Effects of molybdenum on the microstructure and mechanical properties of Ti(C,N)-based cermets with low Ni

The effects of Mo on the microstructure and mechanical properties of Ti（C,N）-based cermets with low Ni have been studied systematically. Different contents of Mo （4-12 wt.%） were added into Tl（C,N）-based cermets. Specimens were fabricated by conventional powder metallurgy and vacuum sintered at temperatures of 1440, 1450, and 1460℃ individually. The microstructure and fracture morphology were investigated by scanning electron microscope, and the mechanical properties such as transverse strength and hardness were measured. The results show that the microstructure is uniform and the thickness of rim phase is moderate when the content of Mo is 8 wt.%; the mechanical properties of the specimens sintered at 1450℃ are better than those sintered at 1440 and 1460℃. The integrated properties of transverse strength and hardness are the best when the content of Mo is 8 wt.% and the sintering temperature is 1450℃.

Effect of VC addition on the microstructure and properties of Ti(C,N)-based nano cermets

In this paper, Ti（C,N）-based nano cermets were prepared by nano particles, and the effect of VC addition on the micmstructure and properties of Ti（C,N）-based nano cermets was investigated. The results showed that there existed black-core grayish-rim strucmre as well as gray-core grayish-rim structure in VC-doped Ti（C,N）-based nano cermets. With the increase of VC addition, the number of gray cores in- creased, the lattice parameter of Ti（C,N） phase increased, the grain size decreased, the hardness and fracture toughness of Ti（C,N）-based nano cermets were enhanced, and nearly full densification could be achieved. However, excessive addition of VC to 1 wt% resulted in slight decrease in hardness and fracture toughness. Some deep dimples were found in the fracture surface of cermets with VC addition, which corresponded to ductile fracture.

Microstructure and cutting performance of Ti(C, N)-based cermets heat-treated in nitrogen

Ti（C, N）-based cermets were treated using hot isostatic pressing （HIP） at 1423 K in nitrogen. The microstructures compared with the as-sintered cermets were investigated using X-ray diffraction, scanning electron microscopy, transmission electron microscopy, energy-dispersive X-ray analysis, and electron microprobe analysis. It was found that high nitrogen activity in the surface zone resulted in the formation of gradient structure. Approximately 20-1am-deep, nitrogen-rich and titanium-rich hard surface zone was introduced by the heat treatment. The nitrogen activity was the driving force that caused the transportation of the atoms through the binder, titanium towards the surface, and tungsten and molybdenum inwards. In the surface zone, the particle size became fine, the inner rim disappeared, and the volume fraction of the outer rim and the binder phase considerably reduced. Small grains of TiN, WC, Mo2C, and nitrogen-rich carbonitlide phases formed in the surface zone during the heat treatment, improving the tlibological property of the heat-treated cermet.

Comparative study of the fabrication of ultrafine Ti(C,N)-based cermets by spark plasma sintering and conventional vacuum sintering

Spark plasma sintering (SPS) and conventional vacuum sintering (VS) wereemployed to fabricate ultrafine Ti(C,N)-based cermets. The shrinkage behavior, microstracture, andporosity and mechanical properties of the samples fabricated by SPS were compared with those of thesamples sintered by VS using optical microscopy, scanning electron microscopy, universal testingmachine, and rockwell tester. The results are as follows: (1) The shrinkage process occurred mainlyin the range of 1000-1300 deg C during the VS process, and only a 0.2 percent linear shrinkage ratioappeared below 800 deg C; during the SPS process, a 60 percent dimensional change occurred below800 deg C as a result of pressure action. (2) By utilizing the SPS technique, it is difficult forobtaining fully dense Ti(C,N)-based cermets. Due to the much existence of pores and un-combinedcarbon, the mechanical properties of the sintered samples by SPS are inferior to sintered ones byVS. (3) grain size of the samples sintered by SPS is still below 0.5 urn, but not by VS; because oflow sintering temperature, there are no typical core/rim structures formed in the sintered samplesby SPS1; the main microstructures of the sintered samples by SPS2 are a white core/grey shellstructure, whereas by VS show a typical black core/grey shell structure.

Effect of Mo_2C on electrochemical corrosion behavior of Ti(C,N)-based cermets

The electrochemical corrosion behavior of Ti(C,N)-based cermets with different Mo2C additions was investigated in freely aerated 10% H2SO4 and potentiodynamic polarization of all the materials was conducted from -0.5 to 1.5 V. There are two passive regions for all polarization curves. The first should be attributed to passive film formation due to Ti(C,N), while the second may be due to the presence of Ni. Corrosion current density increases with Mo2C content increasing, from 2.06×10-3 to 6.70×10-3 mA/cm2 . It is indicated that the corrosion resistance of Ti(C,N)-based cermets decreases with the increase of Mo2C addition. A skeleton of Ti(C,N) gains is observed after dissolution of Ni. The inner rim of cermets, rich in Mo2C, is corroded along with Ni binder and is more serious with the increase of Mo2C content. The secondary carbide Mo2C can be oxidized and dissolved in sulphuric acid.

Influence of preparation process on sintering behavior and mechanical properties of ultrafine grained Ti(C, N)-based cermets

The influences of forming and sintering processes on distortion, cracking as well as mechanical properties of sintered bodies of ultrafine grained Ti(C, N)-based cermets were investigated. The results show that lubricant is indispensable to fabrication of ultrafine Ti(C, N)-based cermets, however, with low binder content in powder mixture, the lubrication action of paraffin is attenuated. A appropriate level of 2% (mass fraction) paraffin is determined for a cermet with binder content of 36% (mass fraction). It is also found that the influence of compaction pressure on distortion and cracking of sintered bodies presents a complex relationship. A relatively lower or higher compaction pressure, less than 100 MPa and more than 400 MPa respectively, favors uniform density distribution in green compact. The heating rate of sintering should be strictly controlled. Too fast heating rate results in enclosed pores to burst and forms large size pores in sintering body. A heating rate of 3 ℃/min is recommended.

Effect of sintering on microstructures and properties of sub-micron Ti(C,N)-based cermets

The influence of different sintering processes, including vacuum sintering, vacuum sintering followed by HIP and sintering-HIP, on the microstructure and properties of sub-micron Ti(C,N) cermets with various binder contents was studied. Image analysis based on back-scattered electrons image observations was used to determine the morphologic and structural characteristics. Transverse rupture strength(TRS), hardness, fracture toughness were measured and TRS data were treated by Weibull statistics further. It is shown that a very significant improvement in TRS can be obtained by HIP or sintering-HIP treatment for the alloys with lower and middle binder content at the controlled cooling rate, but the effect is not obvious for the alloys with higher binder content. HIP is also helpful for improving the hardness of sub-micron Ti(C,N) cermets, however, but can lower the fracture toughness. The variation of these properties was interpreted in terms of the difference in morphologic and structural characteristics.

Microstructure and mechanical properties of Ti(C, N)-based cermets with different molybdenum contents

The microstructure and mechanical properties of Ti(C, N)-based cermets with different content Mo were studied. Different Mo contents were added into Ti(C, N)-based cermets. Effect of sintering temperature on mechanical properties of the cermets was also investigated. Specimens were fabricated by conventional powder metallurgy techniques and vacuum sintered at different temperatures. The microstructure and the fracture morphology were investigated using scanning electron microscope. Transverse strength and hardness were measured. The results show that the microstructure is uniform and the thickness of rim phase is moderate when the content of Mo is 8%. The mechanical properties are the best when the content of Mo is 8% and the sintering temperature is 1450℃.

Effect of sintering parameters on powder injection molded Ti(C, N)-based cermets

Effect of two-stage sintering parameters such as heating rate, top sintering temperature and holding time, sintering temperature and holding time at the second stage on relative density, transverse rupture strength(TRS) and microstructures of powder injection molded Ti(C, N)-based cermets were investigated, by means of Archimedes’s method, three-point bending test and micrographic analysis. The results show that the optimum sintering cycle for powder injection molded Ti(C, N)-based cermets comprises rapid heating (10℃/min) at low temperatures, slow heating (5℃/min) at intermediate temperatures, holding at the highest sintering temperature (1420℃) for a short time (10min), and holding at the second stage (1360℃) for a longer time (6h) to avoid grain coarsening, and that its TRS reaches 624MPa, and there are little pores in their microstructures.

Effect of Powder Particle Size on the Properties and Microstructure of Ti(C,N)-Based Cermet

The influence of raw powder particle size on the properties and microstructures of Ti (C, N)-based cermets has been studied. The conclusions are as follows: The microstructures of cermets were composed of two kinds of grains, the one with black cores surrounded by obvious rim structures, and the other whose cores were white with unconspicuous rim structures and adhesive phase. In the cermet made from fine powders, the amount of grains with white cores was much more than that in cermet made from coarse powders. In addition, their properties were also much better.

Microstructure and shear strength of the brazed joint of Ti(C,N)-based cermet to steel

Firm joins were obtained between Ti（C,N）-based cermet and steel with Ag-Cu-Zn-Ni filler metal by vacuum brazing. The effects of technological parameters such as brazing temperature, holding time, and filler thickness on the shear strength of the joints were investigated. The microstructure of welded area and the reaction products of the filler metal were examined by scanning electron microscopy （SEM）, metallographic microscope （OM）, energy-dispersive X-ray analysis （EDS）, and X-ray diffraction （XRD）. The brazing temperature of 870℃, holding time of 15 min, and filler thickness of 0.4 mm are a set of optimum technological parameters, under which the maximum shear strength of the joints, 176.5 MPa, is achieved. The results of microstructure show that the wettability of the filler metal on Ti（C,N）-based cermet and steel is well. A mutual solution layer and a diffusion layer exist between the welding base materials and the filler metal.

Spark Plasma Sintering Properties of Ultrafine Ti(C,N)-based Cermet

Ultrafine Ti(C,N)-based cermet was sintered by SPS from 1050℃ to 1450℃ and its sintering properties,such as porosity,mechanical properties and phase transformation,were investigated by optical microscopy (OM),scanning electron microscopy (SEM),X-ray diffraction (XRD),and differential scanning calorimeter (DSC).It is found that the spark plasma sintering properties of Ti(C,N)-based cermet differ from those of conventional vacuum sintering.The liquid phase appearance is at least lower by 150℃ than that in vacuum sintering.The porosity decreases sharply below 1 200℃ and reaches minimum at 1 200℃,and afterwards it almost keeps invariable and no longer increases.SPS remarkably accelerates the phase transformation of Ti(C,N)-based cermet and it has a powerful ability to remove oxides in Ti(C,N)-based cermets.Above 1 350℃,denitrification occurred.Fresh graphite phase formed above 1 430℃.Both the porosity and graphite are responsible for the poor TRS.

Microstructural evolution and characteristics during sintering of submicron Ti(C,N)-based cermet

Ti（C,N）-based cermets were prepared with submicron powders. The microstructure evolution and characteristics during the sintering of cermet were studied by TEM, SEM, EDX and XRD. The forming mechanism of the structures was also studied. There exist inner rim and outer rim between the hard cores and the binder. The inner rim is enriched in Mo and W compared with the outer rim, and is formed during the solid sintering by counter diffusion of TiC, Mo2C and WC. The outer rim is formed during the liquid sintering by Ostwald ripening mechanism.

Characterization of phase transformation and microstructure of nano hard phase Ti(C,N)-based cermet by spark plasma sintering

By means of optical microscope , scanning electron microscope （SEM） and transmission electron microscope （TEM）, the process of densification, the characterization of phase transformation and the microstructure for spark plasma sintering （SPS） nano hard phase Ti（C,N）-based cermet were investigated. It is found that the spark plasma sintering （SPS） enables the nano hard phase Ti（C,N）-based cermet to densify rapidly, however, the full densification of the sintered samples can not be obtained. The rate of phase transformation is significantly quick. When being sintered at 1 200 ℃ for 8 min, Mo2C is completely dissolved, and TiN dissolves into TiC entirely and disappears. Above 1 200 ℃, Ti（C,N） begins to decompose and the atoms of C and N separate from Ti（C,N） resulting in the generation of N2 and the graphite. Due to the denitrification and the graphitization, the density and the hardness of sintered samples are rather low. The distribution of grain size of the sample sintered at 1 350 ℃ covers a wide range of 90500 nm, and most of the grain size are about 200 nm. The hard phase is not of typical core-rim structure. Oxides on the surface of particles can not be fully removed and present in sample as titanium oxide TiO2. Graphite exists in band-like shape.

Effect of hot isostatic pressing nitrogen on the microstructure and properties of a Ti(C,N)-based cermet

The high-temperature, high-pressure hot isostatic pressing technology was used for depositing hard coatings on Ti（C, N）-based cermets. The rnicrostructure and properties of the sample were investigated using optical microscopy, scan- ning electron microscopy, X-ray diffraction, electron probe microanalysis, and microhardness tester. The results showed that the rich titanium and nitrogen in surface zone were induced by the heat treatment. The high nitrogen activity of the surface region was the driving force for outward transport of titanium and inward transport of tungsten in the cobalt binder. The toughness and hardness were improved and a hardness gradient was formed. It is the high-temperature, high-pressure N2 that enables closure of holes, thereby alleviating defects and prolonging tool life.

Preparation of ultrafine Ti (C, N)-based cermet using oxygen-rich powders

The availability using oxygen-rich powders to prepare ultrafine Ti(C,N)-based cermets was investigated. The deoxidation process, denitrification phenomenon and the effect of deoxidation on microstructure and mechanical properties of sintered samples were discussed, respectively. The results show that oxygen in the samples prepared even with high oxygen contained in starting powders can be almost completely cleaned away through suitable sintering process. The ultrafine oxygen-rich powders have a significant effect on microstructure, which promotes the formation of white core phase. A ultrafine Ti(C,N)-based cermet with mean particle size of 0. 30 μm, uniform microstructure and excellent mechanical properties is successfully prepared. It is also found that there exists severe denitrification phenomenon in the preparation process of ultrafine Ti(C,N)-based cermet.

Evolution of Ti(C,N)-based cermet microstructures

Two series of Ti(C,N) based cermet materials originating from the same chemical composition but with different grain size distribution and sintered to different stages of the sintering cycle have been studied using SEM, TEM, EDX, and XRD. Much of the surrounding structure is formed during solid state sintering. During the solid state sintering, at first, the Mo and W rich (Ti,Mo,W)C inner rim is formed by the interaction among TiC, WC, and Mo 2C; then the Mo and W lean (Ti,Mo,W)(C,N)outer rim is formed. During the liquid phase sintering, the outer rim of coarse grains grows rapidly throw a solution reprecipitation process; also coarse grains grow by particle coalescence. The interface between coarse grain outer rim and binder is flat (crystal surface).

牙轮钻头Ti(C,N)基金属陶瓷密封配副磨损研究

目前牙轮钻头金属密封环通常采用相同的金属材料,其磨损性能不佳,易造成金属密封因磨损严重而失效。为提高金属密封的磨损性能,提出采用Ti(C,N)基金属陶瓷作为牙轮钻头密封副,并开展其与不同材料配副的磨损试验,研究不同摩擦副的摩擦磨损性能和磨损形式;建立适用于牙轮钻头金属密封材料的数值磨损模型,开展Ti(C,N)基金属陶瓷与不同材料配副的双金属密封性能的数值模拟,基于磨损模型预测使用30 h后不同双金属密封的磨损体积。试验结果表明:当Ti(C,N)基金属陶瓷作为动摩擦副,9CrSi作为静摩擦副时,金属环表面平均磨损体积最小,同时摩擦因数较小,磨损性能更佳。通过试验与仿真数据对比,验证了建立的数值磨损模型适用于双金属密封。仿真结果表明:当Ti(C,N)基金属陶瓷作为动金属环,9CrSi作为静金属环时密封端面磨损体积最小,金属密封磨损性能显著提高,其接触应力最大值为23.243 MPa,能够满足密封要求。

不同量Ta的添加对Ti(C,N)基金属陶瓷显微组织和力学性能的影响

向Ti(C,N)基金属陶瓷中加入不同量的钽,随后检测了含钽量不同的金属陶瓷的显微组织和力学性能.结果表明:Ti(C,N)基金属陶瓷硬质相主要由黑芯、白色内壳和灰色外壳构成,Ta添加量超过4%的Ti(C,N)基金属陶瓷有白芯相和无芯相;随着Ta添加量的增加,硬质相的尺寸减小,Ta添加量为4%的Ti(C,N)基金属陶瓷硬质相尺寸最小;随着Ta添加量的增加,Ti(C,N)基金属陶瓷的硬度和抗弯强度先增加后减小,断裂韧度增加.

EFFECT OF RARE EARTH ELEMENT Er ON STRENGTHENING OF INTERFACE OF Ti（C，N） BASED CERMETS

ＥＦＦＥＣＴＯＦＲＡＲＥＥＡＲＴＨＥＬＥＭＥＮＴＥｒＯＮＳＴＲＥＮＧＴＨＥＮＩＮＧＯＦＩＮＴＥＲＦＡＣＥＯＦＴｉ（Ｃ，Ｎ）ＢＡＳＥＤＣＥＲＭＥＴＳ￥ＬｉｕＮｉｎｇ（ＤｅｐａｒｔｍｅｎｔｏｆＭａｔｅｒｉａｌｓＳｃｉｅｎｃｅａｎｄＥｎｇｉｎｅｅｒｉｎｇ，...