Abstract A method of Baotou mixed rare earth concen- trate leaching was investigated. According to the principle of complex leaching, the quadratic orthogonal regression experiment was used to investigate effect of si...Abstract A method of Baotou mixed rare earth concen- trate leaching was investigated. According to the principle of complex leaching, the quadratic orthogonal regression experiment was used to investigate effect of six factors. An optimal condition of low energy and environment friendly was determined as follows: HCl acidity is 4 mol.L-1, AlCl3 concentration is 2 mol.L-l, reaction temperature is 85 ℃, reaction time is 90 rain, liquid to solid ratio is 35 ml.g-1, and stirring speed is 100 r.min-1. According to this condition, the leaching ratio of mixed rare earth con- centrate is 76.5 %. The analyses of X-ray diffraction shows that bastnasite disappears, and the main peaks of filter residue is monazite and cheralite after leaching of HCl- AlCl3 solution. The result indicates that REFCO3 of the mixed rare earth concentrate can be dissolved, but REPO4 remains in the leaching residue. This method provides a way to separate and extract rare earth.展开更多
Waste selective catalytic reduction(SCR)catalysts are potential environmental hazards.In this study,the recovery of vanadium and tungsten from waste SCR catalysts by K_(2)CO_(3)roasting and water leaching was investig...Waste selective catalytic reduction(SCR)catalysts are potential environmental hazards.In this study,the recovery of vanadium and tungsten from waste SCR catalysts by K_(2)CO_(3)roasting and water leaching was investigated.The roasting and leaching conditions were optimized:the leaching efficiencies of vanadium and tungsten were 91.19%and 85.36%,respectively,when 18 equivalents of K_(2)CO_(3)were added to perform the roasting at 900℃ for 2 h,followed by leaching at 90°C for 1 h.Notably,in the described conditions,the leaching rate of silicon was only 28.55%.Titanates,including K_(2)Ti_(6)O_(13)and KTi8017,were also produced.Si removal was achieved in 85%efficiency adjusting the pH to 9.5,and the Si impurity thus isolated was composed of amorphous Si.Tungsten and vanadium were precipitated using CaCl_(2).At pH 10 and following the addition of 0.10 mol of H_(2)O_(2)and 16 equivalents of CaCl_(2),the precipitating efficiencies of tungsten and vanadium were 96.89%and 99.65%,respectively.The overall yield of tungsten and vanadium was 82.71%and 90.87%,respectively.展开更多
基金financially supported by the National Nature Science Foundation of China (No. 51174115)National Outstanding Youth Science Foundation of China (No. 51025416)Program for Changjiang Scholars and Innovative Research Team in University (No. IRT1065)
文摘Abstract A method of Baotou mixed rare earth concen- trate leaching was investigated. According to the principle of complex leaching, the quadratic orthogonal regression experiment was used to investigate effect of six factors. An optimal condition of low energy and environment friendly was determined as follows: HCl acidity is 4 mol.L-1, AlCl3 concentration is 2 mol.L-l, reaction temperature is 85 ℃, reaction time is 90 rain, liquid to solid ratio is 35 ml.g-1, and stirring speed is 100 r.min-1. According to this condition, the leaching ratio of mixed rare earth con- centrate is 76.5 %. The analyses of X-ray diffraction shows that bastnasite disappears, and the main peaks of filter residue is monazite and cheralite after leaching of HCl- AlCl3 solution. The result indicates that REFCO3 of the mixed rare earth concentrate can be dissolved, but REPO4 remains in the leaching residue. This method provides a way to separate and extract rare earth.
基金from the Fundamental Research Funds for the Central Universities(2010YH14).
文摘Waste selective catalytic reduction(SCR)catalysts are potential environmental hazards.In this study,the recovery of vanadium and tungsten from waste SCR catalysts by K_(2)CO_(3)roasting and water leaching was investigated.The roasting and leaching conditions were optimized:the leaching efficiencies of vanadium and tungsten were 91.19%and 85.36%,respectively,when 18 equivalents of K_(2)CO_(3)were added to perform the roasting at 900℃ for 2 h,followed by leaching at 90°C for 1 h.Notably,in the described conditions,the leaching rate of silicon was only 28.55%.Titanates,including K_(2)Ti_(6)O_(13)and KTi8017,were also produced.Si removal was achieved in 85%efficiency adjusting the pH to 9.5,and the Si impurity thus isolated was composed of amorphous Si.Tungsten and vanadium were precipitated using CaCl_(2).At pH 10 and following the addition of 0.10 mol of H_(2)O_(2)and 16 equivalents of CaCl_(2),the precipitating efficiencies of tungsten and vanadium were 96.89%and 99.65%,respectively.The overall yield of tungsten and vanadium was 82.71%and 90.87%,respectively.