In this study,waste cotton fabric was used as cellulose raw material and pretreated in aqueous NaOH/urea solution system to investigate the effect of NaOH/urea pretreatment solution on the hydrolysis of cotton fiber.T...In this study,waste cotton fabric was used as cellulose raw material and pretreated in aqueous NaOH/urea solution system to investigate the effect of NaOH/urea pretreatment solution on the hydrolysis of cotton fiber.The cotton fiber was pretreated with different conditions of aqueous NaOH/urea solution,and the pretreated cotton fiber was hydrolyzed under the same conditions as the original cotton fiber.The results of characterization analysis showed that water retention value of pretreated cotton fiber was higher than that of unpretreated sample.Moreover,the cotton fiber presented both a convoluted structure and a coarser surface,XRD results suggested that the crystallinity degree of cellulose decreased dramatically,more cellulose II appeared,and the hydrogen bond is broken.Among the different pretreatment conditions,the pretreatment effect was the best when the reaction temperature was 0°C,the solid-liquid ratio was 2:50,and the NaOH/urea ratio was 7:12.The hydrolysis experiments of pretreated and unpretreated cotton fibers showed that when the hydrothermal temperature was 230°C,the heat preservation was 2 h,and the hydrochloric acid concentration was 5 wt.%,the glucose yield reached 29.99%.H+could catalyze the hydrolysis of cotton fiber more effectively due to damage to crystal structure and hydrogen bonds.展开更多
Hydroxypropyl celluloses(HPC) were homogenously synthesized by the reaction of cellulose with propylene oxide in NaOH/urea aqueous solution.Water-soluble HPC with molar degree of substitution(MSNMR) in the range of 0....Hydroxypropyl celluloses(HPC) were homogenously synthesized by the reaction of cellulose with propylene oxide in NaOH/urea aqueous solution.Water-soluble HPC with molar degree of substitution(MSNMR) in the range of 0.52~0.78 was prepared from microcrystalline cellulose,cotton linters,and spruce sulfite pulp.The structure of the HPC samples was characterized by means of FT-IR,NMR,gas chromatography(GC),and size exclusion chromatography(SEC) analyses.Three types of cellulose samples with different molecular weights were found to dissolve well in the NaOH/urea solvent with no obvious differences in reactivity and regioselectivity.The relative reactivity of hydroxyl groups in the glycosyl unit was in the following order:O-6>O-2>O-3.In addition,the results of the study indicated that the tandem reaction during hydroxypropylation could be ignored.展开更多
基金supported by the National Natural Science Foundation of China[Nos.51703153 and 21802101].
文摘In this study,waste cotton fabric was used as cellulose raw material and pretreated in aqueous NaOH/urea solution system to investigate the effect of NaOH/urea pretreatment solution on the hydrolysis of cotton fiber.The cotton fiber was pretreated with different conditions of aqueous NaOH/urea solution,and the pretreated cotton fiber was hydrolyzed under the same conditions as the original cotton fiber.The results of characterization analysis showed that water retention value of pretreated cotton fiber was higher than that of unpretreated sample.Moreover,the cotton fiber presented both a convoluted structure and a coarser surface,XRD results suggested that the crystallinity degree of cellulose decreased dramatically,more cellulose II appeared,and the hydrogen bond is broken.Among the different pretreatment conditions,the pretreatment effect was the best when the reaction temperature was 0°C,the solid-liquid ratio was 2:50,and the NaOH/urea ratio was 7:12.The hydrolysis experiments of pretreated and unpretreated cotton fibers showed that when the hydrothermal temperature was 230°C,the heat preservation was 2 h,and the hydrochloric acid concentration was 5 wt.%,the glucose yield reached 29.99%.H+could catalyze the hydrolysis of cotton fiber more effectively due to damage to crystal structure and hydrogen bonds.
文摘Hydroxypropyl celluloses(HPC) were homogenously synthesized by the reaction of cellulose with propylene oxide in NaOH/urea aqueous solution.Water-soluble HPC with molar degree of substitution(MSNMR) in the range of 0.52~0.78 was prepared from microcrystalline cellulose,cotton linters,and spruce sulfite pulp.The structure of the HPC samples was characterized by means of FT-IR,NMR,gas chromatography(GC),and size exclusion chromatography(SEC) analyses.Three types of cellulose samples with different molecular weights were found to dissolve well in the NaOH/urea solvent with no obvious differences in reactivity and regioselectivity.The relative reactivity of hydroxyl groups in the glycosyl unit was in the following order:O-6>O-2>O-3.In addition,the results of the study indicated that the tandem reaction during hydroxypropylation could be ignored.