WC-10Co cemented carbides with finer WC and narrower grain size distributions are produced by using(Cr,V)_(2)(C,N)as grain growth inhibitors.As a result,with the increase of(Cr_(0.9),V_(0.1))_(2)(C,N)and(V_(0.9),Cr_(0...WC-10Co cemented carbides with finer WC and narrower grain size distributions are produced by using(Cr,V)_(2)(C,N)as grain growth inhibitors.As a result,with the increase of(Cr_(0.9),V_(0.1))_(2)(C,N)and(V_(0.9),Cr_(0.1))_(2)(C,N),the grains size of WC and mean free path of Co phase decrease,and adjacency of WC increases.Refinement and homogenization of grains enhance the transverse rupture strength(TRS)and the hardness.Meanwhile,the deflection and bridging of cracks keep the fracture toughness at a respectable level.The WC-10Co-0.6(Cr_(0.9),V_(0.1))_(2)(C,N)-0.025(V_(0.9),Cr_(0.1))_(2)(C,N)cemented carbides exhibit excellent comprehensive mechanical properties with the TRS of 4602.6 MPa,hardness of 1835 kg/mm^(2),and fracture toughness of 10.39 MPa·m^(1/2),respectively.However,the large pores are caused by excess N larger than 0.03 wt%and deteriorates the mechanical properties.We provide a new approach to WC-Co cemented carbides preparation with a narrow grain size distribution by adding novel grain growth inhibitors.展开更多
The high-pressure diagram of V–N compounds is enriched by proposed seven new stable high-pressure phases.The P-1-VN_4with the armchair N-rich structure may be quenched to ambient conditions.The formed N–N covalent b...The high-pressure diagram of V–N compounds is enriched by proposed seven new stable high-pressure phases.The P-1-VN_4with the armchair N-rich structure may be quenched to ambient conditions.The formed N–N covalent bond plays an important role for the structural stability of N-chain.The charge transfer results in a V–N ionic bond interaction,which further improves the stability of N-chain structure.The P-1-VN_4,P4mnc-VN_8,and Immm-VN_(10)with the outstanding detonation properties have potential application in explosive field.展开更多
基金Funded by the 2021 Strategic Cooperation Project between Sichuan University and The People's Government of Zigong(No.2021CDZG-1)Major Science and Technology Research Projects of Panxi,Sichuan Province(No.2022PXZB-04)。
文摘WC-10Co cemented carbides with finer WC and narrower grain size distributions are produced by using(Cr,V)_(2)(C,N)as grain growth inhibitors.As a result,with the increase of(Cr_(0.9),V_(0.1))_(2)(C,N)and(V_(0.9),Cr_(0.1))_(2)(C,N),the grains size of WC and mean free path of Co phase decrease,and adjacency of WC increases.Refinement and homogenization of grains enhance the transverse rupture strength(TRS)and the hardness.Meanwhile,the deflection and bridging of cracks keep the fracture toughness at a respectable level.The WC-10Co-0.6(Cr_(0.9),V_(0.1))_(2)(C,N)-0.025(V_(0.9),Cr_(0.1))_(2)(C,N)cemented carbides exhibit excellent comprehensive mechanical properties with the TRS of 4602.6 MPa,hardness of 1835 kg/mm^(2),and fracture toughness of 10.39 MPa·m^(1/2),respectively.However,the large pores are caused by excess N larger than 0.03 wt%and deteriorates the mechanical properties.We provide a new approach to WC-Co cemented carbides preparation with a narrow grain size distribution by adding novel grain growth inhibitors.
文摘The high-pressure diagram of V–N compounds is enriched by proposed seven new stable high-pressure phases.The P-1-VN_4with the armchair N-rich structure may be quenched to ambient conditions.The formed N–N covalent bond plays an important role for the structural stability of N-chain.The charge transfer results in a V–N ionic bond interaction,which further improves the stability of N-chain structure.The P-1-VN_4,P4mnc-VN_8,and Immm-VN_(10)with the outstanding detonation properties have potential application in explosive field.