The mixture of Nano-graphite and organic vehicles doped to Nano-diamond paste. The suitable paste proportion was found. Nano-diamond film (NDF) was prepared by sol-gel coating method on ITO glass at 3000/min. The fiel...The mixture of Nano-graphite and organic vehicles doped to Nano-diamond paste. The suitable paste proportion was found. Nano-diamond film (NDF) was prepared by sol-gel coating method on ITO glass at 3000/min. The field emission characteristics of luminance-current, luminance-voltage and luminance-power of Nano-diamond film were analyzed and tested. Comparing these tested curves, the luminance was well proportional to current was got. Theoretic, the inner resistance of NDF field emission display (FED) consumes electric energy and real voltage change between the cathode and the anode of NDF-FED was very small after electrons emit. So the characteristic of NDF-FED was preferable to describe by luminance-current linear relationship, which was advantageous to device tested and designed.展开更多
The low-cost and large area screen-printed nano-diamond film (NDF) for electronic emission was fabricated. The edges and corners of nanocrystalline diamond are natural field-emitters. The nano-diamond paste for screen...The low-cost and large area screen-printed nano-diamond film (NDF) for electronic emission was fabricated. The edges and corners of nanocrystalline diamond are natural field-emitters. The nano-diamond paste for screen-printing was fabricated of mixing nano-graphite and other inorganic or organic vehicles. Through enough disperse in isopropyl alcohol by ultrasonic nano-diamond paste was screen-printed on the substrates to form NDF. SEM images showed that the surface morphology of NDF was improved, and the nano-diamond emitters were exposed from NDF through the special thermal-sintering technique and post-treatment process. The field emission characteristics of NDF were measured under -6 all conditions with 10 Pa pressure. The results indicated that the field emission stability and emission uniformity of NDF were improved through hydrogen plasma post-treatment process. The turn-on field decreased from 1.60 V/ μm to 1.25 V/ μm . The screen-printed NDF can be applied to the displays electronic emission cathode for low-cost outdoor in large area.展开更多
文摘The mixture of Nano-graphite and organic vehicles doped to Nano-diamond paste. The suitable paste proportion was found. Nano-diamond film (NDF) was prepared by sol-gel coating method on ITO glass at 3000/min. The field emission characteristics of luminance-current, luminance-voltage and luminance-power of Nano-diamond film were analyzed and tested. Comparing these tested curves, the luminance was well proportional to current was got. Theoretic, the inner resistance of NDF field emission display (FED) consumes electric energy and real voltage change between the cathode and the anode of NDF-FED was very small after electrons emit. So the characteristic of NDF-FED was preferable to describe by luminance-current linear relationship, which was advantageous to device tested and designed.
基金supported by the National Scientific Fund of China (no.90923040 and no.60844006)National 973 program of China(no.2009CB724202)Ningxia higher education Scientific Fund (no.2008JY002)
文摘The low-cost and large area screen-printed nano-diamond film (NDF) for electronic emission was fabricated. The edges and corners of nanocrystalline diamond are natural field-emitters. The nano-diamond paste for screen-printing was fabricated of mixing nano-graphite and other inorganic or organic vehicles. Through enough disperse in isopropyl alcohol by ultrasonic nano-diamond paste was screen-printed on the substrates to form NDF. SEM images showed that the surface morphology of NDF was improved, and the nano-diamond emitters were exposed from NDF through the special thermal-sintering technique and post-treatment process. The field emission characteristics of NDF were measured under -6 all conditions with 10 Pa pressure. The results indicated that the field emission stability and emission uniformity of NDF were improved through hydrogen plasma post-treatment process. The turn-on field decreased from 1.60 V/ μm to 1.25 V/ μm . The screen-printed NDF can be applied to the displays electronic emission cathode for low-cost outdoor in large area.