison with the pure TiO2 films. However, the photocatalytic abilities of heterogeneous composite films do not depend on the n（Zn）/n（Ti） but rather on the microstructures of the TiO2-ZnO composite films. Degradation rate of the film reaches the maximum and the photocatalytic decomposition of pollutants works best when n（Zn）/n（Ti）=1：9.3.
基金This research was financially supported by the National Natural Science Foundation of China(Grant Nos.52004306 and 52174045)the Strategic Cooperation Technology Projects of CNPC and CUPB(Grant Nos.ZLZX2020-01 and ZLZX2020-02)the National Sciencea and Technology Major Projects of China(Grant Nos.2016ZX05030005and 2016ZX05051003).
文摘Slickwater-based fracturing fluid has recently garnered significant attention as the major fluid for volumetric fracturing;however,lots of challenges and limitations such as low viscosity,poor salt tolerance,and possible formation damage hinder the application of the conventional simple slickwater-based fracturing fluid.In addition,nanomaterials have proven to be potential solutions or improvements to a number of challenges associated with the slickwater.In this paper,molybdenum disulfide(MoS_(2))nanosheets were chemically synthesized by hydrothermal method and applied to improve the performance of conventional slickwater-based fracturing fluid.Firstly,the microstructure characteristics and crystal type of the MoS_(2)nanosheets were analyzed by SEM,EDS,TEM,XPS,and Raman spectroscopy techniques.Then,a series of evaluation experiments were carried out to compare the performance of MoS_(2)nanosheet-modified slickwater with the conventional slickwater,including rheology,drag reduction,and sand suspension.Finally,the enhanced imbibition capacity and potential mechanism of the nanosheet-modified slickwater were systematically investigated.The results showed that the self-synthesized MoS_(2)nanosheets displayed a distinct ultrathin flake-like morphology and a lateral size in the range of tens of nanometers.In the nano-composites,each MoS_(2)nanosheet plays the role of cross-linking point,so as to make the spatial structure of the entire system more compact.Moreover,nanosheet-modified slickwater demonstrates more excellent properties in rheology,drag reduction,and sand suspension.The nanosheet-modified slickwater has a higher apparent viscosity after shearing 120 min under 90℃ and 170 s^(−1).The maximum drag reduction rate achieved 76.3%at 20℃,and the sand settling time of proppants with different mesh in the nano-composites was prolonged.Spontaneous imbibition experiments showed that the gel-breaking fluid of nanosheet-modified slickwater exhibited excellent capability of oil-detaching,and increase the oil recovery to∼35.43%.By observing and analyzing the interfacial behavior of MoS_(2)nanosheets under stimulated reservoir conditions,it was found that the presence of an interfacial tension gradient and the formation of a climbing film may play an essential role in the spontaneous imbibition mechanism.This work innovatively uses two-dimensional MoS_(2)nanosheets to modify regular slickwater and confirms the feasibility of flake-like nanomaterials to improve the performance of slickwater.The study also reveals the underlying mechanism of enhanced imbibition efficiency of the nano-composites.
文摘In order to clarify the respective role of the UV light, catalyst, external bias as well as their combined effects on the photodegradation process and to clarify the photocatalytic mechanism under different experimental conditions, a series of experiments were conducted in a shallow pond photoreactor with an effective volume of 100 mL using TiO 2/Ti thin film prepared by anodization as photocatalyst. A 300W UV lamp( E max =365 nm)was used as side light source. The effect of light intensity on photocatalysis was also conducted. The results show that photocatalytic oxidation is an effective method for phenol removal from waters. The degradation rate can be improved by applying an anodic bias to the TiO 2/Ti film electrode, phenol can not be decomposed under only 365 nm UV light irradiation even in the presence of hydrogen peroxide. In the range of our research, the phenol removal rate can be described in terms of pseudo first order kinetics.
文摘In this work, TiO2/Ti composite films were fabricated by 2-setp MCT and the following high temperature oxidation. Antibacterial activity of the composite films treated by ultrasonic cleaning to increase the performance reliability was examined. The prepared TiO2/Ti composite films showed high photocatalytic activity in the degradation of methylene blue solution. It is obvious that? TiO2/Ti composite films have antibacterial activity under UV irradiation.
基金Funded by the National Natural Science Foundation of China(No.50901089)the Project supported by Army Important Researches(No.2012ZB02)
文摘In order to prolong the service life of piston rings of heavy vehicle engine and decrease the friction and wear of piston rings and cylinder liner,CrMoN/MoS_2 multilayer films were deposited on the surface of rings by magnetron sputtering and low temperature ion sulfuration.FESEM equipped with EDX was adopted to analyze the compositions and morphologies of surface,cross-section,and wear scars of the multilayer films.The nano-hardness and Young＇s modulus of the films were measured by a nano tester.Tribologicalproperties of the films were tested by an SRV~174;4 wear tester.The experimentalresults indicate that the structures of the multilayer films are dense and compact.The films possess nano hardness value of approximately 26.7 GPa and superior ability of plastic deformation resistance.The multilayer films can activate solid lubricating,and possess an excellent antifriction and wear resistance under the conditions of heavy load,high frequency,high temperature,and dynamic load.