Nanostructured anisotropic Nd-Fe-B/Fe(C) composite powders were prepared by coating Fe(C) softmagnetic nanoparticles on HDDR Nd-Fe-B hard magnetic powders using iron pentacarbonyl Fe(CO)5 as soft-phase precursor.The e...Nanostructured anisotropic Nd-Fe-B/Fe(C) composite powders were prepared by coating Fe(C) softmagnetic nanoparticles on HDDR Nd-Fe-B hard magnetic powders using iron pentacarbonyl Fe(CO)5 as soft-phase precursor.The effect of Fe(CO)5-loading amount on soft-phase purity,coating morphology and magnetic properties of the composite powders was investigated.Dense and continuous Fe(C) softphase coatings with average particle sizes of 58-68 nm are obtained at Fe(CO)5 loading amounts of x <12 wt%,leading to enhanced remanence and improved energy product of the coated powders.Positive value in δM-plots and single-phase-like demagnetization curves are observed in the Nd-Fe-B/Fe(C) composite powders,indicating the exchange coupling effect between the coated Fe(C) soft phases and the Nd-Fe-B hard phase.展开更多
基金Project supported by the National Natural Science Foundation of China(51771219,51771220,and 51422106)the State Key Laboratory of Rare Earth Permanent Magnetic Materials Opening Foundation(SKLREPM170F03)+1 种基金the China Postdoctoral Science Foundation(2016M601989)the Natural Science Foundation of Ningbo City(2016A610249 and 2017A610030)
文摘Nanostructured anisotropic Nd-Fe-B/Fe(C) composite powders were prepared by coating Fe(C) softmagnetic nanoparticles on HDDR Nd-Fe-B hard magnetic powders using iron pentacarbonyl Fe(CO)5 as soft-phase precursor.The effect of Fe(CO)5-loading amount on soft-phase purity,coating morphology and magnetic properties of the composite powders was investigated.Dense and continuous Fe(C) softphase coatings with average particle sizes of 58-68 nm are obtained at Fe(CO)5 loading amounts of x <12 wt%,leading to enhanced remanence and improved energy product of the coated powders.Positive value in δM-plots and single-phase-like demagnetization curves are observed in the Nd-Fe-B/Fe(C) composite powders,indicating the exchange coupling effect between the coated Fe(C) soft phases and the Nd-Fe-B hard phase.