3-乙酰基-6-苯甲酰基-N-乙基咔唑的合成

The novel carbazole derivative — 3-biacetyl-6-benzoyl-N-ethylcarbazole was synthesized through alkylation and Friedel-Crafts acylation from carbazole.The structure of the target compound was characterized by 1HNMR,13CNMR,UV,IR and elemental analysis.The optimal synthetical conditions for the monoacylation was achieved by carrying out orthogonal experiments:when the mole ratio of benzoyl chloride and N-ethyl-carbazole was1.2:1,while the mole ratio of catalyst and N-ethylcarbazole was 1.2:1 at 25℃for 3h.The yield was about 94.6%.

2-糠醛缩N-乙基-3,6-二氨基咔唑双席夫碱的合成及其性能

以咔唑为起始原料经N-取代、硝化和还原反应制备中间体N-乙基-3,6-二氨基咔唑,然后以其与2-糠醛发生缩合反应制得新型双席夫碱化合物N-乙基-3,6-二(2-亚糠基亚氨基)咔唑,产率为72.36%。通过元素分析、FTIR、UV-Vis、1H NMR、溶液及固体荧光光谱、循环伏安(CV)和TG-DTA分析研究了标题化合物的分子结构、光物理特性、电化学特性和热稳定性。结果表明,化合物的DMF稀溶液在200~400 nm波段有较宽较强的紫外吸收;在365nm波长激发下,溶液发射深蓝色荧光,λem为446nm,固体荧光为λem=467nm的蓝色荧光,与溶液荧光相比固体荧光红移了21nm。由循环伏安测试得到产物的Eg=2.19e V,IP=4.99e V以及EA=2.80e V,说明其具有良好的空穴和电子传输材料性能。TG-DTA测试显示目标产物具有良好的热稳定性。该化合物在有机荧光、空穴注入传输材料以及电子传输材料方面具有潜在应用前景。

新型二胺扩链剂对合成聚脲机械性能的影响

以咔唑为原料合成了新型扩链剂N-乙基-3,6-二氨基咔唑;将其与端氨基聚醚和甲苯-2,4-二异氰酸酯(TDI)经溶液聚合合成了新型聚脲;采用红外光谱表征了新型扩链剂和聚脲的结构.结果表明,以N-乙基-3,6-二氨基咔唑作为扩链剂合成聚脲时,随异氰酸酯质量分数的增加,凝胶时间逐渐变短;所制备的聚脲的拉伸强度达25MPa,断裂伸长率降低为105%.