Characterization and Stability of Na-doped p-type ZnO Thin Films Preparation by Reactive DC Magnetron Sputtering

Na-doped p-type ZnO thin films have been realized by DC reactive magnetron sputtering with a set of metal-Zn targets doped with various Na contents and under different substrate temperatures, respectively. Hall effect measurement, field-emission SEM, X-ray diffraction and optical transmission were carried out to investigate the effects of Na content and substrate temperature on the properties of p-type films. Results indicate that all the Na-doped ZnO films are strongly （002） oriented, and have an average transmittance -85 % in the visible region. Na-doped p-type ZnO films with good structural, electrical, and optical properties can only be obtained at an intermediate amount of Na content and under appropriate substrate temperature. At the optimal condition, the Na-doped p-type ZnO has the lowest resistivity of 13. 8 Ω· cm with the carrier concentration as high as 1.07 × 10^18 em^-3. The stability of the Na-doped p-type ZnO is also studied in this paper and it is found that the electrical properties keep stable in a period of one month.

Influence of dopant content on morphology and optical constants of ZnO:Na films by sol-gel method

Undoped and Na-doped ZnO films were deposited by sol-gel method.The effects of sodium incorporation on structure,surface morphology and optical constants of the films were investigated.X-ray diffraction patterns show the hexagonal wurtzite polycrystalline structure and that the sodium incorporation leads to the change in the structural characteristics of ZnO films.The SEM observations show that the surface morphology of the films is affected by the sodium incorporation.The transmission spectra show that the average transmittance of the films is above 85% in the visible range.The absorption edge initially blue-shifts and then red-shifts with the increase of Na doping content.The optical constants of these films were calculated using transmission spectra.Refractive indices of the films in the visible range decrease at first and then increase with increasing Na doping content.

Effect of annealing atmosphere on magnetic properties of pure ZnO and Na:ZnO films

Pure ZnO and Zn0.96Na0.04O films were grown on quartz substrates by sol-gel technology.The XRD analysis revealed that all thin films had hexagonal wurtzite structure and obvious c-axis preferred orientation.Ferromagnetism was precisely measured by an alternating gradient magnetometer (AGM).To explore the nature original ferromagnetism,the effect of annealing atmosphere on magnetic properties of the films was studied.Compared with pure ZnO,magnetic hysteresis loops showed that doping Na atoms enhanced saturation magnetism.The mag-netism of the films annealed in the air atmosphere was significantly better than that in the O2 atmosphere.The photoluminescence (PL) spec-trum analysis suggested that the ferromagnetism was due to the defects in the films.

Effect of Na Concentrations on Microstructure and Optical Properties of ZnO Films

Na-doped ZnO thin films were deposited on the glass substrates using sol-gel method. The effect of Na concentrations on the structural and optical properties of ZnO films was studied. As Na concentration increases from 0.0 at% to 16.0 at%, preferential c-axis orientation becomes more and more obvious, and the intensity of the diffraction peaks from （103） increases. The optical band gap Eg value increases from 3.261 to 3.286 eV first and then decreases as Na concentration increases from 0.0 to 2.0 at% and then beyond 2.0 at%. The intensity of all the emissions increases with increasing Na concentration and the origins of the violet emission （wavelength in the 400-407 nm） and the blue emission （wavelength at 473 nm） were discussed in detail.