Formation and Growth of Granular Carbides in Multiple Alloying Wear Resistant Cast Iron Containing RE Through Hot Deformation

The granular carbides formed from hot deformation in multiple alloying wear resistant cast iron were studied through the observation by means of optical microscope, SEM and TEM. The experimental results show that carbides with large size are formed from original short rhabdoid carbides existing in cast, those with small size directly nucleate in the matrix. Carbides with the size between the above are formed from precipitation induced by hot deformation. The bigger the deformation is, the larger the number of microsized granular carbides is. The mechanisms of nucleation and growth of granular carbides and the function of RE were discussed.

Ca－Ni－Ti－Bi多元微合金化铸铁电弧冷焊同质焊条的研究

通过Ｃａ－Ｎｉ－Ｔｉ－Ｂｉ多元合金的复合加入，研制出灰铁芯和球铁芯两种铸铁电弧冷焊条。对焊补区性能的测试结果表明：两种焊条获得的结合强度分别为ＨＴσｂ≥２００ＭＰａ，ＱＴσｂ≥４５０ＭＰａ，δ≮６％，硬度和颜色与母材一致；焊缝为铸铁组织，抗裂性好；熔合区基本无白口，机械加工性能良好。

微合金化多元合金高铬铸铁破碎机板锤的研制与应用

研制了一种微合金化多元合金高铬铸铁耐磨材料 ,试验了不同奥氏体化加热温度和不同温度回火热处理对组织和性能的影响。结果表明 ,高铬铸铁奥氏体化加热温度为 960℃时空冷铸件具有较高的硬度 ,2 0 0～ 40 0℃回火高铬铸铁具有良好的韧性。提出了高铬铸铁板锤的最佳热处理工艺 。

Ca-Ni-Ti-Bi多元微合金化铸铁同质气焊丝的焊接性能研究

采用多元微合金化铸铁同质气焊丝对HT250铸铁板材进行了气焊研究,测试和分析了焊接接头的硬度、抗裂性和机械加工性能。研究结果表明:接头颜色和硬度与母材一致,焊缝组织为珠光体加小团状石墨,抗裂性能良好,机械加工性能优良。

轻稀土镁复合球化、孕育处理工艺在轧辊生产中的应用

叙述生产轧辊类超厚大断面球墨铸铁件所用的轻稀土镁球化剂、孕育剂和复合球化、孕育处理过程及其对原铁水的要求,同时介绍了所生产轧辊的组织、性能和良好的使用效果。

离心铸造钨合金铸铁辊环的研究

研究了复合变质处理工艺，离心铸造工艺，软化退火工艺和淬火加回火工艺对多元钨合金铸铁辊环组织和性能的影响，结果表明，离心铸造钨合金铸铁辊环具有硬度高、硬度均匀性好、淬硬层深和生产工艺简单等特点，是取代高铬铸铁辊坏和镍铬合金铸铁辊环的理想产品。