A clean and efficient route for the utilization of ilmenite concentrates was proposed by direct carbothermic reduction in microwave field.High dosage of Na_(2)CO_(3),which can be recycled,was added to accelerate the r...A clean and efficient route for the utilization of ilmenite concentrates was proposed by direct carbothermic reduction in microwave field.High dosage of Na_(2)CO_(3),which can be recycled,was added to accelerate the reduction reaction of ilmenite concentrates.After microwave heating in the temperature range of 1073−1123 K for 20 min,the main products were Na_(2)TiO_(3) and metallic Fe with the metallization ratios being as high as 92.67%−93.21%.The reduction products were processed by water leaching,ball-milling in CO2 atmosphere and magnetic separation in turn.The final products after magnetic separation were Fe-rich materials and Ti-rich materials(90.04 wt.%TiO2),which can be used to produce iron and TiCl4 or TiO2.The optimized heating temperature was 1123 K in terms of metallization ratios,magnetic separation and caking property of the reduction products.Besides,the reduction mechanism of ilmenite concentrates with the addition of Na_(2)CO_(3) in microwave field was also proposed.展开更多
基金financially supported by the National Natural Science Foundation of China(Nos.51734002,51474141)China Postdoctoral Science Foundation(No.2020M671071)Independent Research and Development Project of State Key Laboratory of Advanced Special Steel,Shanghai Key Laboratory of Advanced Ferrometallurgy,Shanghai University,China(No.SKLASS 2019-Z014)。
文摘A clean and efficient route for the utilization of ilmenite concentrates was proposed by direct carbothermic reduction in microwave field.High dosage of Na_(2)CO_(3),which can be recycled,was added to accelerate the reduction reaction of ilmenite concentrates.After microwave heating in the temperature range of 1073−1123 K for 20 min,the main products were Na_(2)TiO_(3) and metallic Fe with the metallization ratios being as high as 92.67%−93.21%.The reduction products were processed by water leaching,ball-milling in CO2 atmosphere and magnetic separation in turn.The final products after magnetic separation were Fe-rich materials and Ti-rich materials(90.04 wt.%TiO2),which can be used to produce iron and TiCl4 or TiO2.The optimized heating temperature was 1123 K in terms of metallization ratios,magnetic separation and caking property of the reduction products.Besides,the reduction mechanism of ilmenite concentrates with the addition of Na_(2)CO_(3) in microwave field was also proposed.