To broaden the application of SiO_(2) sol-bonded castables,using micro-or nano-Al_(2)O_(3) powder and SiO_(2) gel powder as the main raw materials,the effects of CaO impurity on the formation of mullite by the reactio...To broaden the application of SiO_(2) sol-bonded castables,using micro-or nano-Al_(2)O_(3) powder and SiO_(2) gel powder as the main raw materials,the effects of CaO impurity on the formation of mullite by the reaction of Al_(2)O_(3) and SiO_(2) at different temperatures(1350,1400,1500,and 1600℃)in different atmospheres(oxidation atmosphere and reduction atmosphere)were studied.The results show that in the oxidizing atmosphere,the introduction of CaO can promote the formation of mullite.When the temperature increases from 1350℃to 1600℃,the amount of mullite formed gradually increases.In the reducing atmosphere,the introduction of CaO is not conducive to the formation of mullite,and the amount of mullite decreases with the increasing temperature.The smaller the particle size of Al_(2)O_(3),the more easily it reacts with SiO_(2) gel powder to form mullite.展开更多
Mullite thermal storage ceramics were prepared by low-cost calcined bauxite and kaolin.The phase composition,microstructure,high temperature resistance and thermophysical properties were characterized by modern testin...Mullite thermal storage ceramics were prepared by low-cost calcined bauxite and kaolin.The phase composition,microstructure,high temperature resistance and thermophysical properties were characterized by modern testing techniques.The experimental results indicate that sample A3(bauxite/kaolin ratio of 5:5)sintered at 1620℃has the optimum comprehensive properties,with bulk density of 2.83 g·cm^(-3)and bending strength of 155.44 MPa.After 30 thermal shocks(1000℃-room temperature,air cooling),the bending strength of sample A3 increases to 166.15 MPa with an enhancement rate of 6.89%,the corresponding thermal conductivity and specific heat capacity are 3.54 W·(m·K)^(-1)and 1.39 kJ·(kg·K)^(-1)at 800℃,and the thermal storage density is 1096 kJ·kg^(-1)(25-800 mullite ceramics;sintering properties;high-temperature thermal storage;thermal shock resistance).Mullite forms a dense and continuous interlaced network microstructure,which endows the samples high thermal storage density and high bending strength,but the decrease of bauxite/kaolin ratio leads to the decrease of mullite content,which reduces the properties of the samples.展开更多
In order to improve the high-temperature performance of mullite ceramic materials,mullite ceramic bodies were placed in closed containers with AlF_(3)·3H_(2)O powder and kept at 1 600 ℃ for 6 h.AlF_(3)·3H_(...In order to improve the high-temperature performance of mullite ceramic materials,mullite ceramic bodies were placed in closed containers with AlF_(3)·3H_(2)O powder and kept at 1 600 ℃ for 6 h.AlF_(3)·3H_(2)O reacts with O_(2) to produce gaseous compounds AlOF and F,which penetrate into the bodies,promote Al2O3 and SiO_(2) to form mullite whiskers,and strengthen the mullite ceramic materials.The results show that the mullite ceramics have enhanced hot strength,increased bulk density and declined apparent porosity by adding a certain amount of AlF_(3)·3H_(2)O in a closed container.When the addition of AlF_(3)·3H_(2)O is 6%,the bulk density of the ceramic material reaches the maximum and the apparent porosity is the lowest;and when the addition of AlF_(3)·3H_(2)O is 8%,the hot strength of the material is the highest.展开更多
Microporous mullite aggregates were prepared from bauxite by dry pressing and firing at 1700℃for 3 h with corn starch,PMMA microspheres or rice husk powder as the porogenic agent.The effects of some porogenic agents ...Microporous mullite aggregates were prepared from bauxite by dry pressing and firing at 1700℃for 3 h with corn starch,PMMA microspheres or rice husk powder as the porogenic agent.The effects of some porogenic agents and their additions(mass fraction of 0,5%,10%,15%and 20%,respectively)on the properties of the microporous mullite aggregates were analyzed by XRD,SEM and Image-Pro Plus software.The results show that the comprehensive performance of the sample with 10%rice husk powder is the best:the closed porosity is 7.1%;the bulk density is 2.63 g·cm^(-3);the compressive strength is 122 MPa;the median pore size is 15.16μm;and the thermal conductivity at 500℃is 2.30 W·m^(-1)·K^(-1).展开更多
用挤压铸造方法制备了Mullite/Al Cu Si复合材料。用硬度 (HB)测试仪、差示扫描量热仪 (DSC)和显微镜研究含Si量变化和Mullite纤维对Al Cu Si合金时效硬化行为的影响 ;元素Si、Mullite纤维以及二者同时存在对Al Cu Si合金时效析出序列...用挤压铸造方法制备了Mullite/Al Cu Si复合材料。用硬度 (HB)测试仪、差示扫描量热仪 (DSC)和显微镜研究含Si量变化和Mullite纤维对Al Cu Si合金时效硬化行为的影响 ;元素Si、Mullite纤维以及二者同时存在对Al Cu Si合金时效析出序列的影响。结果表明 :Si和Mullite纤维明显抑制了Al Cu合金GP区的形成 ;随着含Si量增加 ,Al Cu Si合金的时效硬化过程加快 ;Mullite纤维对Al Cu和Al Cu Si合金的时效硬化过程都具有加速作用 ,同时提高了基体合金的时效硬度 ,但相对而言 ,Mullite纤维对无Si的Al Cu合金的时效硬化加速作用更为明显一些。展开更多
基金This work was financially supported by National Natural Science Foundation of China(Nos.52172031 and 51872266).
文摘To broaden the application of SiO_(2) sol-bonded castables,using micro-or nano-Al_(2)O_(3) powder and SiO_(2) gel powder as the main raw materials,the effects of CaO impurity on the formation of mullite by the reaction of Al_(2)O_(3) and SiO_(2) at different temperatures(1350,1400,1500,and 1600℃)in different atmospheres(oxidation atmosphere and reduction atmosphere)were studied.The results show that in the oxidizing atmosphere,the introduction of CaO can promote the formation of mullite.When the temperature increases from 1350℃to 1600℃,the amount of mullite formed gradually increases.In the reducing atmosphere,the introduction of CaO is not conducive to the formation of mullite,and the amount of mullite decreases with the increasing temperature.The smaller the particle size of Al_(2)O_(3),the more easily it reacts with SiO_(2) gel powder to form mullite.
基金Funded by the National Key Research and Development Program of Science and Technology of China(No.2018YFB1501002)。
文摘Mullite thermal storage ceramics were prepared by low-cost calcined bauxite and kaolin.The phase composition,microstructure,high temperature resistance and thermophysical properties were characterized by modern testing techniques.The experimental results indicate that sample A3(bauxite/kaolin ratio of 5:5)sintered at 1620℃has the optimum comprehensive properties,with bulk density of 2.83 g·cm^(-3)and bending strength of 155.44 MPa.After 30 thermal shocks(1000℃-room temperature,air cooling),the bending strength of sample A3 increases to 166.15 MPa with an enhancement rate of 6.89%,the corresponding thermal conductivity and specific heat capacity are 3.54 W·(m·K)^(-1)and 1.39 kJ·(kg·K)^(-1)at 800℃,and the thermal storage density is 1096 kJ·kg^(-1)(25-800 mullite ceramics;sintering properties;high-temperature thermal storage;thermal shock resistance).Mullite forms a dense and continuous interlaced network microstructure,which endows the samples high thermal storage density and high bending strength,but the decrease of bauxite/kaolin ratio leads to the decrease of mullite content,which reduces the properties of the samples.
基金supported by the National Natural Science Foundation of ChinaKey Projects of Henan United Fund(NSFCNo.U1904217).
文摘In order to improve the high-temperature performance of mullite ceramic materials,mullite ceramic bodies were placed in closed containers with AlF_(3)·3H_(2)O powder and kept at 1 600 ℃ for 6 h.AlF_(3)·3H_(2)O reacts with O_(2) to produce gaseous compounds AlOF and F,which penetrate into the bodies,promote Al2O3 and SiO_(2) to form mullite whiskers,and strengthen the mullite ceramic materials.The results show that the mullite ceramics have enhanced hot strength,increased bulk density and declined apparent porosity by adding a certain amount of AlF_(3)·3H_(2)O in a closed container.When the addition of AlF_(3)·3H_(2)O is 6%,the bulk density of the ceramic material reaches the maximum and the apparent porosity is the lowest;and when the addition of AlF_(3)·3H_(2)O is 8%,the hot strength of the material is the highest.
文摘Microporous mullite aggregates were prepared from bauxite by dry pressing and firing at 1700℃for 3 h with corn starch,PMMA microspheres or rice husk powder as the porogenic agent.The effects of some porogenic agents and their additions(mass fraction of 0,5%,10%,15%and 20%,respectively)on the properties of the microporous mullite aggregates were analyzed by XRD,SEM and Image-Pro Plus software.The results show that the comprehensive performance of the sample with 10%rice husk powder is the best:the closed porosity is 7.1%;the bulk density is 2.63 g·cm^(-3);the compressive strength is 122 MPa;the median pore size is 15.16μm;and the thermal conductivity at 500℃is 2.30 W·m^(-1)·K^(-1).
文摘用挤压铸造方法制备了Mullite/Al Cu Si复合材料。用硬度 (HB)测试仪、差示扫描量热仪 (DSC)和显微镜研究含Si量变化和Mullite纤维对Al Cu Si合金时效硬化行为的影响 ;元素Si、Mullite纤维以及二者同时存在对Al Cu Si合金时效析出序列的影响。结果表明 :Si和Mullite纤维明显抑制了Al Cu合金GP区的形成 ;随着含Si量增加 ,Al Cu Si合金的时效硬化过程加快 ;Mullite纤维对Al Cu和Al Cu Si合金的时效硬化过程都具有加速作用 ,同时提高了基体合金的时效硬度 ,但相对而言 ,Mullite纤维对无Si的Al Cu合金的时效硬化加速作用更为明显一些。